Pd/Co_(2)MnSi(CMS)/Co/Pd multilayer films were designed based on the idea of combining highly spin-polarized materials with strong perpendicular magnetic anisotropy(PMA)films.The PMA of Pd/CMS/Co/Pd multilayer films was studied by optimizing the growth conditions and thickness of each film layer.The optimal structure of the multilayer films was Pd(6 nm)/CMS(5 nm)/Co(2 nm)/Pd(1 nm).Its abnormal Hall resistance(R_(Hall)),coercivity(H_(c))and effective magnetic anisotropy constant(Keff)are 0.08Ω,284 Oe and 1.36 Merg/cm^(3),respectively,which are 100%,492%,and 183%higher than the corresponding values(0.04Ω,48 Oe,and 0.48 Merg/cm^(3))of the Pd(6 nm)/Co(1 nm)/Pd(3 nm)trilayer films.The analysis shows that the increases of the above values are the result of the Pd/CMS interface effect and CMS/Co interface ferromagnetic(FM)coupling,and that it is closely related to the thickness of each film layer in the multilayer films and the growth conditions of the multilayer films.