Soil tensile strength is a critical parameter governing the initiation and propagation of tensile cracking.This study proposes an eco-friendly approach to improve the tensile behavior and crack resistance of clayey so...Soil tensile strength is a critical parameter governing the initiation and propagation of tensile cracking.This study proposes an eco-friendly approach to improve the tensile behavior and crack resistance of clayey soils.To validate the feasibility and efficacy of the proposed approach,direct tensile tests were employed to determine the tensile strength of the compacted soil with different W-OH treatment concentrations and water contents.Desiccation tests were also performed to evaluate the effectiveness of W-OH treatment in enhancing soil tensile cracking resistance.During this period,the effects of W-OH treatment concentration and water content on tensile properties,soil suction and microstructure were investigated.The tensile tests reveal that W-OH treatment has a significant impact on the tensile strength and failure mode of the soil,which not only effectively enhances the tensile strength and failure displacement,but also changes the brittle failure behavior into a more ductile quasi-brittle failure behavior.The suction measurements and mercury intrusion porosimetry(MIP)tests show that W-OH treatment can slightly reduce soil suction by affecting skeleton structure and increasing macropores.Combined with the microstructural analysis,it becomes evident that the significant improvement in soil tensile behavior through W-OH treatment is mainly attributed to the W-OH gel's ability to provide additional binding force for bridging and encapsulating the soil particles.Moreover,desiccation tests demonstrate that W-OH treatment can significantly reduce or even inhibit the formation of soil tensile cracking.With the increase of W-OH treatment concentration,the surface crack ratio and total crack length are significantly reduced.This study enhances a fundamental understanding of eco-polymer impacts on soil mechanical properties and provides valuable insight into their potential application for improving soil crack resistance.展开更多
DMR-249 A is an indigenously developed high strength low alloy steel for Indian ship building industry for making ship-hull and is extensively used in the construction of war ships and submarines. Welding electrodes c...DMR-249 A is an indigenously developed high strength low alloy steel for Indian ship building industry for making ship-hull and is extensively used in the construction of war ships and submarines. Welding electrodes conforming to SFA 5.5 AWS E8018 C1 has been indigenously developed for welding of this steel using shielded metal arc welding process. In the present study, susceptibility to hydrogen assisted cracking of DMR-249 A steel welds made using this electrode has been assessed using implant test. Implant tests were conducted using this electrode at two different levels of diffusible hydrogen, measured using gas chromatography technique. It is observed that both the steel and the welding consumable are not susceptible to hydrogen assisted cracking even with a high diffusible hydrogen level of 9 m L/100 g of weld metal. In implant tests, specimen did not fracture even after loading to stress levels higher than the yield strength of the base metal. The good resistance of this steel and the welding consumable, even with high levels of diffusible hydrogen, is attributed to absence of a susceptible microstructure in both the weld metal and heat affected zone. Hence, this study shows that, in the absence of a susceptible microstructure, hydrogen assisted cracking is unlikely to occur even if hydrogen level is high. It also confirms that in welding of DMR-249 A with indigenously developed E8018 C1 electrode, hydrogen assisted cracking is not a concern and no preheating is required to avoid it during welding.展开更多
Gas Transmitting From West to East Project' is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long li...Gas Transmitting From West to East Project' is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long line, complex weather and geology features. In this paper, the welding cold cracking susceptibility of domestic X 70 pipeline steel adopted by the project, which is one of the most interesting questions of welding quality about petrol pipeline, was studied by means of oblique Y groove cracking test. The crack ratio of surface and section was tested under the conditions of different welding materials and preheat temperature .The thickness of plate steel was 14.7 mm and 10.3 mm . The results reveal that X 70 pipeline steel has good crack resistance. The research has important value for the construction of large scale pipeline engineering and the application of domestic X 70 pipeline steel.展开更多
