This study investigated the effect of pre-friction surfacing heat treatment of consumable rods and heat input during friction surfacing on the microstructure,mechanical properties,and wear resistance of hypereutectic ...This study investigated the effect of pre-friction surfacing heat treatment of consumable rods and heat input during friction surfacing on the microstructure,mechanical properties,and wear resistance of hypereutectic Al-Si alloy deposited on a commercially pure aluminum substrate.The results show that regardless of the consumable rod’s heat treatment conditions,the coating’s efficiency has increased with the increase in heat input,so the coating efficiency increases by 20%and 30%in the solid solution-treated rod and the artificially aged rod,respectively.By increasing the heat input,the average grain size in the coating fabricated by solid solution-treated rod and artificially aged rod increased from 0.1 to 0.9μm and from 0.2 to 1.3μm,respectively.At constant heat input,the average hardness and wear resistance of the coating created in the solid solution-treated rod are lower than those of the artificially aged rod.By decreasing heat input,the wear loss in the coating fabricated by solid solution-treated rod and artificially aged rod decreased by 10%and 20%,respectively,reaching 0.1 and 0.03μg/m.展开更多
The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing...The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing compounds in the alloys produced by conventional casting process are detrimental to the strength of matrix. The effect of ultrasonic vibration （USV） on the morphology change of Fe-containing intermetallic compounds in the hypereutectic Al-17Si-xFe （x=2, 3, 4, 5） alloys was systematically studied. The results show that, the Fe-containing intermetallic compounds are mainly composed of long needle-like β-Al5FeSi phase with a small amount of plate-like δ-Al4FeSi2 phase in Al-17Si-2Fe alloy produced by conventional casting process. With the increase of Fe content from 2% to 5% in the alloys, the amount of plate-like or coarse needle-like δ-Al4FeSi2 phase increases while the amount of long needle-like β-Al5FeSi phases decreases. In Al-17Si-5Fe alloy, the Fe-containing intermetallic compounds exist mainly as coarse needle-like δ-Al4FeSi2 phase. After USV treatment, the Fe-containing compounds in the Al-17Si-xFe alloys are refined and exist mainly as δ-Al4FeSi2 particles, with average grain size ranging from 26 μm to 37 μm, and only a small amount of β-Al5FeSi phases remain. The mechanism of USV on the morphology of Fe-containing intermetallic compounds was also discussed.展开更多
The effect of iron content on wear behavior of hypereutectic Al?17Si?2Cu?1Ni alloy produced by rheocasting process was investigated. The dry sliding wear tests were carried out with a pin-on-disk wear tester. The resu...The effect of iron content on wear behavior of hypereutectic Al?17Si?2Cu?1Ni alloy produced by rheocasting process was investigated. The dry sliding wear tests were carried out with a pin-on-disk wear tester. The results show that the wear rate of the rheocast alloy is lower than that of the alloy produced by conventional casting process under the same applied load. The fine particle-likeδ-Al4(Fe,Mn)Si2 and polygonalα-Al15(Fe,Mn)3Si2 phases help to improve the wear resistance of rheocast alloys. As the volume fraction of fine Fe-bearing compounds increases, the wear rate of the rheocast alloy decreases. Moreover, the wear rate of rheocast alloy increases with the increase of applied load from 50 to 200 N. For the rheocast alloy with 3% Fe, oxidation wear is the main mechanism at low applied load (50 N). At higher applied loads, a combination of delamination and oxidation wear is the dominant wear mechanism.展开更多
Hypereutectic Al-Si alloy with variant Mg contents were fabricated by casting,and the effects of Mg content on the microstructure of primary Mg2Si particles in hypereutectic Al-Si alloys were investigated.The results ...Hypereutectic Al-Si alloy with variant Mg contents were fabricated by casting,and the effects of Mg content on the microstructure of primary Mg2Si particles in hypereutectic Al-Si alloys were investigated.The results show that the volume fraction of primary Mg2Si particles increases linearly with raising the Mg content,but the average size of Mg2Si particles does not exhibit a corresponding change.When the Mg content is 3%,á1 0 0？ directions have the fastest growth velocity,so that Mg2Si particles are likely to form octahedron shape.When gradually increasing the Mg content,the distributions of Mg and Si atoms on the solid-liquid interface become inhomogeneous,which results in the formation of irregular octahedron structures.Finally,when the Mg content is about 10%,the morphology of primary Mg2Si particles changes from the octahedron shape into various complex structures with a large size.展开更多
The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The r...The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope（SEM）,and energy dispersive analysis of X-rays（EDAX） that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.展开更多
