An amorphous ferric oxide layer was prepared on a bismuth vanadate photoanode.This resulted in improved charge carrier separation and surface catalytic performance compared with the photoanode without the oxide layer....An amorphous ferric oxide layer was prepared on a bismuth vanadate photoanode.This resulted in improved charge carrier separation and surface catalytic performance compared with the photoanode without the oxide layer.The photocurrent of the oxide‐layer‐containing photoanode was2.52mA/cm2at1.23V versus the reversible hydrogen electrode,in potassium phosphate buffer,(0.5mol/L,pH=7.0).The amorphous ferric oxide layer on the photoanode contained low‐valence‐state iron species(FeII),which enabled efficient hole extraction and transfer.展开更多
基金supported by the National Natural Science Foundation of China(21373083,21573068)Program of Shanghai Subject Chief Scientist(15XD1501300)+1 种基金the Scientific Research Foundation for the Returned Overseas Chinese Scholars,State Education MinistryScience Technology Commission of Shanghai Municipality(14JC1490900)~~
文摘An amorphous ferric oxide layer was prepared on a bismuth vanadate photoanode.This resulted in improved charge carrier separation and surface catalytic performance compared with the photoanode without the oxide layer.The photocurrent of the oxide‐layer‐containing photoanode was2.52mA/cm2at1.23V versus the reversible hydrogen electrode,in potassium phosphate buffer,(0.5mol/L,pH=7.0).The amorphous ferric oxide layer on the photoanode contained low‐valence‐state iron species(FeII),which enabled efficient hole extraction and transfer.