Despite the success of guided wave ultrasonic inspection for internal defect detection in steel pipes,its application on polyethylene(PE)pipe remains relatively unexplored.The growth of internal cracks in PE pipe seve...Despite the success of guided wave ultrasonic inspection for internal defect detection in steel pipes,its application on polyethylene(PE)pipe remains relatively unexplored.The growth of internal cracks in PE pipe severely affects its pressure-holding capacity,hence the early detection of internal cracks is crucial for effective pipeline maintenance strategies.This study extends the scope of guided wave-based ultrasonic testing to detect the growth of internal cracks in a natural gas distribution PE pipe.Laboratory experiments and a finite element model were planned to study the wave-crack interaction at different stages of axially oriented internal crack growth with a piezoceramic transducer-based setup arranged in a pitch-catch configuration.Mode dispersion analysis supplemented with preliminary experiments was performed to isolate the optimal inspection frequency,leading to the selection of the T(0,1)mode at 50-kHz for the investigation.A transmission index based on the energy of the T(0,1)mode was developed to trace the extent of simulated crack growth.The findings revealed an inverse linear correlation between the transmission index and the crack depth for crack growth beyond 20%crack depth.展开更多
Cohesive element is developed from the Dugdal-Barenblatt model in the field of fracture mechanics. The mechanical constitutive relation of cohesive element can be artificially assumed depending on the specific applica...Cohesive element is developed from the Dugdal-Barenblatt model in the field of fracture mechanics. The mechanical constitutive relation of cohesive element can be artificially assumed depending on the specific applications. It has been successfully applied in the study of crystal plasticity/brittle fracture process and decohesion between delaminations. In this paper, tensile experiments of large steel plate with different length of pre-existing cracks are conducted. Based on commercial software ABAQUS, cohesive element is adopted to simulate the tensile tests, and appropriate parameter values are obtained by fitting displacement-force curves. Using these parameters, a numerical method is presented by applying cohesive element to thermo-elastic-plastic finite element method （TEP-FEM） to simulate plate rigid restraint cracking （PRRC） tests. By changing constitutive relation of cohesive element, dimensions of the model and welding conditions, the influence of welding restraint intensity and welding conditions on the crack propagation are discussed, respectively. Three types of welding cold cracking are simulated. Significant influence of welding cold cracking on resistant stress in welding line is captured by this numerical method.展开更多
In order to reduce the randomness of the occurrence of cracks and shorten the long cracking time in the traditional concentric ring tests,the elliptical ring test,the square-eccentric ring test,and the eccentric ring ...In order to reduce the randomness of the occurrence of cracks and shorten the long cracking time in the traditional concentric ring tests,the elliptical ring test,the square-eccentric ring test,and the eccentric ring test have been gradually developed.In this paper,we reported experiments on the eccentric ring test and concentric ring test that were carried out to compare the differences between the two methods.It is found that an increase in the water-cement ratio and the amount of aggregate will increase the cracking time.However,a more obvious cracking tendency of cement-based materials can be seen in the eccentric ring test.The correlation between humidity and strain was established by the use of the Kelvin equation and the Laplace equation so that the coupling analysis of humidity and strain during the drying process of cement-based materials could be determined.The experimental results show that the external surface humidity will decrease rapidly in the early stage of drying,while the interior areas of the cement-based materials decrease more slowly.The closer to the inner circle will decrease the humidity slowly.展开更多
The longitudinal cracks distributed along the dam axis in the corridor of a dam may have potential safety hazards.According to the detection results of crack depth and width and the analysis of monitoring data,a three...The longitudinal cracks distributed along the dam axis in the corridor of a dam may have potential safety hazards.According to the detection results of crack depth and width and the analysis of monitoring data,a three-dimensional finite element model is established for numerical simulation calculation and the influence of cracks on the safety of dam structure is analyzed from different aspects such as deformation,stress value,and distribution range.The calculation results show that the maximum principal tensile stress value and the location of the dam body are basically independent of the change of crack depth(within 1.0 m).Regarding local stress around the corridor,the high upstream water level causes cracks to deepen,resulting in an increase in the maximum tensile stress near the crack tip and an expansion of the tensile stress region.展开更多
The catalytic cracking of light diesel oil （235–337 ＆#176;C） over gold‐modified ZSM‐5 was investigated in a small confined fluidized bed at 460 ＆#176;C and ambient pressure. Different Au/ZSM‐5 catalysts were p...The catalytic cracking of light diesel oil （235–337 ＆#176;C） over gold‐modified ZSM‐5 was investigated in a small confined fluidized bed at 460 ＆#176;C and ambient pressure. Different Au/ZSM‐5 catalysts were prepared by a modified deposition‐precipitation method by changing the preparation procedure and the amount of gold loading and were characterized by X‐ray diffraction, N2 adsorp‐tion‐desorption, temperature‐programmed desorption of NH3, transmission electron microscopy and inductively coupled plasma spectrometer. It was found that a small amount of gold had a posi‐tive effect on the catalytic cracking of light diesel oil and increased propylene production at a rela‐tively low temperature. The maintenance of the ZSM‐5 MFI structure, pore size distribution and the density of weak and strong acid sites of the Au/ZSM‐5 catalysts depended on the preparation pa‐rameters and the Au loading. Simultaneous enhancement of the micro‐activity and propylene pro‐duction relies on a synergy between the pore size distribution and the relative intensity of the weak and strong acid sites. A significant improvement in the micro‐activity index with an increase of 4.5 units and in the propylene selectivity with an increase of 23.2 units was obtained over the Au/ZSM‐5 catalyst with an actual Au loading of 0.17 wt%.展开更多
