摘要
为了改善方镁石-尖晶石质耐火材料的性能,以高纯镁砂颗粒(5~2和≤2 mm)、电熔镁砂细粉(≤0.088 mm)和预合成烧结富镁尖晶石(≤1 mm)为主要原料,以Y-PSZ为添加剂,经1 650℃保温3 h烧成了方镁石-尖晶石试样,研究了Y-PSZ加入量(w)为0、0.5%、1.0%、1.5%、2.0%时对该材料性能的影响。采用国标进行各项性能检测,采用X射线衍射仪和扫描电镜-能谱仪做显微结构分析。结果表明:1)烧成后,Zr O2由单斜相转变为四方相;2)随着Y-PSZ的加入,试样的抗热震性得到显著提高;3)从显微结构照片可以看出,加入Y-PSZ后方镁石晶粒明显长大,同时试样的断裂机制由穿晶断裂转变为沿晶断裂。当Y-PSZ的加入量(w)为0.5%~1.0%时,试样的综合性能最优。
In order to improve the properties of periclase-spinel refractories,the specimens were prepared using high purity magnesia particle （5 -2, ≤2 ram） ,fused magnesia fines （ ≤0. 088 mm） ,and pre-synthe- sized sintered magnesia-rich spinel （ ≤1 mm） as starting materials,Y-PSZ as an additive,fired at 1 650 ≤3 for 3 h. Effects of Y- PSZ additions （0,0.5 %, 1.0%, 1.5 %, and 2.0%, by mass, the same hereinafter） on properties of the specimens were researched. The results reveal that. （1） after sintering,ZrO2 transforms from monoclinic to tetragonal; （2） adding Y-PSZ,the thermal shock resistance improves obviously; （3） ac- cording to microstructure, adding Y-PSZ, the periclase grains grow greatly, and the fracture mechanism changes from transgranular fracture to intergranular fracture. The properties of specimen are the optimal with 0.5% - 1.0% Y-PSZ.
出处
《耐火材料》
CAS
北大核心
2017年第2期118-122,共5页
Refractories
基金
2015年国家级大学生创新创业训练计划项目(201510488001)
关键词
Y—PSZ
方镁石-镁铝尖晶石
相变增韧
yttrium-partial stabilized zirconia
periclase-magnesium aluminate spinel
phase transformationtoughening