Microstructural evolution and phase transformation induced by different heat treatments of the hypereutectic aluminium-silicon alloy, Al-25Si-5Fe-3Cu （wt%, signed as 3C）, fabricated by traditional cast （TC） and sp...Microstructural evolution and phase transformation induced by different heat treatments of the hypereutectic aluminium-silicon alloy, Al-25Si-5Fe-3Cu （wt%, signed as 3C）, fabricated by traditional cast （TC） and spray forming （SF） processes, were investigated by differential scanning calorimetry （DSC） and scanning electron microscopy （SEM） combined with energy dispersive X-ray spectroscopy and X-ray diffraction techniques. The results show that A17Cu2Fe phase can be formed and transformed in TC- and SF-3C alloys between 802-813 K and 800-815 K, respectively. The transformation from β-Al5FeSi to δ-Al4FeSi2 phase via peritectic reaction can occur at around 858-870 K and 876-890 K in TC- and SF-3C alloys, respectively. The starting precipitation temperature of δ-Al4FeSi2 phase as the dominant Fe-bearing phase in the TC-3C alloy is 997 K and the exothermic peak about the peritectic transformation of δ-Al4FeSi2→β-Al5FeSi is not detected in the present DSC experiments. Also, the mechanisms of the microstructural evolution and phase transformation are discussed.展开更多
The influence of high pressure and manganese addition on Fe-rich phases(FRPs)and mechanical properties of Al-14Si-2Fe alloy with rheo-squeeze casting(RSC)was investigated.The semi-solid alloy melt was treated by ultra...The influence of high pressure and manganese addition on Fe-rich phases(FRPs)and mechanical properties of Al-14Si-2Fe alloy with rheo-squeeze casting(RSC)was investigated.The semi-solid alloy melt was treated by ultrasonic vibration(UV)firstly,and then formed by squeeze casting(SC).Results show that the FRPs in as-cast SC alloys are composed of coarseβ-Al5(Fe,Mn)Si,δ-Al4(Fe,Mn)Si2 and bone-shapedα-Al15(Fe,Mn)3Si2 phases when the pressure is 0 MPa.With RSC process,the FRPs are first refined by UV,and then the solidification under pressure further causes the grains to become smaller.The peritectic transformation occurs during the formation ofαphase.For the alloy with the same composition,the ultimate tensile strength(UTS)of RSC sample is higher than that of the SC sample.With the same forming process,the UTS of Al-14Si-2Fe-0.8Mn alloy is higher than that of Al-14Si-2Fe-0.4Mn alloy.展开更多
The feasibility of semi solid processing of hypereutectic A390 alloys using a novel rheoforming process was investigated. A combination of the swirl enthalpy equilibration device （SEED） process, isothermal holding u...The feasibility of semi solid processing of hypereutectic A390 alloys using a novel rheoforming process was investigated. A combination of the swirl enthalpy equilibration device （SEED） process, isothermal holding using insulation and addition of solid alloy during swirling was introduced as a novel method to improve the processability of semi solid slurry. The effects of isothermal holding and the addition of solid alloy on the temperature gradient between the centre and the wall and on the formation of a（Al） particles were examined. In additional tests, phosphorus and strontium were added to the molten metal to refine the primary and eutectic silicon structure to facilitate semi solid processing. The results show that the combination of the SEED process with two additional processing steps can produce semi-solid A390 alloys that can be rheoprocessed. The microstructure reveals an adequate amount of non-dendritic a（Al） globules surrounded by liquid, which greatly improves the processability of semi-solid slurry.展开更多
The effects of pouring temperature,vibration frequency,and the number of curves in a serpentine channel,on themicrostructure and mechanical properties of Al-30%Si alloy processed by rheo-diecasting(RDC)were investigat...The effects of pouring temperature,vibration frequency,and the number of curves in a serpentine channel,on themicrostructure and mechanical properties of Al-30%Si alloy processed by rheo-diecasting(RDC)were investigated.The semisolidAl-30%Si alloy slurry was prepared by vibration serpentine channel pouring(VSCP)process in the RDC process.The results showthat the pouring temperature,the vibration frequency,and the number of the curves strongly affect the microstructure and mechanicalproperties of Al-30%Si alloy.Under experimental conditions of a pouring temperature of850°C,a twelve-curve copper channel anda vibration frequency of80Hz,the primary Si grains are refined into fine compact grains with average grain size of about24.6μm inthe RDC samples assisted with VSCP.Moreover,the ultimate tensile strength(UTS),elongation and hardness of the RDC sample are296MPa,0.87%and HB155,respectively.It is concluded that the VSCP process can effectively refine the primary Si grains.Therefinement of primary Si grains is the major cause for the improvement of the mechanical properties of the RDC sample.展开更多
Controlled Diffusion Solidification(CDS) is a promising process relied on mixing two liquid alloys of precisely controlled chemistry and temperature in order to produce a predetermined alloy composition. In this study...Controlled Diffusion Solidification(CDS) is a promising process relied on mixing two liquid alloys of precisely controlled chemistry and temperature in order to produce a predetermined alloy composition. In this study, the CDS was employed to prepare hypereutectic Al-20%Si(mass fraction) alloy using Al-30%Si and pure Al of different temperatures. The mixing rate was controlled using three small crucibles with a hole of different diameters in their bottom. The effect of mixing rate and temperature on the microstructure of the primary Si-phase during the mixing of molten Al and Al-30%Si was studied. The results showed that when the diameter of the small crucible bottom hole is 16 mm, a higher mass mixing rate 0.217 kg·s-1 would results in a lower stream velocity 0.414 m·s-1. Conversely a lower mass