摘要
This paper reports a new technique to fabricate an ion-exchange polymer-metal composite (IPMC) actuator. This technique is based on a hybrid organic-inorganic composite membrane. In the fabrication course, silica oxide particles, prepared from hydrolysis of tetraethyl orthosilicate in situ with sol-gel reaction, co-crystallize with perfluorosulfonate acid (PFSA) ionomer. Attenuated total reflectance fourier transform infrared spectroscopy (ATR-FTIR) analyses demonstrate that a highly water-saving hybrid membrane is formed. Measurements of mechanical properties reveal that elastic modulus and hardness of the hybrid membrane are about 2 times compared to a commercial PFSA membrane. Scanning electron microscopy (SEM) results show that the hybrid membrane has a high porosity. Inside the membrane pores, there exists a great quantity of micro scale channels in the range of 100―300 nm. After fabrication of IPMC actuator, an electric current sensor, a force sensor, and a high speed camera are assembled and used to evaluate IPMC performance. It is shown that, compared to an IPMC actuator made from a commercial membrane, the electromechanical performance of the new actuator increases 6―8 times; when it is actuated in air, its stable non-water working time is prolonged for 6―7 times.
This paper reports a new technique to fabricate an ion-exchange polymer-metal composite (IPMC) actuator. This technique is based on a hybrid organic-inorganic composite membrane. In the fabrication course, silica oxide particles, prepared from hydrolysis of tetraethyl orthosilicate in situ with sol-gel reaction, co-crystallize with perfluorosulfonate acid (PFSA) ionomer. Attenuated total reflectance fourier transform infrared spectroscopy (ATR-FTIR) analyses demonstrate that a highly water-saving hybrid membrane is formed. Measurements of mechanical properties reveal that elastic modulus and hardness of the hybrid membrane are about 2 times compared to a commercial PFSA membrane. Scanning electron microscopy (SEM) results show that the hybrid membrane has a high porosity. Inside the membrane pores, there exists a great quantity of micro scale channels in the range of 100–300 nm. After fabrication of IPMC actuator, an electric current sensor, a force sensor, and a high speed camera are assembled and used to evaluate IPMC performance. It is shown that, compared to an IPMC actuator made from a commercial membrane, the electromechanical performance of the new actuator increases 6–8 times; when it is actuated in air, its stable non-water working time is prolonged for 6–7 times.
基金
Supported by the National Natural Key Science Foundation of China (Grant No. 60535020)
National Natural Science Foundation of China (Grant Nos. 50705043 and 50805076)
Natural Science Foundation of Jiangsu Province (Grant No. 2007202)