摘要
Background Biphasic calcium phosphate （BCP） ceramics has a potential advantage as an osteoconductive matrix and has an optimal resorption rate for bone formation. Using BCP ceramics as a bone graft during spinal fusion requires osteogenesis within the material and subsequent bridging between adjacent vertebraes to provide long-term support. Bisphosphonates have been reported to prolong the process of bone healing. The influence of bisphosphonate treatment on bone formation within BCP ceramics in spinal fusion remains unknown. The aim of this study was to evaluate the influence of alendronate on BCP osteoaenesis in Dosterolateral spinal fusion.Methods Posterolateral spinal fusion with pedicle screw fixation was performed at the lumbar spine in twenty-two pigs. BCP ceramics were applied as a bone graft to obtain bone fusion between adjacent transverse processes. Eleven pigs in the treatment group received oral alendronate 10 mg/d for three months postoperatively. Eleven pigs in the control group did not receive treatment with alendronate. All animals underwent posterolateral spinal fusion with BCP ceramics. The fusion rate was evaluated three months after the operation.Results The fusion rates evaluated by X-ray were 27.3% in the treatment group and 20% in the control group. The fusion rates using histological evaluation were 18.2% in the treatment group and 20% in the control group. The mean volumes of fusion mass were （3.64±0.86） cm^3 in the treatment group and （4.26±0.63） cm^3 in the control group. No significant differences were found in either trabecular bone volume or residual BCP volume between treatment and control groups using histological evaluation. The new bone formation within BCP ceramics was greater in the area adjacent to transverse process （P 〈0.01）.Conclusion Oral alendronate with a dose of 10 mg daily do not inhibit bone formation within BCP ceramics or affect the fusion rate in posterolateral spinal fusion from porcine models.
Background Biphasic calcium phosphate （BCP） ceramics has a potential advantage as an osteoconductive matrix and has an optimal resorption rate for bone formation. Using BCP ceramics as a bone graft during spinal fusion requires osteogenesis within the material and subsequent bridging between adjacent vertebraes to provide long-term support. Bisphosphonates have been reported to prolong the process of bone healing. The influence of bisphosphonate treatment on bone formation within BCP ceramics in spinal fusion remains unknown. The aim of this study was to evaluate the influence of alendronate on BCP osteoaenesis in Dosterolateral spinal fusion.Methods Posterolateral spinal fusion with pedicle screw fixation was performed at the lumbar spine in twenty-two pigs. BCP ceramics were applied as a bone graft to obtain bone fusion between adjacent transverse processes. Eleven pigs in the treatment group received oral alendronate 10 mg/d for three months postoperatively. Eleven pigs in the control group did not receive treatment with alendronate. All animals underwent posterolateral spinal fusion with BCP ceramics. The fusion rate was evaluated three months after the operation.Results The fusion rates evaluated by X-ray were 27.3% in the treatment group and 20% in the control group. The fusion rates using histological evaluation were 18.2% in the treatment group and 20% in the control group. The mean volumes of fusion mass were （3.64±0.86） cm^3 in the treatment group and （4.26±0.63） cm^3 in the control group. No significant differences were found in either trabecular bone volume or residual BCP volume between treatment and control groups using histological evaluation. The new bone formation within BCP ceramics was greater in the area adjacent to transverse process （P 〈0.01）.Conclusion Oral alendronate with a dose of 10 mg daily do not inhibit bone formation within BCP ceramics or affect the fusion rate in posterolateral spinal fusion from porcine models.
