With high effective screen-printing technique, a new triode field emission display (FED)with enhanced petaling cold cathode was fabricated. For enhancing the field emission performance,a series of improved measures was adopted in the fabrication course. Seen from the fabrication structure of enhanced petaling cold cathode,the bar conducting electrode and the petaling bottom electrode were fabricated with the sintered silver slurry on cathode glass faceplate. The luminescence image with green phosphor was displayed for the sealed enhanced petaling cold cathode FED. The measured results showed that the enhanced petaling cold cathode had good field emission performance. The enhanced petaling cold cathode FED possessed low turn-on electric-field of 1. 95 V /μm,large emission current of 1 389. 6 μA,and high luminance brightness of 1 520 cd /m2 .
With high effective screen-printing technique, a new triode field emission display （FED）with enhanced petaling cold cathode was fabricated. For enhancing the field emission performance,a series of improved measures was adopted in the fabrication course. Seen from the fabrication structure of enhanced petaling cold cathode,the bar conducting electrode and the petaling bottom electrode were fabricated with the sintered silver slurry on cathode glass faceplate. The luminescence image with green phosphor was displayed for the sealed enhanced petaling cold cathode FED. The measured results showed that the enhanced petaling cold cathode had good field emission performance. The enhanced petaling cold cathode FED possessed low turn-on electric-field of 1. 95 V /μm,large emission current of 1 389. 6 μA,and high luminance brightness of 1 520 cd /m2 .
基金
National Natural Science Foundations of China(No.60976058,No.61274078)
Natural Science Research Project of Henan Province Education Department,China(No.2009B510019)