研究了本材-金属复合材料制备工艺,扫描电子显微镜(SEM)观察表明:化学镀镍后,木材表面呈光亮的银灰色,但镀层的平整度和光亮度不高,受木材表面粗糙度影响较大;经过抛光的木材看似光滑,实质上比较粗糙,存在有大量的木材纤维和导管孔洞;能谱分析(EDS)表明:镀层为Ni-P合金,Ni和P的质量百分数分别为95.36%和4.64%,为低磷合金镀层.
Preparation technology of timber-metal composite materias is studied. In this paper, scanning electron microscopy （SEM） observation showes that the wood surface is bright silver after electroless nickel plating, but the flatness of the coating and brightness is not high, and the surface roughness of wood have a greater impact on the quality of the nickel coating. After polishing the wood surface appears to be smooth, actually rough. There are a large number of wood fiber and duct openings on the surface. Spectrum analysis （EDS） showes that the coating is Ni-P low-phosphorus alloy,and the content of Ni and P is 95.36 percent and 4.64 percent.