The aluminum foil for high voltage aluminum electrolytic capacitor was immersed in 0.5 mol/L H3PO4 or 0.125 mol/L NaOH solution at 40 ℃ for different time and then DC electro-etched in 1 mol/L HC1＋2.5 mol/L H2SO4 el...The aluminum foil for high voltage aluminum electrolytic capacitor was immersed in 0.5 mol/L H3PO4 or 0.125 mol/L NaOH solution at 40 ℃ for different time and then DC electro-etched in 1 mol/L HC1＋2.5 mol/L H2SO4 electrolyte at 80 ℃. The pitting potential and self corrosion potential of A1 foil were measured with polarization curves （PC）. The potentiostatic current--time curve was recorded and the surface and cross section images of etched A1 foil were observed with SEM. The electrochemical impedance spectroscopy （EIS） of etched A1 foil and potential transient curves （PTC） during initial etching stage were measured. The results show the chemical pretreatments can activate A1 foil surface, facilitate the absorption, diffusion and migration of C1- onto the A1 foil during etching, and improve the initiation rate of meta-stable pits and density of stable pits and tunnels, leading to much increase in the real surface area and special capacitance of etched A1 foil.展开更多
The Al foil for high voltage Al electrolytic capacitor usage was immersed in 5.0%NaOH solution containing trace amount of Zn2＋and Zn was chemically plated on its surface through an immersion-reduction reaction. Such ...The Al foil for high voltage Al electrolytic capacitor usage was immersed in 5.0%NaOH solution containing trace amount of Zn2＋and Zn was chemically plated on its surface through an immersion-reduction reaction. Such Zn-deposited Al foil was quickly transferred into HCl-H 2 SO 4 solution for DC-etching. The effects of Zn impurity on the surface and cross-section etching morphologies and electrochemical behavior of Al foil were investigated by SEM, polarization curve （PC） and electrochemical impedance spectroscopy （EIS）. The special capacitance of 100 V formation voltage of etched foil was measured. The results show that the chemical plating Zn on Al substrate in alkali solution can reduce the pitting corrosion resistance, enhance the pitting current density and improve the density and uniform distribution of pits and tunnels due to formation of the micro Zn-Al galvanic local cells. The special capacitance of etched foil grows with the increase of Zn2＋concentration.展开更多
Aluminum capacitor foils with a tunnel etch structure were reacted with boiling water and then anodized at 530 V in boric acid solution or boric acid＋citric acid mixed solution.The microstructure and crystallinity of...Aluminum capacitor foils with a tunnel etch structure were reacted with boiling water and then anodized at 530 V in boric acid solution or boric acid＋citric acid mixed solution.The microstructure and crystallinity of the resulting anodized film were examined by TEM and XRD.The special capacitance,resistance and withstanding voltage of the film were explored with electrochemical impedance spectroscopy（EIS）,LCR meter and small-current charging.The results show that the high voltage anodized oxide film consists of an inner layer with high crystallinity and an outer layer with low crystallinity.However,the crystallinity of the film formed in boric acid＋citric acid mixed solution is higher than that of the film formed in only boric acid solution,leading to an increase in film＇s field strength and special capacitance.Meanwhile,there are more defects from phase transformation in the out layer of the film formed in boric acid＋citric acid mixed solution than in that of film formed in only boric acid solution,leading to a decrease in film＇s resistance and withstanding voltage.展开更多
Ni coating was deposited on carbon steel by a mechanical attrition enhanced electroplating （MAEE） process. During the electroplating, the mechanical attrition（MA） was introduced by impact of glass balls on the sam...Ni coating was deposited on carbon steel by a mechanical attrition enhanced electroplating （MAEE） process. During the electroplating, the mechanical attrition（MA） was introduced by impact of glass balls on the sample surface with a special vibrating frequency. The surface and cross-sectional images of Ni coating were observed with SEM. The microstructure and crystallinity of coating were examined with TEM and XRD. The electrochemical performance of coating was measured with polarization curves and electrochemical impedance spectroscopy （EIS） and its mechanical behaviours, such as tensile strength and hardness, were studied. The results show that the MA has significant effects on the microstructure and property of the electroplated Ni coating. By MA, the coating becomes smooth, compact, thin and has refined grains and is free of cracks and pores. Consequently, the adhesion, tensile strength, hardness and corrosion resistance of coating are improved significantly.展开更多
基金Project supported by University New Materials Disciplines Constructions Program of Beijing Region,ChinaProject(51172102/E020801) supported by the National Natural Science Foundation of China
文摘The aluminum foil for high voltage aluminum electrolytic capacitor was immersed in 0.5 mol/L H3PO4 or 0.125 mol/L NaOH solution at 40 ℃ for different time and then DC electro-etched in 1 mol/L HC1＋2.5 mol/L H2SO4 electrolyte at 80 ℃. The pitting potential and self corrosion potential of A1 foil were measured with polarization curves （PC）. The potentiostatic current--time curve was recorded and the surface and cross section images of etched A1 foil were observed with SEM. The electrochemical impedance spectroscopy （EIS） of etched A1 foil and potential transient curves （PTC） during initial etching stage were measured. The results show the chemical pretreatments can activate A1 foil surface, facilitate the absorption, diffusion and migration of C1- onto the A1 foil during etching, and improve the initiation rate of meta-stable pits and density of stable pits and tunnels, leading to much increase in the real surface area and special capacitance of etched A1 foil.
