摘要
Poly（St-co-BuA）/silica nanocomposite latexes were synthesized via conventional emulsion polymerization in the presence of 3-（trimethoxysilyl）propyl methacrylate modified colloidal nano-silica. The effects of surface property, particle size and content of colloidal nano-silica as well as the concentrations of monomer and surfactant on the morphology of nanocomposite latex particles were investigated by transmission electron microscope （TEM） and scanning electron microscope （SEM） in detail. Various interesting morphologies such as grape-like, Chinese gooseberry-like, pomegranate-like and normal core-shell structures were observed. Droplet nucleation mechanism competing with micelle nucleation mechanism was proposed to explain the morphological evolution of the nanocomposite particles.
Poly（St-co-BuA）/silica nanocomposite latexes were synthesized via conventional emulsion polymerization in the presence of 3-（trimethoxysilyl）propyl methacrylate modified colloidal nano-silica. The effects of surface property, particle size and content of colloidal nano-silica as well as the concentrations of monomer and surfactant on the morphology of nanocomposite latex particles were investigated by transmission electron microscope （TEM） and scanning electron microscope （SEM） in detail. Various interesting morphologies such as grape-like, Chinese gooseberry-like, pomegranate-like and normal core-shell structures were observed. Droplet nucleation mechanism competing with micelle nucleation mechanism was proposed to explain the morphological evolution of the nanocomposite particles.
基金
This research was financially supported by the Key Project of China Educational Ministry (No. 103064)the Doctoral Foundation of University (No. 20020246031)