摘要
采用化学镀技术对聚酰胺6织物进行表面处理,借助SEM和XRD对镀层表面形貌与结构进行分析,探讨化学镀前后聚酰胺6织物的厚度、拉伸断裂强力、悬垂性、抗弯刚度、透气性、抗紫外性能以及表面电阻。结果表明:通过化学镀可以获得颗粒分布均匀的镀银层,且织物表面镀覆的是纯度很高的单质银;表面方阻开始时随着增重率的增加急剧减小,当增重率大于30%时方阻减小趋势变缓;化学镀银使织物的抗紫外性能、拉伸断裂强力、抗弯刚度及悬垂性增加,而透气性有所下降。
Polyamide 6 fabric is treated on the surface by electroless plating,the fabric is investigated by SEM and XRD to characterize its surface morphology and structure systematic investigations,including thickness,tensile strength,fabric draping,fabric stiffness,wrinkle-resistant property,air permeability,anti-ultraviolet property and surface resistance are carried out before and after electroless sliver plating.The results show that the particles of the metal-layer are high purity sliver and evenly distributed on the surface of fabric,the fabric surface resistance decreases greatly when the rate of mass gain increases at the beginning.However,the surface resistance reduces slightly when the rate of mass gain is over 30%.The Ag-plated polyamide fabric has higher anti-ultraviolet property,tensile strength,stiffness and draping,but lower air permeability than the original fabric.
出处
《浙江理工大学学报（自然科学版）》
2011年第4期515-518,共4页
Journal of Zhejiang Sci-Tech University(Natural Sciences)
基金
浙江省质量技术监督系统科研计划项目(重大20090105)
长江学者和创新团队发展计划项目(IRT0654)
关键词
化学镀银
聚酰胺6织物
织物性能
electroless sliver plating
PA6 fabric
fabric properties