围绕着开发可溶液法加工非聚(3,4-乙烯二氧噻吩单体):聚苯乙烯磺酸钠(poly(3,4-ethylendioxythiophene):poly(sodium-p-styrenesulfonate),PEDOT:PSS)电极界面修饰材料的核心目的,研究了基于磷钼酸(phosphomolybdic acid,PMA)和纳米氧化钼(Mo O3)复合物的新型空穴传输材料.通过将PMA溶液和Mo O3纳米粒子溶液进行混合,制备了复合墨水(PMA:Mo O3).该复合墨水在有机活性层表面具有很好的浸润性和成膜性.利用PMA:Mo O3复合空穴传输层(hole transport layer,HTL)制备的倒置P3HT:PC61BM光伏器件的开路电压和填充因子(fill factor,FF)均比基于单一PMA或Mo O3制备的器件有所提升.进一步优化了PMA:Mo O3复合墨水中两个组分间的比例,发现当复合墨水中Mo O3的含量为66%时,器件性能达到最优,其光电转换效率(power conversion efficiency,PCE)为3.71%.成功验证了利用金属氧化物与多金属氧簇(polyoxometalate,POM)复合物作为电极界面缓冲层制备有机太阳能电池的可行性,为开发新型电极界面修饰材料提供了一个新的研究思路.
To develop PEDOT：PSS（poly（3,4-ethylendioxythiophene）：poly（sodium-pstyrenesulfonate）—hole transporting materials in polymer solar cells, a solution-processable nanocomposite ink based on MoO3 nano-particles and phosphomolybdic acid（PMA） is reported. The PMA：MoO3 composite ink can be easily prepared by simply mixing PMA and MoO3 solutions in different weight ratios. This PMA：MoO3 composite ink shows good wettability on polymer surface. A smooth and homogeneous thin film can be easily deposited on polymer surface via a spin-coating process without any surface treatment.Both open circuit voltage（VOC） and fill factor（FF） of the PMA：MoO3-based P3 HT：PC61 BM cells are higher than that based on PMA or MoO3 cells. Influence of the blend ratio between PMA and MoO3 on solar cell performance was carried out, and the optimized best blend ratio was found to be 1∶2 for PMA：MoO3, with which a highest device performance of 3.71% was achieved. The current work demonstrates that nanocomposite of metal oxide and polyoxometalate（POM） can serve as an excellent electrode buffer layer for solutionprocessed organic electronics.
作者
王宜玲
伊金垛
骆群
谢中明
李艳青
马昌期
罗立强
WANG Yiling;YI Jinduo;LUO Qun;XIE Zhongrning;LI Yanqing;MA Changqi;LUO Liqiang(College of Sciences, Shanghai University, Shanghai 200444, China;Printable Electronics Research Center, Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Sciences, Suzhou 215123, Jiangsu, China;Collaborative Innovation Center of Suzhou Nano Science and Technology, Institute of Functional Nano and Soft Materials, Soochow University, Suzhou 215123, Jiangsu, China)
出处
《上海大学学报（自然科学版）》
CAS
CSCD
北大核心
2018年第2期225-235,共11页
Journal of Shanghai University:Natural Science Edition
基金
国家自然科学基金资助项目(61306073
61571278)
江苏省自然科学基金资助项目(BK20130346)
中国科学院战略重点研究资助项目(XDA09020201)