The ZSM-22 and ZSM-35 zeolites were synthesized via the hydrothermal crystallization method. The samples were characterized by XRD, SEM, N_2 adsorption-desorption, NH_3-TPD, TPO, TG, and Raman spectrometry, and the results showed that ZSM-22 and ZSM-35 possessed similar microporous volume and acidity. In the alkylation of benzene with methanol, ZSM-22 and ZSM-35 showed different coke location, coking rate and graphitizing degree. Compared with the industrial ZSM-5, ZSM-22 and ZSM-35 both showed higher selectivity of toluene and xylene(93.63% and 96.50%,respectively) during the alkylation of benzene with methanol, and the selectivity of para-xylene in xylene isomers was51.96% and 41.45%, respectively. Meanwhile, the selectivity of ethylbenzene and C_9^+ aromatics was also lower than that of industrial ZSM-5.
The ZSM-22 and ZSM-35 zeolites were synthesized via the hydrothermal crystallization method. The samples were characterized by XRD, SEM, N_2 adsorption-desorption, NH_3-TPD, TPO, TG, and Raman spectrometry, and the results showed that ZSM-22 and ZSM-35 possessed similar microporous volume and acidity. In the alkylation of benzene with methanol, ZSM-22 and ZSM-35 showed different coke location, coking rate and graphitizing degree. Compared with the industrial ZSM-5, ZSM-22 and ZSM-35 both showed higher selectivity of toluene and xylene(93.63% and 96.50%,respectively) during the alkylation of benzene with methanol, and the selectivity of para-xylene in xylene isomers was51.96% and 41.45%, respectively. Meanwhile, the selectivity of ethylbenzene and C_9^+ aromatics was also lower than that of industrial ZSM-5.
基金
financial support from the National Natural Science Foundation of China (No.2177061270)