mixing rate 0.114 kg·s-1(the diameter of the small crucible bottom hole is 8 mm) would result in a higher fluid stream velocity 0.879 m·s-1. A lower mass mixing rate would be better to refine the primary Si than a higher mass mixing rate. Meanwhile, the morphology and distribution of primary Si could also be improved. Especially, when Al-30%Si alloy at 820 °C was mixed with pure Al at 670 °C in the case of a mass mixing rate of 0.114 kg·s-1 and a pouring temperature of 680 °C, the average size of the primary Si phase would be only 18.2 μm. Its morphology would mostly be octahedral and the primary Si would distribute uniformly in the matrix microstructure. The lower mass mixing rate(0.114 kg·s-1) will enhance the broken tendency of Al-30%Si steam and the mixing agitation of resultant melt, so the primary Si phase can be better refined.展开更多
Semisolid hypereutectic Al Si alloy billets were obtained by electromagnetic stirring, in which microstructure of primary silicon gets rounder and there are a large number of rosette α phases appearing. Compared with...Semisolid hypereutectic Al Si alloy billets were obtained by electromagnetic stirring, in which microstructure of primary silicon gets rounder and there are a large number of rosette α phases appearing. Compared with conventional gravity die casting alloys, the tensile strength and elongation of semisolid forming hypereutectic Al Si get obviously improved. Change of primary silicon morphology of semisolid hypereutectic Al Si alloy made by electromagnetic stirring is the main reason of better tensile strength, and a large number of rosette α phases precipitation is the main reason of better elongation.展开更多
This study aimed at optimizing impact toughness and abrasion wear resistance of 15%Cr-2%Mo hypereutectic abrasion-resistant white irons. The effects of dynamic solidification, niobium addition, combined action of them...This study aimed at optimizing impact toughness and abrasion wear resistance of 15%Cr-2%Mo hypereutectic abrasion-resistant white irons. The effects of dynamic solidification, niobium addition, combined action of them and heat treatment have been investigated. Investigations were performed by means of the image analyzer, scanning electron microscopy (SEM), energy-dispersive spectrometry (EDS) and X-ray diffraction. Impact toughness and abrasion wear resistance tests were conducted. Fracture and worn surfaces were studied. Results indicated that microstructural control during solidifciation is the most valuable tool to attain the optimum combination between impact toughness and wear resistance in hypereutectic iron. Combined action of Nb addition and dynamic solidifciation improves impact toughness and wear resistance even more than the action of each individual factor. In the as-cast condition, impact toughness and abrasion resistance were increased after dynamic solidification compared to statically solidified one by 71.4% and 10%, respectively. This enhancement was increased to 114.3 % and 28.8 % by adding 2% Nb. Lower tempering temperature of 260°C exhibits better impact and abrasion resistance than the sub-critical tempering temperature of 500°C.展开更多
In this paper, the ring-type ingot of hypereutectic high Cr cast iron was obtained by slope cooling bodycentrifugal casting method （SC-CCM）, and its microstructure and impact toughness were investigated, respectivel...In this paper, the ring-type ingot of hypereutectic high Cr cast iron was obtained by slope cooling bodycentrifugal casting method （SC-CCM）, and its microstructure and impact toughness were investigated, respectively. The results indicated that, first, the primary carbides in the microstructure are prominently finer than those in the hypereutectic high Cr cast iron prepared by conventional casting method. Second, in the ring-type ingot, the primary carbides near radial outer field are finer than those near radial inner field; furthermore, there is dividing field in the microstructure. Finally, the impact toughness values of the specimens impacted on the radial outer face and on the radial inner face are improved respectively about 36% and 138% more than that of the hypereutectic high Cr one prepared by conventional casting method.展开更多
The hypereutectic Al-Si alloy was fabricated by hot extrusion process after solidified under electromagnetic stirring,and the microstructure and mechanical properties of the alloy were studied.The results show that th...The hypereutectic Al-Si alloy was fabricated by hot extrusion process after solidified under electromagnetic stirring,and the microstructure and mechanical properties of the alloy were studied.The results show that the ultimate tensile strength and elongation of the alloy reached 229.5 MPa and 4.6%,respectively with the extrusion ratio of 10,and 263.2 MPa and 5.4%,respectively with extrusion ratio of 20.This indicates that the mechanical properties of the alloy are obviously improved with the increase of extrusion ratio.After hot extruded,the primary Si,eutectic Si,Mg2Si,AlNi,Al7Cu4Ni and Al-Si-Mn-Fe-Cr-Mo phases are refined to different extent,and the efficiency of refinement is obvious more and more with the increase of extrusion ratio.After T6 heat treatment,the sharp corners of these phases become passivated and roundish,and the mechanical properties are improved.The ultimate tensile strength of the extruded alloy after T6 heat treatment reaches 335.3 MPa with extrusion ratio of 10 and 353.6 MPa with extrusion ratio of 20.展开更多
