摘要
对高强度PC钢丝断裂原因进行了分析,认为连铸坯的中心偏析、中心缩孔、疏松和夹杂是导致PC钢丝断裂的冶金原因;轧制过程中,较差的修磨质量、表面缺陷导致的微裂纹,过烧以及不适当的冷却速度导致的非正常显微组织,盘条头部的耳子、盘条本身折叠是导致PC钢丝断裂的主要原因;同时,不恰当的酸洗、较差的磷化及热处理质量、不适当拉丝裂纹的产生、拉拔模具安放不正导致的横裂也是PC钢丝断裂的原因。并且针对上述部分原因提出改进措施。
The fracture reasons of high strength PC steel wire are analyzed, it＇ s considered that center segreption, central cavitation, poriness and inclusion are the metallurgical reasons which lead to the facture of PC steel wire and in the rolling process, differential coping quality, microcrack caused by surface defect, abnormal microstructure caused by burnt and improper cooling velocity, the ears on the head of the wire, overlapping of the wiry rod itself are the main masons which lead to the facture of PC steel wire. At the same time, iratppropriate pickling, differential phosphorization quality, the had heat treatment quality, the generation of crack in the improper drawing and transverse crack caused by abnormal laying of the drawing die are also the reasons of the cracking of PC wire. Improvement measures are put forward on the part reasons dascribed alive.
出处
《山东冶金》
CAS
2006年第6期36-40,共5页
Shandong Metallurgy
关键词
PC钢丝
断裂
原因分析
改进措施
PC steel wire
fracture
reason analysis
improvement measures