摘要
A novel open-framework ecomaterial silicotitanate (Na_4Ti_4Si_3O_(10)) wassynthesized by a combination of solgel and hydrothermal methods. The investigation on ion exchangeproperties shows that Na_4Ti_4Si_3O_(10) exhibits high ad-sorption for cesium, i.e., K_d is as highas 60 000 mL/g in neutral solution. The crystal structure of Na_4Ti_4Si_3O_(10) was characterized byX-ray difiraction (XRD), scanning electronic microscope (SEM), transmission electron microscope(TEM), Raman spectrum, differential thermal and thermogravimetric analysis (DTA/TGA), inductivelycoupled plasma (ICP), and X fluorescence analysis. The compound is tetragonal, P4_2, a=b = 0.781 10nm, c = 1.196 45 nm, alpha =beta = gamma = 90 deg, Z = 4, and R^a = 0.041; Na_4Ti_4Si_3O_(10) has athree dimensional framework consisting of Ti-O octahedral clusters and Si-O tetrahedra. The resultsshow that Na_4Ti_4Si_3O_(10) has good chemical stability, thermal stability, and high cesium ionexchange capacity in the whole pH range.
A novel open-framework ecomaterial silicotitanate (Na_4Ti_4Si_3O_(10)) wassynthesized by a combination of solgel and hydrothermal methods. The investigation on ion exchangeproperties shows that Na_4Ti_4Si_3O_(10) exhibits high ad-sorption for cesium, i.e., K_d is as highas 60 000 mL/g in neutral solution. The crystal structure of Na_4Ti_4Si_3O_(10) was characterized byX-ray difiraction (XRD), scanning electronic microscope (SEM), transmission electron microscope(TEM), Raman spectrum, differential thermal and thermogravimetric analysis (DTA/TGA), inductivelycoupled plasma (ICP), and X fluorescence analysis. The compound is tetragonal, P4_2, a=b = 0.781 10nm, c = 1.196 45 nm, alpha =beta = gamma = 90 deg, Z = 4, and R^a = 0.041; Na_4Ti_4Si_3O_(10) has athree dimensional framework consisting of Ti-O octahedral clusters and Si-O tetrahedra. The resultsshow that Na_4Ti_4Si_3O_(10) has good chemical stability, thermal stability, and high cesium ionexchange capacity in the whole pH range.
基金
This work was financially supported by the Foundation for the Author of National Excellent Doctor Dissertation of China.