Large and segregated primary Si particles may drastically decrease the mechanical properties of AI-Si alloys. To solve this problem, a P-Cr complex modifier was added into the alloy, and the effects of P-Cr complex mo...Large and segregated primary Si particles may drastically decrease the mechanical properties of AI-Si alloys. To solve this problem, a P-Cr complex modifier was added into the alloy, and the effects of P-Cr complex modification and solidification conditions on the microstructure of hypereutectic Al-Si alloys casting produced in wedge-shaped copper mould were studied. The thermal analysis technique was applied to calculate the cooling rate during solidification. The microstructures were observed by means of optical and scanning electron microscopies. Results showed that the primary Si segregates in the as-cast hypereutectic AI-Si alloys. The segregation of primary Si can be inhibited by adding a P＋Cr complex modifier and increasing the cooling rate during solidification. The refinement of primary Si particles by P＋Cr complex modification is due to the formation of CrSi2 and AlP particles which act as the heterogeneous nuclei for the primary Si phase. The segregation of Si was also inhibited through the adherence of heavier CrSi2 particles to the primary Si particles.展开更多
In order to review the effect of partial remelting time on the morphology of initial carbides, semisolid ingots of hypereutectic high Cr17 cast iron were remelted at 1270℃ for four different times, and the changing c...In order to review the effect of partial remelting time on the morphology of initial carbides, semisolid ingots of hypereutectic high Cr17 cast iron were remelted at 1270℃ for four different times, and the changing characteristics of shape factor and the equivalent diameter of initial carbides were analyzed quantitatively using a Leica image analyzer. The results indicate that firstly, the evolution process of the initial carbides' morphology undergoes melting, spheroidization and refining during the partial remelting; secondly, the solute diffusion and interface tension take dominant roles at the primary and the middle-final stages respectively in the process of initial carbide evolution; finally, a perfect structure can be obtained by remelting semisolid ingots at 1270℃ for 15 min.展开更多
A hypereutectic Al-Si alloy powder was prepared by ultrasonic gas atomization process. The morphologies, microstructure and phase constituent of the alloy powder were studied. The results showed that powder of the all...A hypereutectic Al-Si alloy powder was prepared by ultrasonic gas atomization process. The morphologies, microstructure and phase constituent of the alloy powder were studied. The results showed that powder of the alloy was very fine and its microstructure was mainly consisted of Si crystals plus intermetallic compound A19FeSi3, which were.very fine and uniformly distributed.展开更多
Recent studies revealed that in eutectic to slightly hypereutectic grey irons （CE = 4.3%-4.5%） the presence of austenite dendrites provides an opportunity to improve the cast iron properties, as a high number of eut...Recent studies revealed that in eutectic to slightly hypereutectic grey irons （CE = 4.3%-4.5%） the presence of austenite dendrites provides an opportunity to improve the cast iron properties, as a high number of eutectic cells are ＂reinforced＂ by austenite dendrites. An iron powder addition proved to be important by promoting dendritic austenite in hypereutectic irons, but was accompanied by adverse effect on the characteristics of potential nuclei for graphite. The purpose of the present paper is to investigate the solidification pattern of these irons. Chill wedges with different cooling moduli （CM = 0.11 - 0.43 cm） were poured in resin bonded sand and metal moulds. Relative clear / mottled / total chill measurement criteria were applied. Iron powder additions led to a higher chill tendency, while single inoculation showed the strongest graphiUzing effect. The various double treatments show an intermediate position, but the inoculant added after iron powder appears to be the most effective in reducing base iron chill tendency, for all cooling moduli and chill evaluation parameters. This performance reflects the improved properties of （Mn,X）S polygonal compounds as nucleation sites for graphite, especially in resin bonded sand mould castings. Both austenite and graphite nucleation benefit from a double addition of iron powder ＋ inoculant, with positive effect on the final structure and chill tendency.展开更多
Effects of processing parameters on microstructure evolutions by mechanical stirring, procedures for obtaining thixotropy in semi solid slurries, and procedure for thixoforging component, were investigated in hypereut...Effects of processing parameters on microstructure evolutions by mechanical stirring, procedures for obtaining thixotropy in semi solid slurries, and procedure for thixoforging component, were investigated in hypereutectic Al Si alloy. It is shown that 605 ℃ was the proper temperature for stirring treatment of this alloy, at which the coarse and plate primary Si crystals were effectively changed to globular crystals with a mean diameter of 200 μm after 50 min stirring, that billets with excellent thixotropy were obtained after 50 min remelting at 575 ℃, in which solid fraction of matrix and primary Si crystals was about 60%, and that a perfect near net shape component of disc casting was obtained by thixoforging.展开更多
