In view of the periodic bending deformation of solid-liquid interface in the solidification process for continuous casting slab, the variation of temperature gradient and dendritic spacing in the front edge of the solid-liquid interface, and the nucleation and propagation process of crack were studied. It is shown that the bending deformation of the interface results in the temperature field change in the front edge of solid-liquid interface, and the occurrence of temperature gradient along drawing direction results in the growth of secondary dendrites. The initial crack formed during the middle and final stage of solidification may extend to the surface of the casting slab and become an internal crack. The results of the theoretical analysis are basically in agreement with that of the experiment.
In view of the periodic bending deformation of solid-liquid interface in the solidification process for continuous casting slab, the variation of temperature gradient and dendritic spacing in the front edge of the solid-liquid interface, and the nucleation and propagation process of crack were studied. It is shown that the bending deformation of the interface results in the temperature field change in the front edge of solid-liquid interface, and the occurrence of temperature gradient along drawing direction results in the growth of secondary dendrites. The initial crack formed during the middle and final stage of solidification may extend to the surface of the casting slab and become an internal crack. The results of the theoretical analysis are basically in agreement with that of the experiment.
基金
supported by the National Natural Science Foundation of China(No.50374043).