Failure of rock mass that is subjected to compressive loads occurs from initiation, propagation, and linkage of new cracks from preexisting fissures. Our research investigates the cracking behaviour and coalescence pr...Failure of rock mass that is subjected to compressive loads occurs from initiation, propagation, and linkage of new cracks from preexisting fissures. Our research investigates the cracking behaviour and coalescence process in a brittle material with two non-parallel overlapping flaws using a high-speed camera. The coalescence tensile crack and tensile wing cracks were the first cracks to occur from the preexisting flaws. The initiation stresses of the primary cracks at the two tips of each flaw were simultaneous and decreased with reduced flaw inclination angle. The following types of coalescence cracks were identified between the flaws: primary tensile coalescence crack, tensile crack linkage, shear crack linkage, mixed tensile-shear crack, and indirect crack coalescence. Coalescence through tensile linkage occurred mostly at pre-peak stress. In contrast, coalescence through shear or mixed tensile-shear cracks occurred at higher stress. Overall, this study indicates that the geometry of preexisting flaws affect crack initiation and coalescence behaviour.展开更多
Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added ...Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added stainless steel is a kind of possible candidate materials for mitigating SCC since reducing the carbon content and adding nitrogen to offset the loss in strength caused by the decrease in carbon content can mitigate the problem of sensitization. However, the reports of SCC of nitrogen-added stainless steels in high temperature water are few available. The effects of applied potential and sensitization treatment on the SCC of a newly developed nitrogen-containing stainless steel （SS） 316LN in high temperature water doped with chloride at 250 ℃ were studied by using slow strain rate tests （SSRTs）. The SSRT results are compared with our data previously published for 316 SS without nitrogen and 304NG SS with nitrogen, and the possible mechanism affecting the SCC behaviors of the studied steels is also discussed based on SSRT and microstucture analysis results. The susceptibility to cracking of 316LN SS normally increases with increasing potential. The susceptibility to SCC of 316LN SS was less than that of 316 SS and 304NG SS. Sensitization treatment at 700℃ for 30 h showed little effect on the S CC of 316LN S S and significant effect on the S CC of 316 S S. The predominant cracking mode for the 316LN S S in both annealed state and the state after the sensitization treatment was transgranular. The presented conditions of mitigating stress corrosion cracking are some useful information for the safe use of 316LN SS in NPPs.展开更多
In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc wel...In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.展开更多
The subcritical crack growth and fracture toughness in peridotite, lherzolite and amphibolite were investigated with double torsion test. The results show that water-rock interaction has a significant influence on sub...The subcritical crack growth and fracture toughness in peridotite, lherzolite and amphibolite were investigated with double torsion test. The results show that water-rock interaction has a significant influence on subcritical crack growth. With water-rock interaction, the crack velocity increases, while the stress intensity factor declines, which illustrates that water-rock interaction can decrease the strength of rocks and accelerate the subcritical crack growth. Based on Charlse theory and Hilling & Charlse theory, the test data were analyzed by regression and the correlation coefficients were all higher than 0.7, which shows the correlation is significant. This illustrates that both theories can explain the results of tests very well. Therefore, it is believed that the subcritical crack growth attributes to the breaking of chemical bond, which is caused by the combined effect of the tensile stress and the chemical reaction between the material at crack tip and the corrosive agent. Meanwhile, water-rock interaction has a vital effect on fracture toughness. The fracture toughness of samples under atmospheric environment is higher than that of samples immersed in water. And water-rock interaction has larger influence on fracture toughness in amphibolite than that in peridotite and lherzolite.展开更多
