摘要
对5052铝合金板进行了多道次模压(GP)变形,研究了GP变形道次对其显微组织和室温拉伸性能的影响。结果表明:该铝合金的平均晶粒尺寸随GP变形道次的增加而减小,4道次变形后平均晶粒尺寸由未变形的43.2μm细化到约1.1μm;抗拉强度随GP变形道次的增加而单调递增,伸长率则先快速下降后缓慢升高;4道次GP变形能使5052铝合金在提高抗拉强度的同时保持良好的塑性。
The 5052 aluminum alloy sheets were processed by the groove pressing（GP）deformation for multi-passes,and the effects of the GP deformation passes on the microstructure and tensile properties at room temperature were studied.The results show that the average grain size of the aluminum alloy decreased with the increase of the GP deformation passes.After deformation for four passes the average grain size was reduced from undeformed 43.2μm to about 1.1μm.The tensile strength monotonously increased with the increase of the GP deformation passes while the elongation first decreased rapidly then increased slowly.The process of GP deformation for four passes can improve the tensile strength and simultaneously maintained the good plasticity of the 5052 aluminum alloy.
出处
《机械工程材料》
CAS
CSCD
北大核心
2016年第4期1-4,共4页
Materials For Mechanical Engineering
基金
广西大学广西有色金属及特色材料加工重点实验室开放基金资助项目(GXKFJ14-02)
福建省高校杰出青年科研人才培育计划资助项目(JA14371)
福建省交通厅重点项目(201210)
关键词
模压变形
5052铝合金
显微组织
拉伸性能
groove pressing deformation
5052 aluminum alloy
microstructure
tensile property