摘要
The phenomenon of stress-induced recrystallization (SIR) and recrystallization- induced plasticity (RIP) in DT4 pure iron was investigated by means of hightemperature tensile test under a constant elastic stress and microstructural observation. It is shown that the macroscopic plastic flow of cold-rolled specimens, which occured during heating process under pre-loaded elastic stress, resulted from stressinduced recrystallization and recrystallization-induced plasticity. The characteristics and mechanism of this phenomenon were also preliminarily discussed.
The phenomenon of stress-induced recrystallization (SIR) and recrystallization- induced plasticity (RIP) in DT4 pure iron was investigated by means of hightemperature tensile test under a constant elastic stress and microstructural observation. It is shown that the macroscopic plastic flow of cold-rolled specimens, which occured during heating process under pre-loaded elastic stress, resulted from stressinduced recrystallization and recrystallization-induced plasticity. The characteristics and mechanism of this phenomenon were also preliminarily discussed.