Cerium-doped MCM-48 molecular sieves were synthesized hydrothermally and characterized by X-ray diffraction, nitrogen adsorption, transmission electron microscope, FT-IR spectroscopy, UV-visible spectroscopy, and Raman spectroscopy. The results showed that all the samples held the structure of MCM-48, and Ce could enter the framework of MCM-48. However, when Ce/Si molar ratio in the sampies was high （0.04 or 0.059）, there were CeO2 crystallites as secondary phase in the extraframework of MCM-48. Ce-doped MCM-48 was a very efficient catalyst for the oxidation of cyclohexane in a solvent-free system with oxygen as an oxidant. In the conditions of 0.5 MPa 02 and 413 K for 5 h, the conversion of cyclohexane was 8.1% over Ce-MCM-48-0.02, the total selectivity of cyclohexanol and cyclohaxnone was 98.7%. With an increase of Ce content, the conversion of cyclohexane and the selectivity to cyclohexanol decreased somewhat, but the selectivity to cyclohexanone increased.
Cerium-doped MCM-48 molecular sieves were synthesized hydrothermally and characterized by X-ray diffraction, nitrogen adsorption, transmission electron microscope, FT-IR spectroscopy, UV-visible spectroscopy, and Raman spectroscopy. The results showed that all the samples held the structure of MCM-48, and Ce could enter the framework of MCM-48. However, when Ce/Si molar ratio in the sampies was high （0.04 or 0.059）, there were CeO2 crystallites as secondary phase in the extraframework of MCM-48. Ce-doped MCM-48 was a very efficient catalyst for the oxidation of cyclohexane in a solvent-free system with oxygen as an oxidant. In the conditions of 0.5 MPa 02 and 413 K for 5 h, the conversion of cyclohexane was 8.1% over Ce-MCM-48-0.02, the total selectivity of cyclohexanol and cyclohaxnone was 98.7%. With an increase of Ce content, the conversion of cyclohexane and the selectivity to cyclohexanol decreased somewhat, but the selectivity to cyclohexanone increased.
基金
the National Basic Research Program of China (2004CB719500)
the Commission of Science and Technology of Shanghai Municipality (06DJ14006)
Shanghai Municipal Education Commission (2008CG35)