The microstructural evolution and apparent viscosity of hypereutectic Al-24%Si alloy during semi-solid state shearing were studied with a Searte type viscometer. When the alloy melt was continuously stirred from 720 d...The microstructural evolution and apparent viscosity of hypereutectic Al-24%Si alloy during semi-solid state shearing were studied with a Searte type viscometer. When the alloy melt was continuously stirred from 720 degreesC to eutectic temperature, the primary Si crystals were gradually changed from elongated platelets to near-spherical shapes. It was found that some nondendritic a-phase formed when the melt was stirred below 585 degreesC. The experiment showed that the semi-solid stirring had strong effect on inhibiting the anisotropic growth of Si crystals during solidification. The apparent viscosity of the alloy melt increased slowly with the decreasing of temperature before the formation of nondendritic alpha -phase, which caused the dramatic increase of apparent viscosity.展开更多
文摘This study investigated the effect of pre-friction surfacing heat treatment of consumable rods and heat input during friction surfacing on the microstructure,mechanical properties,and wear resistance of hypereutectic Al-Si alloy deposited on a commercially pure aluminum substrate.The results show that regardless of the consumable rod’s heat treatment conditions,the coating’s efficiency has increased with the increase in heat input,so the coating efficiency increases by 20%and 30%in the solid solution-treated rod and the artificially aged rod,respectively.By increasing the heat input,the average grain size in the coating fabricated by solid solution-treated rod and artificially aged rod increased from 0.1 to 0.9μm and from 0.2 to 1.3μm,respectively.At constant heat input,the average hardness and wear resistance of the coating created in the solid solution-treated rod are lower than those of the artificially aged rod.By decreasing heat input,the wear loss in the coating fabricated by solid solution-treated rod and artificially aged rod decreased by 10%and 20%,respectively,reaching 0.1 and 0.03μg/m.
基金Project(2012CB619600)supported by the National Basic Research Program of ChinaProject(50775086)supported by the National Natural Science Foundation of China
文摘The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing compounds in the alloys produced by conventional casting process are detrimental to the strength of matrix. The effect of ultrasonic vibration （USV） on the morphology change of Fe-containing intermetallic compounds in the hypereutectic Al-17Si-xFe （x=2, 3, 4, 5） alloys was systematically studied. The results show that, the Fe-containing intermetallic compounds are mainly composed of long needle-like β-Al5FeSi phase with a small amount of plate-like δ-Al4FeSi2 phase in Al-17Si-2Fe alloy produced by conventional casting process. With the increase of Fe content from 2% to 5% in the alloys, the amount of plate-like or coarse needle-like δ-Al4FeSi2 phase increases while the amount of long needle-like β-Al5FeSi phases decreases. In Al-17Si-5Fe alloy, the Fe-containing intermetallic compounds exist mainly as coarse needle-like δ-Al4FeSi2 phase. After USV treatment, the Fe-containing compounds in the Al-17Si-xFe alloys are refined and exist mainly as δ-Al4FeSi2 particles, with average grain size ranging from 26 μm to 37 μm, and only a small amount of β-Al5FeSi phases remain. The mechanism of USV on the morphology of Fe-containing intermetallic compounds was also discussed.
基金Project(2015M572135)supported by the China Postdoctoral Science FoundationProject(2012CB619600)supported by the National Basic Research Program of China
文摘The effect of iron content on wear behavior of hypereutectic Al?17Si?2Cu?1Ni alloy produced by rheocasting process was investigated. The dry sliding wear tests were carried out with a pin-on-disk wear tester. The results show that the wear rate of the rheocast alloy is lower than that of the alloy produced by conventional casting process under the same applied load. The fine particle-likeδ-Al4(Fe,Mn)Si2 and polygonalα-Al15(Fe,Mn)3Si2 phases help to improve the wear resistance of rheocast alloys. As the volume fraction of fine Fe-bearing compounds increases, the wear rate of the rheocast alloy decreases. Moreover, the wear rate of rheocast alloy increases with the increase of applied load from 50 to 200 N. For the rheocast alloy with 3% Fe, oxidation wear is the main mechanism at low applied load (50 N). At higher applied loads, a combination of delamination and oxidation wear is the dominant wear mechanism.
基金Project(CDJZR12240056)supported by the Fundamental Research Funds for Central Universities,ChinaProject(cstc2013jcyj A50014)supported by the Foundational and Cutting-edge Research Plan of Chongqing,China
文摘Hypereutectic Al-Si alloy with variant Mg contents were fabricated by casting,and the effects of Mg content on the microstructure of primary Mg2Si particles in hypereutectic Al-Si alloys were investigated.The results show that the volume fraction of primary Mg2Si particles increases linearly with raising the Mg content,but the average size of Mg2Si particles does not exhibit a corresponding change.When the Mg content is 3%,á1 0 0？ directions have the fastest growth velocity,so that Mg2Si particles are likely to form octahedron shape.When gradually increasing the Mg content,the distributions of Mg and Si atoms on the solid-liquid interface become inhomogeneous,which results in the formation of irregular octahedron structures.Finally,when the Mg content is about 10%,the morphology of primary Mg2Si particles changes from the octahedron shape into various complex structures with a large size.
