通过浸渍法制备了Mn/Zr O2(Y2O3)催化剂,并对其CO催化氧化性能进行研究。研究表明经过350℃煅烧且不预处理的负载12%Mn的催化剂,具有较高的催化活性。催化剂催化氧化的起燃温度T50=104℃,完全反应温度为T95=142℃,该催化剂显示了较好的CO催化氧化活性。
Mn / Zr O2（ Y2O3） catalyst was prepared by impregnation method. The catalytic oxidation for CO was studied. The results showed that the catalyst of the load 12% Mn,which was calcined at 350 ℃ and without pretreatment,it＇s catalytic activity was higher. The catalyst by starting temperature was T50= 104 ℃,the all- reaction temperature was T95= 142 ℃,shown the best catalytic activity.