High-temperature chromium(Cr)-zirconium(Zr)interdiffusion commonly occurs in Cr-coated zircaloys applied for enhanced accident-tolerant fuel(ATF)claddings.Such interdiffusion changes the interfacial microstructure and...High-temperature chromium(Cr)-zirconium(Zr)interdiffusion commonly occurs in Cr-coated zircaloys applied for enhanced accident-tolerant fuel(ATF)claddings.Such interdiffusion changes the interfacial microstructure and thus the fracture mechanism of the coating under external loading.In this study,the interdiffusion behavior in a magnetron sputtered Cr coating deposited on a Zr-4 alloy was studied in a vacuum environment at 1160C.In addition,the effect of interdiffusion on the microcracking behavior of the Cr coating was determined by in situ three-point bending tests.The experimental results show that the interdiffusion behavior resulted in the formation of a ZrCr2 layer,accompanied by the consumption of Cr coating and interfacial roughening.The growth of the diffusion layer followed a nearly parabolic law with respect to annealing time,and the residual stress of the annealed coating decreased with increasing annealing time.Under external loading,a large number of cracks were generated in the brittle interlayer,and some interfacial cracks were formed and grew at the ZrCr2/Zr-4 interface.Despite the remarkable microcracks in the ZrCr2 layer,the vacuum-annealed Cr coating has significantly fewer cracks than the original coating,mainly because of the recrystallization of the coating during annealing.展开更多
The HAZ cracking test in EB welding condition and hot ductility test show that the cracking mechanism is the formation of Ni - Ni5Zr eutectic which is resulting from the enrichment of Zr in grain boundaries during ...The HAZ cracking test in EB welding condition and hot ductility test show that the cracking mechanism is the formation of Ni - Ni5Zr eutectic which is resulting from the enrichment of Zr in grain boundaries during welding.In order to eliminate HAZ cracks the diffusion and recrystalization anealing treatment after cast and during cold rolling should be conducted in vacuum or protecting atmosphere and at the same time a slow welding speed is necessary.展开更多
Eddy current testing is a nondestructive testing method, which is used to detect discontinuities and defects in conductive materials. Using this technique, two different types of artificial defects in a railhead were ...Eddy current testing is a nondestructive testing method, which is used to detect discontinuities and defects in conductive materials. Using this technique, two different types of artificial defects in a railhead were evaluated in order to analyze the relationship between different types of defects and eddy current signals, and to obtain data on the size of the rail surface defects and crack location. The actually used rail sample was also studied. Surface cracks and defects were clearly observed as amplitude and phase changes of detected signals. This study succeeds in quantitatively analyzing and discriminating the damage types.展开更多
Slow strain rate testing （SSRT） was employed to study the stress corrosion cracking （SCC） behavior of ZE41 magnesium alloy in 0.01 M NaCl solution. Smooth tensile specimens with different thicknesses were strained...Slow strain rate testing （SSRT） was employed to study the stress corrosion cracking （SCC） behavior of ZE41 magnesium alloy in 0.01 M NaCl solution. Smooth tensile specimens with different thicknesses were strained dynamically in both longitudinal and transverse direction under permanent immersions at a strain rate of 10-6 s-1. It is found that ZE41 magnesium alloy is susceptible to SCC in 0.01 M NaCl solution. The SCC susceptibility of the thinner specimen is lower than that of the thicker specimen. Also, the longitudinal specimens are slightly more susceptible to SCC than the transverse specimens. The SCC mechanism of magnesium alloy is attributed to the combination of anodic dissolution with hydrogen embrittlement.展开更多
For decades, nacre has inspired researchers because of its sophisticated hierarchical structure and remarkable mechanical properties, especially its extreme fracture toughness compared with that of its predominant con...For decades, nacre has inspired researchers because of its sophisticated hierarchical structure and remarkable mechanical properties, especially its extreme fracture toughness compared with that of its predominant constituent,CaCO3, in the form of aragonite. Crack deflection has been extensively reported and regarded as the principal toughening mechanism for nacre. In this paper, our attention is focused on crack evolution in nacre under a quasi-static state. We use the notched three-point bending test of dehydrated nacre in situ in a scanning electron microscope(SEM) to monitor the evolution of damage mechanisms ahead of the crack tip. The observations show that the crack deflection actually occurs by constrained microcracking. On the basis of our findings, a crack propagation model is proposed, which will contribute to uncovering the underlying mechanisms of nacre’s fracture toughness and its damage evolution. These investigations would be of great value to the design and synthesis of novel biomimetic materials.展开更多