文摘The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope（SEM）,and energy dispersive analysis of X-rays（EDAX） that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.
基金supported by the Major State Basic Research & Development Program of China (No2006CB605204)
文摘Microstructural evolution and phase transformation induced by different heat treatments of the hypereutectic aluminium-silicon alloy, Al-25Si-5Fe-3Cu （wt%, signed as 3C）, fabricated by traditional cast （TC） and spray forming （SF） processes, were investigated by differential scanning calorimetry （DSC） and scanning electron microscopy （SEM） combined with energy dispersive X-ray spectroscopy and X-ray diffraction techniques. The results show that A17Cu2Fe phase can be formed and transformed in TC- and SF-3C alloys between 802-813 K and 800-815 K, respectively. The transformation from β-Al5FeSi to δ-Al4FeSi2 phase via peritectic reaction can occur at around 858-870 K and 876-890 K in TC- and SF-3C alloys, respectively. The starting precipitation temperature of δ-Al4FeSi2 phase as the dominant Fe-bearing phase in the TC-3C alloy is 997 K and the exothermic peak about the peritectic transformation of δ-Al4FeSi2→β-Al5FeSi is not detected in the present DSC experiments. Also, the mechanisms of the microstructural evolution and phase transformation are discussed.
基金Project(51605342) supported by the National Natural Science Foundation of ChinaProject(2015CFB431) supported by the Natural Science Foundation of Hubei Province,China+1 种基金Project(K201520) supported by the Science Research Foundation of Wuhan Institute of Technology,ChinaProject(2016KA01) supported by the Open Research Fund Program of Hubei Provincial Key Laboratory of Chemical Equipment Intensification and Intrinsic Safety,China
文摘The influence of high pressure and manganese addition on Fe-rich phases(FRPs)and mechanical properties of Al-14Si-2Fe alloy with rheo-squeeze casting(RSC)was investigated.The semi-solid alloy melt was treated by ultrasonic vibration(UV)firstly,and then formed by squeeze casting(SC).Results show that the FRPs in as-cast SC alloys are composed of coarseβ-Al5(Fe,Mn)Si,δ-Al4(Fe,Mn)Si2 and bone-shapedα-Al15(Fe,Mn)3Si2 phases when the pressure is 0 MPa.With RSC process,the FRPs are first refined by UV,and then the solidification under pressure further causes the grains to become smaller.The peritectic transformation occurs during the formation ofαphase.For the alloy with the same composition,the ultimate tensile strength(UTS)of RSC sample is higher than that of the SC sample.With the same forming process,the UTS of Al-14Si-2Fe-0.8Mn alloy is higher than that of Al-14Si-2Fe-0.4Mn alloy.
基金the financial support provided by the Natural Sciences and Engineering Research Council of Canada (NSERC) and Rio Tinto Alcan through the NSERC Industrial Research Chair in Metallurgy of Aluminum Transformation at Université du Québec à Chicoutimi
文摘The feasibility of semi solid processing of hypereutectic A390 alloys using a novel rheoforming process was investigated. A combination of the swirl enthalpy equilibration device （SEED） process, isothermal holding using insulation and addition of solid alloy during swirling was introduced as a novel method to improve the processability of semi solid slurry. The effects of isothermal holding and the addition of solid alloy on the temperature gradient between the centre and the wall and on the formation of a（Al） particles were examined. In additional tests, phosphorus and strontium were added to the molten metal to refine the primary and eutectic silicon structure to facilitate semi solid processing. The results show that the combination of the SEED process with two additional processing steps can produce semi-solid A390 alloys that can be rheoprocessed. The microstructure reveals an adequate amount of non-dendritic a（Al） globules surrounded by liquid, which greatly improves the processability of semi-solid slurry.
基金Project(5077400) supported by the National Natural Science Foundation of China
文摘The effects of pouring temperature,vibration frequency,and the number of curves in a serpentine channel,on themicrostructure and mechanical properties of Al-30%Si alloy processed by rheo-diecasting(RDC)were investigated.The semisolidAl-30%Si alloy slurry was prepared by vibration serpentine channel pouring(VSCP)process in the RDC process.The results showthat the pouring temperature,the vibration frequency,and the number of the curves strongly affect the microstructure and mechanicalproperties of Al-30%Si alloy.Under experimental conditions of a pouring temperature of850°C,a twelve-curve copper channel anda vibration frequency of80Hz,the primary Si grains are refined into fine compact grains with average grain size of about24.6μm inthe RDC samples assisted with VSCP.Moreover,the ultimate tensile strength(UTS),elongation and hardness of the RDC sample are296MPa,0.87%and HB155,respectively.It is concluded that the VSCP process can effectively refine the primary Si grains.Therefinement of primary Si grains is the major cause for the improvement of the mechanical properties of the RDC sample.
