摘要
The oxidation behaviors of AZ80,AZ8O-0.32 Y and AZ8O-0.38 Nd(wt.%)alloys were researched at 413℃,420℃,427v and 433℃for up to 6 h in air environment via a high precision analytical balance,a laser confocal microscope,differential scanning calorimeter(DSC)analysis,X-ray diffraction(XRD)analysis,scanning electron microscope(SEM)observation,and X-ray photoelectron spectroscopy(XPS)analysis.The results show that the weight gain and oxidation rate of AZ80 are reduced significantly,the initiation form and propagation of cracks in oxide layer are changed.Compact and protective oxide layer forms on alloy surface with Y or Nd addition.And the activation energies of AZ80,AZ80-0.32Y and AZ8O-0.38Nd alloys calculated via Arrhenius equation are 82.556 kJ/mol,177.148kJ/mol and 136.738 kJ/mol,respectively.
基金
the National Key Research and Development Program of China(No.2016YFB0301104)
Nation Natural Science Foundation of China(No.51771043)
Foundation of State Key Laboratory of Baiyunobo Rare Earth researches and Comprehensive Utilization,and Programme of Introducing Talents of Discipline Innovation to Universities 2.0(the 111 Project 2.0 of China,No.BP0719037).