High-performance concrete （HPC） is stronger and more durable than conventional concrete. However, shrinkage and shrinkage cracking are common phenomena in HPC, especially early-age cracking. This study assessed earl...High-performance concrete （HPC） is stronger and more durable than conventional concrete. However, shrinkage and shrinkage cracking are common phenomena in HPC, especially early-age cracking. This study assessed early-age cracking of HPC for two mixtures using restrained ring tests. The two mixtures were produced with water/binder mass ratio （mw/mB） of 0.22 and 0.40, respectively. The results show that, with greater steel thickness, the higher degree of restraint resulted in a higher interface pressure and earlier cracking. With steel thickness of 6 mm, 19 mm, and 30 mm, the age of cracking were, respectively, 12 days, 8 days, and 5.4 days with the mw/mB = 0.22 mixture; and 22.5 days, 12.6 days, and 7.1 days with the mw/mB= 0.40 mixture. Cases of the same steel thickness show that the ring specimens with a thicker concrete wall crack later. With the mw/mB = 0.22 mixture, concrete walls with thicknesses of 37.5 mm, 75 mm, and 112.5 mm cracked at 3.4 days, 8.0 days, and 9.8 days, respectively; with the mw/mB = 0.40 mixture, the ages of cracking were 7.1 days, 12.6 days, and 16.0 days, respectively.展开更多
The effect of hydrogen on the fractttre behaviors of Incoloy alloy 825 was investigated by means of slow strain rate testing （SSRT） Hydrogen was introduced into the sample by electrochemical charging. The results sh...The effect of hydrogen on the fractttre behaviors of Incoloy alloy 825 was investigated by means of slow strain rate testing （SSRT） Hydrogen was introduced into the sample by electrochemical charging. The results show that surface microcracks form gradually during ag- ing at room temperature when desorption of hydrogen takes place after hydrogen charging at a current density of 5 mA/cm^2 for 24 h. SSRT shows that the increase of ductility loss is significantly obvious as the hydrogen charging current density increases. Scanning electron microscopy （SEM） images reveal ductile fracture in the pre-charged sample with low current densities, while the fracture includes small quasi-cleavage regions and tends to be brittle fracture as the hydrogen charging current density increases to 5 mA/cm^2.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.41925012,42230710)Key Laboratory Cooperation Special Project of Western Cross Team of Western Light,Chinese Academy of Sciences(Grant No.xbzg-zdsys-202107).
文摘Soil tensile strength is a critical parameter governing the initiation and propagation of tensile cracking.This study proposes an eco-friendly approach to improve the tensile behavior and crack resistance of clayey soils.To validate the feasibility and efficacy of the proposed approach,direct tensile tests were employed to determine the tensile strength of the compacted soil with different W-OH treatment concentrations and water contents.Desiccation tests were also performed to evaluate the effectiveness of W-OH treatment in enhancing soil tensile cracking resistance.During this period,the effects of W-OH treatment concentration and water content on tensile properties,soil suction and microstructure were investigated.The tensile tests reveal that W-OH treatment has a significant impact on the tensile strength and failure mode of the soil,which not only effectively enhances the tensile strength and failure displacement,but also changes the brittle failure behavior into a more ductile quasi-brittle failure behavior.The suction measurements and mercury intrusion porosimetry(MIP)tests show that W-OH treatment can slightly reduce soil suction by affecting skeleton structure and increasing macropores.Combined with the microstructural analysis,it becomes evident that the significant improvement in soil tensile behavior through W-OH treatment is mainly attributed to the W-OH gel's ability to provide additional binding force for bridging and encapsulating the soil particles.Moreover,desiccation tests demonstrate that W-OH treatment can significantly reduce or even inhibit the formation of soil tensile cracking.With the increase of W-OH treatment concentration,the surface crack ratio and total crack length are significantly reduced.This study enhances a fundamental understanding of eco-polymer impacts on soil mechanical properties and provides valuable insight into their potential application for improving soil crack resistance.
文摘DMR-249 A is an indigenously developed high strength low alloy steel for Indian ship building industry for making ship-hull and is extensively used in the construction of war ships and submarines. Welding electrodes conforming to SFA 5.5 AWS E8018 C1 has been indigenously developed for welding of this steel using shielded metal arc welding process. In the present study, susceptibility to hydrogen assisted cracking of DMR-249 A steel welds made using this electrode has been assessed using implant test. Implant tests were conducted using this electrode at two different levels of diffusible hydrogen, measured using gas chromatography technique. It is observed that both the steel and the welding consumable are not susceptible to hydrogen assisted cracking even with a high diffusible hydrogen level of 9 m L/100 g of weld metal. In implant tests, specimen did not fracture even after loading to stress levels higher than the yield strength of the base metal. The good resistance of this steel and the welding consumable, even with high levels of diffusible hydrogen, is attributed to absence of a susceptible microstructure in both the weld metal and heat affected zone. Hence, this study shows that, in the absence of a susceptible microstructure, hydrogen assisted cracking is unlikely to occur even if hydrogen level is high. It also confirms that in welding of DMR-249 A with indigenously developed E8018 C1 electrode, hydrogen assisted cracking is not a concern and no preheating is required to avoid it during welding.