基金supported by the National Natural Science Foundation of China(Grant Nos.51064017 and 51464031)
文摘Controlled Diffusion Solidification(CDS) is a promising process relied on mixing two liquid alloys of precisely controlled chemistry and temperature in order to produce a predetermined alloy composition. In this study, the CDS was employed to prepare hypereutectic Al-20%Si(mass fraction) alloy using Al-30%Si and pure Al of different temperatures. The mixing rate was controlled using three small crucibles with a hole of different diameters in their bottom. The effect of mixing rate and temperature on the microstructure of the primary Si-phase during the mixing of molten Al and Al-30%Si was studied. The results showed that when the diameter of the small crucible bottom hole is 16 mm, a higher mass mixing rate 0.217 kg·s-1 would results in a lower stream velocity 0.414 m·s-1. Conversely a lower mass mixing rate 0.114 kg·s-1(the diameter of the small crucible bottom hole is 8 mm) would result in a higher fluid stream velocity 0.879 m·s-1. A lower mass mixing rate would be better to refine the primary Si than a higher mass mixing rate. Meanwhile, the morphology and distribution of primary Si could also be improved. Especially, when Al-30%Si alloy at 820 °C was mixed with pure Al at 670 °C in the case of a mass mixing rate of 0.114 kg·s-1 and a pouring temperature of 680 °C, the average size of the primary Si phase would be only 18.2 μm. Its morphology would mostly be octahedral and the primary Si would distribute uniformly in the matrix microstructure. The lower mass mixing rate(0.114 kg·s-1) will enhance the broken tendency of Al-30%Si steam and the mixing agitation of resultant melt, so the primary Si phase can be better refined.
文摘Semisolid hypereutectic Al Si alloy billets were obtained by electromagnetic stirring, in which microstructure of primary silicon gets rounder and there are a large number of rosette α phases appearing. Compared with conventional gravity die casting alloys, the tensile strength and elongation of semisolid forming hypereutectic Al Si get obviously improved. Change of primary silicon morphology of semisolid hypereutectic Al Si alloy made by electromagnetic stirring is the main reason of better tensile strength, and a large number of rosette α phases precipitation is the main reason of better elongation.
文摘This study aimed at optimizing impact toughness and abrasion wear resistance of 15%Cr-2%Mo hypereutectic abrasion-resistant white irons. The effects of dynamic solidification, niobium addition, combined action of them and heat treatment have been investigated. Investigations were performed by means of the image analyzer, scanning electron microscopy (SEM), energy-dispersive spectrometry (EDS) and X-ray diffraction. Impact toughness and abrasion wear resistance tests were conducted. Fracture and worn surfaces were studied. Results indicated that microstructural control during solidifciation is the most valuable tool to attain the optimum combination between impact toughness and wear resistance in hypereutectic iron. Combined action of Nb addition and dynamic solidifciation improves impact toughness and wear resistance even more than the action of each individual factor. In the as-cast condition, impact toughness and abrasion resistance were increased after dynamic solidification compared to statically solidified one by 71.4% and 10%, respectively. This enhancement was increased to 114.3 % and 28.8 % by adding 2% Nb. Lower tempering temperature of 260°C exhibits better impact and abrasion resistance than the sub-critical tempering temperature of 500°C.
基金This work was supported by the National Natural Science Foundation of China under grant No.50571079.
文摘In this paper, the ring-type ingot of hypereutectic high Cr cast iron was obtained by slope cooling bodycentrifugal casting method （SC-CCM）, and its microstructure and impact toughness were investigated, respectively. The results indicated that, first, the primary carbides in the microstructure are prominently finer than those in the hypereutectic high Cr cast iron prepared by conventional casting method. Second, in the ring-type ingot, the primary carbides near radial outer field are finer than those near radial inner field; furthermore, there is dividing field in the microstructure. Finally, the impact toughness values of the specimens impacted on the radial outer face and on the radial inner face are improved respectively about 36% and 138% more than that of the hypereutectic high Cr one prepared by conventional casting method.
基金supported by National Natural Science Foundation of China (Grant No. 50971092)Innovation Team Plan pf Liaoning Provincical Education Department (Grant no. 2007T132)
文摘The hypereutectic Al-Si alloy was fabricated by hot extrusion process after solidified under electromagnetic stirring,and the microstructure and mechanical properties of the alloy were studied.The results show that the ultimate tensile strength and elongation of the alloy reached 229.5 MPa and 4.6%,respectively with the extrusion ratio of 10,and 263.2 MPa and 5.4%,respectively with extrusion ratio of 20.This indicates that the mechanical properties of the alloy are obviously improved with the increase of extrusion ratio.After hot extruded,the primary Si,eutectic Si,Mg2Si,AlNi,Al7Cu4Ni and Al-Si-Mn-Fe-Cr-Mo phases are refined to different extent,and the efficiency of refinement is obvious more and more with the increase of extrusion ratio.After T6 heat treatment,the sharp corners of these phases become passivated and roundish,and the mechanical properties are improved.The ultimate tensile strength of the extruded alloy after T6 heat treatment reaches 335.3 MPa with extrusion ratio of 10 and 353.6 MPa with extrusion ratio of 20.
