摘要
针对多膛炉焙烧氧化锌烟尘氟氯脱除率低的问题,开展氧化锌烟尘焙烧过程热力学分析,基于热力学分析结果进行试验验证。研究结果表明:在烟气流量400 mL/min,烟气成分为SO_(2)0.32%、O_(2)7.61%、H_(2)O 9.61%、N_(2)82.46%(烟气成分为模拟回转窑烟气),焙烧温度700℃,焙烧时间210 min的较优条件下,氟氯的脱除率分别为98.06%、91.56%。
To address low removal rate of fluorine and chlorine from zinc oxide flue dust roasted in multi hearth furnace,thermodynamic analysis of zinc oxide flue dust roasting process was carried out,and experimental verification was carried out based on thermodynamic analysis results.The results show that removal rates of fluorine and chlorine is 98.06% and 91.56% respectively under the condition including flue gas flow of 400 mL/min,flue gas components of SO_(2)0.32%,O_(2)7.61%,H;O 9.61%,N_(2)82.46%(simulation of flue gas of rotary kiln),roasting temperature of 700℃,and roasting time of 210 min.
作者
吴星琳
林泓富
张恒星
陈杭
匡晨
衷水平
迟晓鹏
WU Xing-lin;LIN Hong-fu;ZHANG Heng-xing;CHEN Hang;KUANG Chen;ZHONG Shui-ping;CHI Xiao-peng(Xiamen Zijin Mining and Metallurgy Technology Co.,Ltd.,Xiamen 361115,Fujian,China;Zijin Mining Group Co.,Shanghang 364200,Fujian,China;Central South University,Changsha 410083,China;Kunming University of Technology,Kunming 650500,China;Zijin School of Mining,Fuzhou University,Fuzhou 350108,China)
出处
《有色金属（冶炼部分）》
CAS
北大核心
2022年第2期21-26,共6页
Nonferrous Metals（Extractive Metallurgy)
基金
国家重点研发计划项目(2018YFC1900405)。
关键词
氧化锌烟尘
焙烧
多膛炉
氟
氯
热力学
zinc oxide dust
roasting
multi hearth furnace
fluorine
chlorine
thermodynamics