文摘Gas Transmitting From West to East Project' is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long line, complex weather and geology features. In this paper, the welding cold cracking susceptibility of domestic X 70 pipeline steel adopted by the project, which is one of the most interesting questions of welding quality about petrol pipeline, was studied by means of oblique Y groove cracking test. The crack ratio of surface and section was tested under the conditions of different welding materials and preheat temperature .The thickness of plate steel was 14.7 mm and 10.3 mm . The results reveal that X 70 pipeline steel has good crack resistance. The research has important value for the construction of large scale pipeline engineering and the application of domestic X 70 pipeline steel.
基金the financial support provided by USDOT Pipeline and Hazardous Materials Safety Administration (PHMSA)through the Competitive Academic Agreement Program (CAAP)。
文摘Despite the success of guided wave ultrasonic inspection for internal defect detection in steel pipes,its application on polyethylene(PE)pipe remains relatively unexplored.The growth of internal cracks in PE pipe severely affects its pressure-holding capacity,hence the early detection of internal cracks is crucial for effective pipeline maintenance strategies.This study extends the scope of guided wave-based ultrasonic testing to detect the growth of internal cracks in a natural gas distribution PE pipe.Laboratory experiments and a finite element model were planned to study the wave-crack interaction at different stages of axially oriented internal crack growth with a piezoceramic transducer-based setup arranged in a pitch-catch configuration.Mode dispersion analysis supplemented with preliminary experiments was performed to isolate the optimal inspection frequency,leading to the selection of the T(0,1)mode at 50-kHz for the investigation.A transmission index based on the energy of the T(0,1)mode was developed to trace the extent of simulated crack growth.The findings revealed an inverse linear correlation between the transmission index and the crack depth for crack growth beyond 20%crack depth.
文摘Cohesive element is developed from the Dugdal-Barenblatt model in the field of fracture mechanics. The mechanical constitutive relation of cohesive element can be artificially assumed depending on the specific applications. It has been successfully applied in the study of crystal plasticity/brittle fracture process and decohesion between delaminations. In this paper, tensile experiments of large steel plate with different length of pre-existing cracks are conducted. Based on commercial software ABAQUS, cohesive element is adopted to simulate the tensile tests, and appropriate parameter values are obtained by fitting displacement-force curves. Using these parameters, a numerical method is presented by applying cohesive element to thermo-elastic-plastic finite element method （TEP-FEM） to simulate plate rigid restraint cracking （PRRC） tests. By changing constitutive relation of cohesive element, dimensions of the model and welding conditions, the influence of welding restraint intensity and welding conditions on the crack propagation are discussed, respectively. Three types of welding cold cracking are simulated. Significant influence of welding cold cracking on resistant stress in welding line is captured by this numerical method.
基金Funded by the National Natural Science Foundation of China(No.51778257)。
文摘In order to reduce the randomness of the occurrence of cracks and shorten the long cracking time in the traditional concentric ring tests,the elliptical ring test,the square-eccentric ring test,and the eccentric ring test have been gradually developed.In this paper,we reported experiments on the eccentric ring test and concentric ring test that were carried out to compare the differences between the two methods.It is found that an increase in the water-cement ratio and the amount of aggregate will increase the cracking time.However,a more obvious cracking tendency of cement-based materials can be seen in the eccentric ring test.The correlation between humidity and strain was established by the use of the Kelvin equation and the Laplace equation so that the coupling analysis of humidity and strain during the drying process of cement-based materials could be determined.The experimental results show that the external surface humidity will decrease rapidly in the early stage of drying,while the interior areas of the cement-based materials decrease more slowly.The closer to the inner circle will decrease the humidity slowly.
基金Zhejiang Provincial Natural Science Foundation of China for Young Scholars(Project No.:LQ20A020009)National College Students’Innovation and Entrepreneurship Training Program(Project No.:202311842014X)。
文摘The longitudinal cracks distributed along the dam axis in the corridor of a dam may have potential safety hazards.According to the detection results of crack depth and width and the analysis of monitoring data,a three-dimensional finite element model is established for numerical simulation calculation and the influence of cracks on the safety of dam structure is analyzed from different aspects such as deformation,stress value,and distribution range.The calculation results show that the maximum principal tensile stress value and the location of the dam body are basically independent of the change of crack depth(within 1.0 m).Regarding local stress around the corridor,the high upstream water level causes cracks to deepen,resulting in an increase in the maximum tensile stress near the crack tip and an expansion of the tensile stress region.
