The rupture behavior of a cast Ni-base superalloy M963 at high temperature has been investi- gated. The microstructure examination shows that there exists a large amount of the carbide and γ-γ' eutectic, which is very harmful to the mechanical properties of M963 superalloy. The tensile strength of M963 superalloy both at room temperature and at high temperatures is higher than that of K17G alloy, but the tensile ductility of the former is much lower than that of the latter. In tensile fracture process with the high strain rate, the open carbides are the initiation site and the carbide/matrix interface is the propagation path of cracks. But in fracture process with the low strain rate, the carbide/matrix interface and cast microvoids are the initiation sites, and the carbide/matrix interface is the propagation path of cracks. The effective ways to improve ductility of M963 superalloy are also suggested.
The rupture behavior of a cast Ni-base superalloy M963 at high temperature has been investi- gated. The microstructure examination shows that there exists a large amount of the carbide and γ-γ' eutectic, which is very harmful to the mechanical properties of M963 superalloy. The tensile strength of M963 superalloy both at room temperature and at high temperatures is higher than that of K17G alloy, but the tensile ductility of the former is much lower than that of the latter. In tensile fracture process with the high strain rate, the open carbides are the initiation site and the carbide/matrix interface is the propagation path of cracks. But in fracture process with the low strain rate, the carbide/matrix interface and cast microvoids are the initiation sites, and the carbide/matrix interface is the propagation path of cracks. The effective ways to improve ductility of M963 superalloy are also suggested.
基金
supported by the Postdoctoral Science Foundation of China