Wire electrical explosion may result in the existence of micro-sized large particles in powders while current injection ways may influence the size and content of micro-sized large particles. Therefore, two kinds of electrical explosion devices with different electrodes by gas discharge were designed in this paper. The pole-board electrodes and the cone electrodes were used respectively for studying copper wire electrical explosion process. The current and voltage data were measured with the Rogowski coil and high voltage probe. The results show that the pulverizing process of electrical explosion is more efficient when the wire electrode current density injected into the cone electrodes is approximately twice as much as the pole-board electrodes. The content of micro-sized large particles is the least among the products of the electrical explosion, when the total deposition energy of the wire prior to vaporization stage is 2. 5 times larger than that of the theoretical value of the completed vaporization.
Wire electrical explosion may result in the existence of micro-sized large particles in powders while current injection ways may influence the size and content of micro-sized large particles. Therefore, two kinds of electrical explosion devices with different electrodes by gas discharge were designed in this paper. The pole-board electrodes and the cone electrodes were used respectively for studying copper wire electrical explosion process. The current and voltage data were measured with the Rogowski coil and high voltage probe. The results show that the pulverizing process of electrical explosion is more efficient when the wire electrode current density injected into the cone electrodes is approximately twice as much as the pole-board electrodes. The content of micro-sized large particles is the least among the products of the electrical explosion, when the total deposition energy of the wire prior to vaporization stage is 2. 5 times larger than that of the theoretical value of the completed vaporization.
基金
This research was supported by National Natural Science Foundation of China （No. 51061011 ）.