基金supported by the Shandong Taishan Scholarship, the Yantai double-hundreds talents planthe Shandong Natural Science Founda-tion (ZR2015BM006)~~
文摘The catalytic cracking of light diesel oil （235–337 ＆#176;C） over gold‐modified ZSM‐5 was investigated in a small confined fluidized bed at 460 ＆#176;C and ambient pressure. Different Au/ZSM‐5 catalysts were prepared by a modified deposition‐precipitation method by changing the preparation procedure and the amount of gold loading and were characterized by X‐ray diffraction, N2 adsorp‐tion‐desorption, temperature‐programmed desorption of NH3, transmission electron microscopy and inductively coupled plasma spectrometer. It was found that a small amount of gold had a posi‐tive effect on the catalytic cracking of light diesel oil and increased propylene production at a rela‐tively low temperature. The maintenance of the ZSM‐5 MFI structure, pore size distribution and the density of weak and strong acid sites of the Au/ZSM‐5 catalysts depended on the preparation pa‐rameters and the Au loading. Simultaneous enhancement of the micro‐activity and propylene pro‐duction relies on a synergy between the pore size distribution and the relative intensity of the weak and strong acid sites. A significant improvement in the micro‐activity index with an increase of 4.5 units and in the propylene selectivity with an increase of 23.2 units was obtained over the Au/ZSM‐5 catalyst with an actual Au loading of 0.17 wt%.
基金supported by the National Natural Science Foundation of China (Grants 41572310, 41272351)the Strategic Priority Research Program of the Chinese Academy of Sciences (Grants XDB10030301, XDB10030304)support provided by the CAS-TWAS Presidential Fellowship, University of Chinese Academy of Sciences, Beijing, China
文摘Failure of rock mass that is subjected to compressive loads occurs from initiation, propagation, and linkage of new cracks from preexisting fissures. Our research investigates the cracking behaviour and coalescence process in a brittle material with two non-parallel overlapping flaws using a high-speed camera. The coalescence tensile crack and tensile wing cracks were the first cracks to occur from the preexisting flaws. The initiation stresses of the primary cracks at the two tips of each flaw were simultaneous and decreased with reduced flaw inclination angle. The following types of coalescence cracks were identified between the flaws: primary tensile coalescence crack, tensile crack linkage, shear crack linkage, mixed tensile-shear crack, and indirect crack coalescence. Coalescence through tensile linkage occurred mostly at pre-peak stress. In contrast, coalescence through shear or mixed tensile-shear cracks occurred at higher stress. Overall, this study indicates that the geometry of preexisting flaws affect crack initiation and coalescence behaviour.
基金supported by National Basic Research Program of China (973 Program, Grant No. 2006CB605005)Shanghai Municipal Committee of Science and Technology of china(Grant No. 005207019,Grant No. 08520708000)
文摘Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added stainless steel is a kind of possible candidate materials for mitigating SCC since reducing the carbon content and adding nitrogen to offset the loss in strength caused by the decrease in carbon content can mitigate the problem of sensitization. However, the reports of SCC of nitrogen-added stainless steels in high temperature water are few available. The effects of applied potential and sensitization treatment on the SCC of a newly developed nitrogen-containing stainless steel （SS） 316LN in high temperature water doped with chloride at 250 ℃ were studied by using slow strain rate tests （SSRTs）. The SSRT results are compared with our data previously published for 316 SS without nitrogen and 304NG SS with nitrogen, and the possible mechanism affecting the SCC behaviors of the studied steels is also discussed based on SSRT and microstucture analysis results. The susceptibility to cracking of 316LN SS normally increases with increasing potential. The susceptibility to SCC of 316LN SS was less than that of 316 SS and 304NG SS. Sensitization treatment at 700℃ for 30 h showed little effect on the S CC of 316LN S S and significant effect on the S CC of 316 S S. The predominant cracking mode for the 316LN S S in both annealed state and the state after the sensitization treatment was transgranular. The presented conditions of mitigating stress corrosion cracking are some useful information for the safe use of 316LN SS in NPPs.
基金Armament Research Board (ARMREB),New Delhi for funding this projectwork (Project No MAA/03/41)
文摘In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.
