摘要
The flexural strengths and oxidative resistant properties of the ceramics derived from polycarbosilane and active fillers (Ti, TiH 2, TiB 2, Cr, and CrSi 2) were measured and characterized. The introduction of active fillers enhances slightly the flexural strengths, and further densification is required to obtain higher strengths. The oxidative resistant behaviors of the specimens with active fillers are, by means of weight gain in air, poorer compared with those without active fillers.
The flexural strengths and oxidative resistant properties of the ceramics derived from polycarbosilane and active fillers (Ti, TiH 2, TiB 2, Cr, and CrSi 2) were measured and characterized. The introduction of active fillers enhances slightly the flexural strengths, and further densification is required to obtain higher strengths. The oxidative resistant behaviors of the specimens with active fillers are, by means of weight gain in air, poorer compared with those without active fillers.