基金financially supported by the National Basic Research Program of China(Grant No.:2012CB723307-03)the Fundamental Research Funds for the Central Universities(Grant No.:N130409003)the National Natural Science Foundation of China(Grant No.:51204046)of China
文摘Large and segregated primary Si particles may drastically decrease the mechanical properties of AI-Si alloys. To solve this problem, a P-Cr complex modifier was added into the alloy, and the effects of P-Cr complex modification and solidification conditions on the microstructure of hypereutectic Al-Si alloys casting produced in wedge-shaped copper mould were studied. The thermal analysis technique was applied to calculate the cooling rate during solidification. The microstructures were observed by means of optical and scanning electron microscopies. Results showed that the primary Si segregates in the as-cast hypereutectic AI-Si alloys. The segregation of primary Si can be inhibited by adding a P＋Cr complex modifier and increasing the cooling rate during solidification. The refinement of primary Si particles by P＋Cr complex modification is due to the formation of CrSi2 and AlP particles which act as the heterogeneous nuclei for the primary Si phase. The segregation of Si was also inhibited through the adherence of heavier CrSi2 particles to the primary Si particles.
文摘In order to review the effect of partial remelting time on the morphology of initial carbides, semisolid ingots of hypereutectic high Cr17 cast iron were remelted at 1270℃ for four different times, and the changing characteristics of shape factor and the equivalent diameter of initial carbides were analyzed quantitatively using a Leica image analyzer. The results indicate that firstly, the evolution process of the initial carbides' morphology undergoes melting, spheroidization and refining during the partial remelting; secondly, the solute diffusion and interface tension take dominant roles at the primary and the middle-final stages respectively in the process of initial carbide evolution; finally, a perfect structure can be obtained by remelting semisolid ingots at 1270℃ for 15 min.
基金This work has been supported by the Flu,tda~ion Of harbin institute of Technology for Out standing YOungScientists (No. 1832).
文摘A hypereutectic Al-Si alloy powder was prepared by ultrasonic gas atomization process. The morphologies, microstructure and phase constituent of the alloy powder were studied. The results showed that powder of the alloy was very fine and its microstructure was mainly consisted of Si crystals plus intermetallic compound A19FeSi3, which were.very fine and uniformly distributed.
文摘Recent studies revealed that in eutectic to slightly hypereutectic grey irons （CE = 4.3%-4.5%） the presence of austenite dendrites provides an opportunity to improve the cast iron properties, as a high number of eutectic cells are ＂reinforced＂ by austenite dendrites. An iron powder addition proved to be important by promoting dendritic austenite in hypereutectic irons, but was accompanied by adverse effect on the characteristics of potential nuclei for graphite. The purpose of the present paper is to investigate the solidification pattern of these irons. Chill wedges with different cooling moduli （CM = 0.11 - 0.43 cm） were poured in resin bonded sand and metal moulds. Relative clear / mottled / total chill measurement criteria were applied. Iron powder additions led to a higher chill tendency, while single inoculation showed the strongest graphiUzing effect. The various double treatments show an intermediate position, but the inoculant added after iron powder appears to be the most effective in reducing base iron chill tendency, for all cooling moduli and chill evaluation parameters. This performance reflects the improved properties of （Mn,X）S polygonal compounds as nucleation sites for graphite, especially in resin bonded sand mould castings. Both austenite and graphite nucleation benefit from a double addition of iron powder ＋ inoculant, with positive effect on the final structure and chill tendency.
文摘Effects of processing parameters on microstructure evolutions by mechanical stirring, procedures for obtaining thixotropy in semi solid slurries, and procedure for thixoforging component, were investigated in hypereutectic Al Si alloy. It is shown that 605 ℃ was the proper temperature for stirring treatment of this alloy, at which the coarse and plate primary Si crystals were effectively changed to globular crystals with a mean diameter of 200 μm after 50 min stirring, that billets with excellent thixotropy were obtained after 50 min remelting at 575 ℃, in which solid fraction of matrix and primary Si crystals was about 60%, and that a perfect near net shape component of disc casting was obtained by thixoforging.
文摘The microstructural evolution and apparent viscosity of hypereutectic Al-24%Si alloy during semi-solid state shearing were studied with a Searte type viscometer. When the alloy melt was continuously stirred from 720 degreesC to eutectic temperature, the primary Si crystals were gradually changed from elongated platelets to near-spherical shapes. It was found that some nondendritic a-phase formed when the melt was stirred below 585 degreesC. The experiment showed that the semi-solid stirring had strong effect on inhibiting the anisotropic growth of Si crystals during solidification. The apparent viscosity of the alloy melt increased slowly with the decreasing of temperature before the formation of nondendritic alpha -phase, which caused the dramatic increase of apparent viscosity.