摘要
Sintered Sm（Coba1FexCu0.1Zr0.03）7.5 （x=0.09-0.21） permanent magnets with higher Fe content were found to have higher remanence Br and maximum energy product （BH）max at room temperature. Br and （BH）max reached maximum of 0.96 T and 176.7 kJ/m^3, respectively at room temperature when the Fe content x reached 0.21. However, the intrinsic coercivity Hci at room temperature increased gradually when the Fe content x increased from 0.09 to 0.15, but when x further increased to 0.21, Hcidecreased. Hci attained its peak value of 2276.6 kA/m with Fe content x=0.15 at room temperature. For magnets with x=0.15, Br, （BH）max and Hc1 reached 0.67 T, 81.2 kJ/m^3 and 509.4 kA/m at 500 ℃, respectively, showing good high temperature stability, which could be used in high temperature applications.
Sintered Sm（Coba1FexCu0.1Zr0.03）7.5 （x=0.09-0.21） permanent magnets with higher Fe content were found to have higher remanence Br and maximum energy product （BH）max at room temperature. Br and （BH）max reached maximum of 0.96 T and 176.7 kJ/m^3, respectively at room temperature when the Fe content x reached 0.21. However, the intrinsic coercivity Hci at room temperature increased gradually when the Fe content x increased from 0.09 to 0.15, but when x further increased to 0.21, Hcidecreased. Hci attained its peak value of 2276.6 kA/m with Fe content x=0.15 at room temperature. For magnets with x=0.15, Br, （BH）max and Hc1 reached 0.67 T, 81.2 kJ/m^3 and 509.4 kA/m at 500 ℃, respectively, showing good high temperature stability, which could be used in high temperature applications.
基金
the National Natural Science Foundation of China (90306015)
National Fund for Distinguished Young Scholars of China (60425102)