In order to understand the stress corrosion behavior of super-high strength aluminum alloys by spray forming, different aluminum alloys by different heat treatment was made. The results showed that the alloy with peak...In order to understand the stress corrosion behavior of super-high strength aluminum alloys by spray forming, different aluminum alloys by different heat treatment was made. The results showed that the alloy with peak aging has the most sensitive stress corrosion cracking, the crack can even be seen using eyes;the alloys with two step aging were better than one step aging alloys, the alloys has not been found stress corrosion cracking.展开更多
The performance of composite ceramic armor penetrated by rod projectile was studied by both numerical simulation and experiment.The penetration and damage mechanisms of the projectile-armor after high-speed collision ...The performance of composite ceramic armor penetrated by rod projectile was studied by both numerical simulation and experiment.The penetration and damage mechanisms of the projectile-armor after high-speed collision were also observed by high-speed photography.The experimental results showed that the ballistic performance of composite ceramic armor was highly affected by the density,hardness and toughness of bulletproof ceramic.The flow stress of the failed bulletproof ceramic is not only related to the pressure but also related to the strain rate.The phenomenological method based on Bodner-Partom ceramic model was introduced to derive the growth rate of damage.Numerical simulation results show good agreement with the experimental results.展开更多
Effects of Al2O3 and Ni as the additives on the sinterability, microstructure and mechanical properties were systematic studied. The experimental results show that only a relative density about 96.2% of hot-pressing T...Effects of Al2O3 and Ni as the additives on the sinterability, microstructure and mechanical properties were systematic studied. The experimental results show that only a relative density about 96.2% of hot-pressing TiB2-30%Al2O3 can be attained due to the plate-like TiB2 particle and its random orientation and excessive Al2O3 grain growth. When sintering temperature is higher than 1 700 ℃, TiB2 grain growth can be found, which obvious improves flexural strength of TiB2 matrix but decreases toughness. It seems that mechanical properties of TiB2-Al2O3 composites are mainly depended on relative density besides grain growth. otherwise, they will be determined by relative density and TiB2 matrix strength together. Anyway, Al2O3 addition can weaken the grain boundary and thus improve the toughness of the materials. A flexural strength of 529 MPa, Vickers hardness of 24.8 GPa and indentation toughness of 4.56 MPa·m1/2 can be achieved inTiB2-30vol% Al2O3.展开更多
文摘In order to understand the stress corrosion behavior of super-high strength aluminum alloys by spray forming, different aluminum alloys by different heat treatment was made. The results showed that the alloy with peak aging has the most sensitive stress corrosion cracking, the crack can even be seen using eyes;the alloys with two step aging were better than one step aging alloys, the alloys has not been found stress corrosion cracking.
文摘The performance of composite ceramic armor penetrated by rod projectile was studied by both numerical simulation and experiment.The penetration and damage mechanisms of the projectile-armor after high-speed collision were also observed by high-speed photography.The experimental results showed that the ballistic performance of composite ceramic armor was highly affected by the density,hardness and toughness of bulletproof ceramic.The flow stress of the failed bulletproof ceramic is not only related to the pressure but also related to the strain rate.The phenomenological method based on Bodner-Partom ceramic model was introduced to derive the growth rate of damage.Numerical simulation results show good agreement with the experimental results.
文摘Effects of Al2O3 and Ni as the additives on the sinterability, microstructure and mechanical properties were systematic studied. The experimental results show that only a relative density about 96.2% of hot-pressing TiB2-30%Al2O3 can be attained due to the plate-like TiB2 particle and its random orientation and excessive Al2O3 grain growth. When sintering temperature is higher than 1 700 ℃, TiB2 grain growth can be found, which obvious improves flexural strength of TiB2 matrix but decreases toughness. It seems that mechanical properties of TiB2-Al2O3 composites are mainly depended on relative density besides grain growth. otherwise, they will be determined by relative density and TiB2 matrix strength together. Anyway, Al2O3 addition can weaken the grain boundary and thus improve the toughness of the materials. A flexural strength of 529 MPa, Vickers hardness of 24.8 GPa and indentation toughness of 4.56 MPa·m1/2 can be achieved inTiB2-30vol% Al2O3.