摘要
This study investigates the effect of the deformation mode on the precipitation behavior of an extruded Mg-8.0Al-0.5Zn-0.2Mn(AZ80)alloy.The alloy samples are compared after the application of 3.5%tension and 3.5%compression along the extrusion direction to induce slip-dominant and twinning-dominant deformation modes,respectively.The pre-compressed(PC)sample,which contained numerous{10-12}tension twins,has a reduced grain size and a higher internal strain than the pre-tensioned(PT)sample,which is attributed to the inherent internal strain that occurs during the formation and growth of the twins.As a result,the precipitation behavior of the PC sample is accelerated,leading to its short peak aging time of 32 h,which is lower than those of the PT and as-extruded samples(48 and 100 h,respectively).Furthermore,fine continuous precipitates(CPs)rapidly form within the{10-12}twins,contributing to the enhanced hardness.Discontinuous precipitates(DPs),which have a hardness comparable to the CP-containing twinned regions,in the PC sample experience less coarsening during aging than those in the PT sample due to growth inhibition by the{10-12}twins.Ultimately,the{10-12}twins generated under the twinning-dominant deformation condition lead to enhanced precipitation behaviors,including the preferential formation and refinement of CPs and the suppressed coarsening of DPs.Consequently,pre-deformation that occurs{10-12}twinning exhibits more pronounced effects on precipitation acceleration and microstructural modification than slip-inducing pre-deformation.
基金
supported by the National Research Foundation of Korea(NRF)grants funded by the Korea government(MSIT)(Nos.RS-2024-00351052 and RS-2024-00450561).