摘要
The practical application of all-inorganic semiconductor lead halide perovskite nanocrystals(LHP NCs)has been limited by their poor stability.Recently,a lot of research on core-shell structure has been done to improve the stability of perovskite NCs,but the effect was far from the application requirements.Herein,we,for the first time,report a convenient approach to synthesize organic-inorganic double shell CsPbBr_(3)@SiO_(2)@polystyrene(PS)NCs with an inter-core of CsPbBr_(3),the intermediate layer of SiO_(2)shell,and outmost PS shell.Particularly,the CsPbBr_(3)@SiO_(2)@PS NCs maintained more than 90%of their initial photoluminescence(PL)intensity under one month's ultraviolet lamp irradiation or in 85℃ and 85%relative humidity(RH)condition.The white-light-emitting-diodes(WLEDs)were fabricated by encapsulating commercial InGaN chip with CsPbBr_(3)@SiO_(2)@PS NCs and K2SiF6:Mn^(4+)(KSF:Mn^(4+))phosphor with a luminous efficacy of~100 lm/W at 20 mA current and a color gamut of 128%of the National Television Standards Committee(NTSC)standard.In addition,these WLEDs still maintain 91%of the initial luminous efficacy after 1200 h of continuous lighting.These results demonstrated that double shell-protected CsPbBr_(3)perovskite NCs have great potential in the field of WLEDs.
基金
This work was supported by the Priority Research Project of Xiamen(No.3502Z20191015)
the Science and Technology Major Project of Fujian Province(No.2021HZ021013)
the Major Research Project of Mindu Innovation Laboratory(No.2021ZZ114).