基金Project (51172102) supported by the National Natural Science Foundation of ChinaProject (BS2011CL011) supported by Promotive Research Fund for Young and Middle-aged Scientists of Shandong Province(doctor fund),China
文摘The Al foil for high voltage Al electrolytic capacitor usage was immersed in 5.0%NaOH solution containing trace amount of Zn2＋and Zn was chemically plated on its surface through an immersion-reduction reaction. Such Zn-deposited Al foil was quickly transferred into HCl-H 2 SO 4 solution for DC-etching. The effects of Zn impurity on the surface and cross-section etching morphologies and electrochemical behavior of Al foil were investigated by SEM, polarization curve （PC） and electrochemical impedance spectroscopy （EIS）. The special capacitance of 100 V formation voltage of etched foil was measured. The results show that the chemical plating Zn on Al substrate in alkali solution can reduce the pitting corrosion resistance, enhance the pitting current density and improve the density and uniform distribution of pits and tunnels due to formation of the micro Zn-Al galvanic local cells. The special capacitance of etched foil grows with the increase of Zn2＋concentration.
基金Project supported by University New Materials Disciplines Construction Program of Beijing Region
文摘Aluminum capacitor foils with a tunnel etch structure were reacted with boiling water and then anodized at 530 V in boric acid solution or boric acid＋citric acid mixed solution.The microstructure and crystallinity of the resulting anodized film were examined by TEM and XRD.The special capacitance,resistance and withstanding voltage of the film were explored with electrochemical impedance spectroscopy（EIS）,LCR meter and small-current charging.The results show that the high voltage anodized oxide film consists of an inner layer with high crystallinity and an outer layer with low crystallinity.However,the crystallinity of the film formed in boric acid＋citric acid mixed solution is higher than that of the film formed in only boric acid solution,leading to an increase in film＇s field strength and special capacitance.Meanwhile,there are more defects from phase transformation in the out layer of the film formed in boric acid＋citric acid mixed solution than in that of film formed in only boric acid solution,leading to a decrease in film＇s resistance and withstanding voltage.
基金Project (51172102/E020801) supported by the National Natural Science Foundation of ChinaProject (31805) supported by Doctoral Fund of Liaocheng University, China
文摘Ni coating was deposited on carbon steel by a mechanical attrition enhanced electroplating （MAEE） process. During the electroplating, the mechanical attrition（MA） was introduced by impact of glass balls on the sample surface with a special vibrating frequency. The surface and cross-sectional images of Ni coating were observed with SEM. The microstructure and crystallinity of coating were examined with TEM and XRD. The electrochemical performance of coating was measured with polarization curves and electrochemical impedance spectroscopy （EIS） and its mechanical behaviours, such as tensile strength and hardness, were studied. The results show that the MA has significant effects on the microstructure and property of the electroplated Ni coating. By MA, the coating becomes smooth, compact, thin and has refined grains and is free of cracks and pores. Consequently, the adhesion, tensile strength, hardness and corrosion resistance of coating are improved significantly.