The optimum coating composition of alkali Fe powder welding rods was designed by orthogonal experiment with mix rates. A new kind of effective RE-Fe powder welding rod was prepared which could be used at the condition...The optimum coating composition of alkali Fe powder welding rods was designed by orthogonal experiment with mix rates. A new kind of effective RE-Fe powder welding rod was prepared which could be used at the condition of direct and indirect current. The arc characteristics and stabilities of effective Fe powder welding rods containing RE were analyzed by HANNOVER analyzer. The efficiency of Fe powder welding rods was tested by weighting method. It was found that the stability of Fe powder welding rods was improved when it was added with rare earths. The results of impact experiment at low temperatures and SEM analysis on impact break showed that the grain was refined, the welding joint was cleaned, and the mechanical properties of joint was enhanced with proper RE content. It was provided with good processing property for this effective RE-Fe powder welding rod, and its efficiency could arrive at 180%.展开更多
采用机械合金化法制备Al V Fe纳米粉末 ,通过测定M ssbauer效应 ,研究了不同球磨能量对制备Al V Fe纳米粉末的影响·结果表明 ,振动球磨与高能球磨所制备的Al V Fe纳米粉末结构均由非晶和α Al纳米晶组成 ,其非晶含量随着球磨能量...采用机械合金化法制备Al V Fe纳米粉末 ,通过测定M ssbauer效应 ,研究了不同球磨能量对制备Al V Fe纳米粉末的影响·结果表明 ,振动球磨与高能球磨所制备的Al V Fe纳米粉末结构均由非晶和α Al纳米晶组成 ,其非晶含量随着球磨能量的增加而有所不同·展开更多
文摘The optimum coating composition of alkali Fe powder welding rods was designed by orthogonal experiment with mix rates. A new kind of effective RE-Fe powder welding rod was prepared which could be used at the condition of direct and indirect current. The arc characteristics and stabilities of effective Fe powder welding rods containing RE were analyzed by HANNOVER analyzer. The efficiency of Fe powder welding rods was tested by weighting method. It was found that the stability of Fe powder welding rods was improved when it was added with rare earths. The results of impact experiment at low temperatures and SEM analysis on impact break showed that the grain was refined, the welding joint was cleaned, and the mechanical properties of joint was enhanced with proper RE content. It was provided with good processing property for this effective RE-Fe powder welding rod, and its efficiency could arrive at 180%.