2E12铝合金热变形过程中的动态软化机制 被引量:4

Dynamic Softening Mechanism of 2E12 Aluminum Alloy during Hot Deformation
在线阅读 下载PDF
导出
摘要 用Gleeble-1500型热模拟试验机对2E12铝合金进行了等温热压缩试验,对热变形后的显微组织进行了透射电镜和场发射扫描电镜观察,研究了2E12合金在不同条件下热变形过程中的动态软化机制及其显微组织演化规律。结果表明:在变形温度不高于400℃时,合金的主要动态软化机制为动态回复;而当变形温度不低于450℃时,其主要的动态软化机制为连续动态再结晶,亚晶扭转合并为动态再结晶的主要形核机制,且沿原始晶界优先形核。 Isothermal hot compression test of 2E12 aluminum alloy was operated on Gleeble-1500 thermal simulation test machine. Microstructure after hot deformation of the alloy was observed by TEM and FE-SEM. Dynamic softening mechanism and microstructure evolution regular of the alloy during hot deformation under different conditions were studied. The results show that when deformation temperature was below 400℃, the main softening mechanism of the alloy was the dynamic recovery. When deformation temperature was above 450℃, the major softening mechanism was continuous dynamic recrystallization(CDRX). The major nucleation mechanism of the alloy dynamic recrystallization was subgrain turning merging and alloy nucleated preferentially along original grain boundary.
出处 《机械工程材料》 CAS CSCD 北大核心 2011年第10期22-27,共6页 Materials For Mechanical Engineering
基金 国家重点基础研究发展规划项目(2005CB623705) 国家自然科学基金资助项目(50871123)
关键词 2E12铝合金 显微组织 动态软化机制 热变形 2E12 aluminum alloy microstrueture dynamic softening mechanism hot deformation
  • 相关文献

参考文献27

  • 1GOURDET S, MONTHEILLET F. An experimental study of the recrystallization mechanism during hot deformation of aluminum[J]. Materials Science and Engineering A, 2000, 283: 274-288.
  • 2MCQUEEN H J. Development of dynamic recrystallization theory[J]. Materials Science and Engineering A, 2004, 387/ 389 : 203-208.
  • 3KASSNER M E, BARRABES S R. New development of geometric dynamic recrystallization[J]. Materials Science and Engineering A, 2005,410/411 : 152 155.
  • 4MCQUEEN H J, POSCHMANN I. Subgrain development in hot working of Al and Al-5Mg[J]. Materials Science and Engineering A, 1997,234/236 : 830-833.
  • 5BAXTER G J, FURU T, ZHU Q, et al. The influence of transient strain-rate deformation conditions on the deformed microstructure of aluminum alloy Al-1 %Mg [J]. Acta Mater, 1999,47(8) :2367 -2376.
  • 6FURU T, SHERCLIFF H R, BAXTER G J,et al. The influence of transient deformation conditions on recrystallization during thermomechanical processing of Al-1% Mg alloy [J ]. Acta Materialia, 1999,47(8) :2377-2389.
  • 7BLUM W, ZHU Q, MERKEI. R, et al. Geometric dynamic recrystallization in hot torsion of Al-SMg-0. 6Mn (AA5083) [J]. Materials Science and Engineering A, 1996,205 : 23-30.
  • 8GOURDET S, MONTHEILLET F. A model of continuous dynamic recrystallization[J]. Acta Materialia, 2003, 51: 2685- 2699.
  • 9SAKAI T, MIURA H, GOLOBRODKO A,et al. Continuous dynamic recrystallization during the transient severe deformation of aluminum alloy 7475[J]. Acta Materialia, 2009,57 (1):153-163.
  • 10KAIBYSHEV R, SITDIKOV O, GOLOBORODKO A, et al. Grain refinement in as-cast 7475 aluminum alloy under hot deformation[J]. Materials Science and Engineering A, 2003, 344:348-356.

二级参考文献106

  • 1杨守杰,戴圣龙.航空铝合金的发展回顾与展望[J].材料导报,2005,19(2):76-80. 被引量:206
  • 2陈文.先进铝合金在A380上的应用[J].航空维修与工程,2005(2):40-41. 被引量:42
  • 3单凤兰,李吉学.形变铜中位错组态的电镜分析[J].电子显微学报,1995,14(3):186-188. 被引量:2
  • 4白秉哲.清华大学博士学位论文[M].,1991..
  • 5刘庆.哈尔滨工业大学博士学位论文[M].,1991..
  • 6Suresh.材料的疲劳[M].北京:国防工业出版社,1999..
  • 7SELLARS C M. Modelling microstmetural development during hot rolling[J]. Mater Sci Technol, 1990, 16(11): 1072-1078.
  • 8HIRSCH J. Thermomechanical control in aluminium sheet production[J]. Materials Science Forum, 2003, 426(1 ): 185 - 194.
  • 9JAKOBSEN B, POULSEN H F, LIENERT U. Formation and subdivision of deformation structures[J]. Science, 2006, 312: 889-892.
  • 10HIRSTH J. Virtual fabrication of aluminum products-microstructure modeling in industrial aluminum production[M]. Weinheim: WILEY-VCH Veflag GmbH&Co KgaA, 2006: 83-110.

共引文献153

同被引文献26

引证文献4

二级引证文献12

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部