A number of processing routes were developed for the synthesis of mullite whiskers. Mullite whiskers that were derived from ytterbia-doped aluminum hydroxide-silica gel were studied; another process for preparing mull...A number of processing routes were developed for the synthesis of mullite whiskers. Mullite whiskers that were derived from ytterbia-doped aluminum hydroxide-silica gel were studied; another process for preparing mullite whiskers from Al2O3-SiO2 oxide mixtures by mechanochemical method was encountered by chance. The method of ytterbia-doped aluminum hydroxide-silica was used to enhance mullite formation from gel. For adding ytterbia, mullite formation can take place at 1000℃and almost single-phase mullite can be achieved at 1150℃, which is a significantly lower temperature than mechanochemical method. This enhancement of mullite formation is also attributed to refinement of aluminum hydroxide-silica by gel. Furthermore, well-developed single-crystal mullite whiskers were produced from the gel powder instead of normal-shaped grains. The presence of YbO might have promoted the formation of nanosized Al2O3 particles, which then acted as a template leading to mullite whiskers at higher sintering temperature.展开更多
基金Project supported by the National High Technology Research and Development Program of China (2004AA332060)
文摘A number of processing routes were developed for the synthesis of mullite whiskers. Mullite whiskers that were derived from ytterbia-doped aluminum hydroxide-silica gel were studied; another process for preparing mullite whiskers from Al2O3-SiO2 oxide mixtures by mechanochemical method was encountered by chance. The method of ytterbia-doped aluminum hydroxide-silica was used to enhance mullite formation from gel. For adding ytterbia, mullite formation can take place at 1000℃and almost single-phase mullite can be achieved at 1150℃, which is a significantly lower temperature than mechanochemical method. This enhancement of mullite formation is also attributed to refinement of aluminum hydroxide-silica by gel. Furthermore, well-developed single-crystal mullite whiskers were produced from the gel powder instead of normal-shaped grains. The presence of YbO might have promoted the formation of nanosized Al2O3 particles, which then acted as a template leading to mullite whiskers at higher sintering temperature.