对A356合金流动性能进行测试。结果表明,下列条件测试结果较佳:采用复沟型金属流动测试仪;涂料涂刷厚度0.5mm^0.8mm,两次涂刷;熔体在720℃保温,30min^40min;浇铸温度为690℃;模具保温温度为60℃~80℃。
This article research measurements of A356 alloy fluidity testing, it shows that testing will have better results under those conditions., use multi- channels fluidity test apparatus; thickness of dope is 0.5-0.8mm, brush twice; hold melt temperature at 720℃, 30min-40min; casting at 690℃ ; hold mould temperature at 60℃- 80℃.