The effects of rare earths with different contents on anti-degradation of Y base heavy rare earths-magnesium and cerium base light rare earths-magnesium nodular cast iron were studied. Curves of the relationship between the spheroidization grade of liguid iron treated by different nodulizers and holding time were obtained. The results show that the more the remains of the rare earth, the longer the anti-degradation time, the liquid iron was treated either by Y-Mg-Si or by Ce-Mg-Si nodulizer. When the rare earth remains are above certain quantity, the spheroidization grade starts to decline. When liquid iron treated by either Y-Mg-Si or Ce-Mg-Si nodulizer with proper remains of rare earths about 0.04% 0.06%（mass fraction）, the anti-degradation is the best, and the remains of Mg being about 0.04% -0.07% （mass fraction）. Rare earths-Mg nodulizer with moderate RE remains is better than that of Mg-Si nodulizer in anti-degradation property. However, Y-Mg-Si nodulizer with moderate remins of Re is better than Ce-Mg-Si nodulizer. Sometimes Ce-Mg- Si nodulizer can be used for the production of heavy section nodular cast iron.
The effects of rare earths with different contents on anti-degradation of Y base heavy rare earths-magnesium and cerium base light rare earths-magnesium nodular cast iron were studied. Curves of the relationship between the spheroidization grade of liguid iron treated by different nodulizers and holding time were obtained. The results show that the more the remains of the rare earth, the longer the anti-degradation time, the liquid iron was treated either by Y-Mg-Si or by Ce-Mg-Si nodulizer. When the rare earth remains are above certain quantity, the spheroidization grade starts to decline. When liquid iron treated by either Y-Mg-Si or Ce-Mg-Si nodulizer with proper remains of rare earths about 0.04% 0.06%（mass fraction）, the anti-degradation is the best, and the remains of Mg being about 0.04% -0.07% （mass fraction）. Rare earths-Mg nodulizer with moderate RE remains is better than that of Mg-Si nodulizer in anti-degradation property. However, Y-Mg-Si nodulizer with moderate remins of Re is better than Ce-Mg-Si nodulizer. Sometimes Ce-Mg- Si nodulizer can be used for the production of heavy section nodular cast iron.
基金
ProjectsupportedbytheNaturalScienceFoundationofHerlongjiangProvince(E2004211)