The partitioning effect of Al（α-phase stabilizer） and V elements（β-phase stabilizer） on strength of the primary α phases in the α/β Ti-6 Al-4 V alloy with the bimodal microstructure was investigated.It was found that partitioning of Al and V elements took place in the Ti-6 Al-4 V alloy during the recrystallization process,leading to the variation of the content of Al and V elements in the primary α phases with changing the volume fraction of the primary α phase.Nanoindentation tests reveal a general trend that the strength of the primary α phases increases with decreasing the volume fraction of the primary α phases,and such trend is independent on the loading direction relative to the c-axis of the α phase.The enhanced strength is attributed to the increase of the content of Al element in the primary α phase,but it is not dominated evidently by the change of the V content.The solid solution strengthening contributed from both the elastic strain introduced by the solute atoms and the variation of the density of states was estimated theoretically.
The partitioning effect of Al（α-phase stabilizer） and V elements（β-phase stabilizer） on strength of the primary α phases in the α/β Ti-6 Al-4 V alloy with the bimodal microstructure was investigated.It was found that partitioning of Al and V elements took place in the Ti-6 Al-4 V alloy during the recrystallization process,leading to the variation of the content of Al and V elements in the primary α phases with changing the volume fraction of the primary α phase.Nanoindentation tests reveal a general trend that the strength of the primary α phases increases with decreasing the volume fraction of the primary α phases,and such trend is independent on the loading direction relative to the c-axis of the α phase.The enhanced strength is attributed to the increase of the content of Al element in the primary α phase,but it is not dominated evidently by the change of the V content.The solid solution strengthening contributed from both the elastic strain introduced by the solute atoms and the variation of the density of states was estimated theoretically.
基金
supported by the National Natural Science Foundation of China (Grant Nos.51371180 and 51571199)