Mass loss and direct reduction characteristics of iron ore-coal composite pellets under different technological parameters were investigated. Meanwhile, changes of iron phase at different temperatures were analyzed by using X-ray diffraction （XRD）, and characteristics of crushed products were studied by using a scanning electron microscope （SEM）. The results showed that heating rate had little influence on the reduction, but the temperature played an important role in the reduction process. The mass loss rate increased rapidly from 800 to 1 100 ℃. The reduction process can be divided into three steps which correspond to different temperature ranges. Fe2 03 began to transform into Fe304 below 500 ℃, and FeO was reduced into Fe from 900 ℃. At 900 ℃, the reduction product showed a clear porous structure, which promoted the reduction progress. At 1000 ℃, the metallic Fe dominated the sample, and the reduction reached a very high degree.
Mass loss and direct reduction characteristics of iron ore-coal composite pellets under different technological parameters were investigated. Meanwhile, changes of iron phase at different temperatures were analyzed by using X-ray diffraction （XRD）, and characteristics of crushed products were studied by using a scanning electron microscope （SEM）. The results showed that heating rate had little influence on the reduction, but the temperature played an important role in the reduction process. The mass loss rate increased rapidly from 800 to 1 100 ℃. The reduction process can be divided into three steps which correspond to different temperature ranges. Fe2 03 began to transform into Fe304 below 500 ℃, and FeO was reduced into Fe from 900 ℃. At 900 ℃, the reduction product showed a clear porous structure, which promoted the reduction progress. At 1000 ℃, the metallic Fe dominated the sample, and the reduction reached a very high degree.
基金
Sponsored by Fundamental Research Funds for the Central Universities of China(FRF-SD-12-007B)
National Science and Technology Support Plan in the 12th Five-year of China(2011BAE13B09)