基金Project(51374246,51474249)supported by the National Natural Science Foundation of ChinaProject(2013FJ6002)supported by the Science-Technology Project of Science-Technology Department of Hunan Province,China
文摘The subcritical crack growth and fracture toughness in peridotite, lherzolite and amphibolite were investigated with double torsion test. The results show that water-rock interaction has a significant influence on subcritical crack growth. With water-rock interaction, the crack velocity increases, while the stress intensity factor declines, which illustrates that water-rock interaction can decrease the strength of rocks and accelerate the subcritical crack growth. Based on Charlse theory and Hilling & Charlse theory, the test data were analyzed by regression and the correlation coefficients were all higher than 0.7, which shows the correlation is significant. This illustrates that both theories can explain the results of tests very well. Therefore, it is believed that the subcritical crack growth attributes to the breaking of chemical bond, which is caused by the combined effect of the tensile stress and the chemical reaction between the material at crack tip and the corrosive agent. Meanwhile, water-rock interaction has a vital effect on fracture toughness. The fracture toughness of samples under atmospheric environment is higher than that of samples immersed in water. And water-rock interaction has larger influence on fracture toughness in amphibolite than that in peridotite and lherzolite.
基金the Guangdong Major Project of Basic and Applied Basic Research(No.2019B030302011)National Natural Science Foundation of China(Nos.52005523,U2032143,11902370)+3 种基金International Sci&Tech Cooperation Program of GuangDong Province(No.2019A050510022)Key Research Project of GuangDong Province(Nos.2019B010943001 and 2017B020235001)China Postdoctoral Science Foundation(Nos.2019M653173 and 2019TQ0374)the Fundamental Research Funds for the Central Universities,Sun Yat-sen University(No.2021qntd12).
文摘High-temperature chromium(Cr)-zirconium(Zr)interdiffusion commonly occurs in Cr-coated zircaloys applied for enhanced accident-tolerant fuel(ATF)claddings.Such interdiffusion changes the interfacial microstructure and thus the fracture mechanism of the coating under external loading.In this study,the interdiffusion behavior in a magnetron sputtered Cr coating deposited on a Zr-4 alloy was studied in a vacuum environment at 1160C.In addition,the effect of interdiffusion on the microcracking behavior of the Cr coating was determined by in situ three-point bending tests.The experimental results show that the interdiffusion behavior resulted in the formation of a ZrCr2 layer,accompanied by the consumption of Cr coating and interfacial roughening.The growth of the diffusion layer followed a nearly parabolic law with respect to annealing time,and the residual stress of the annealed coating decreased with increasing annealing time.Under external loading,a large number of cracks were generated in the brittle interlayer,and some interfacial cracks were formed and grew at the ZrCr2/Zr-4 interface.Despite the remarkable microcracks in the ZrCr2 layer,the vacuum-annealed Cr coating has significantly fewer cracks than the original coating,mainly because of the recrystallization of the coating during annealing.
文摘The HAZ cracking test in EB welding condition and hot ductility test show that the cracking mechanism is the formation of Ni - Ni5Zr eutectic which is resulting from the enrichment of Zr in grain boundaries during welding.In order to eliminate HAZ cracks the diffusion and recrystalization anealing treatment after cast and during cold rolling should be conducted in vacuum or protecting atmosphere and at the same time a slow welding speed is necessary.
文摘Eddy current testing is a nondestructive testing method, which is used to detect discontinuities and defects in conductive materials. Using this technique, two different types of artificial defects in a railhead were evaluated in order to analyze the relationship between different types of defects and eddy current signals, and to obtain data on the size of the rail surface defects and crack location. The actually used rail sample was also studied. Surface cracks and defects were clearly observed as amplitude and phase changes of detected signals. This study succeeds in quantitatively analyzing and discriminating the damage types.
基金Funded by the National Natural Science Foundation of China (No.50771093)
文摘Slow strain rate testing （SSRT） was employed to study the stress corrosion cracking （SCC） behavior of ZE41 magnesium alloy in 0.01 M NaCl solution. Smooth tensile specimens with different thicknesses were strained dynamically in both longitudinal and transverse direction under permanent immersions at a strain rate of 10-6 s-1. It is found that ZE41 magnesium alloy is susceptible to SCC in 0.01 M NaCl solution. The SCC susceptibility of the thinner specimen is lower than that of the thicker specimen. Also, the longitudinal specimens are slightly more susceptible to SCC than the transverse specimens. The SCC mechanism of magnesium alloy is attributed to the combination of anodic dissolution with hydrogen embrittlement.
基金supported by the National Natural Science Foundation of China (Grants 91216108, 11432014, 11672301, 11372318, and 11502273)the Strategic Priority Research Program of the Chinese Academy of Sciences (Grant XDB22040501)
文摘For decades, nacre has inspired researchers because of its sophisticated hierarchical structure and remarkable mechanical properties, especially its extreme fracture toughness compared with that of its predominant constituent,CaCO3, in the form of aragonite. Crack deflection has been extensively reported and regarded as the principal toughening mechanism for nacre. In this paper, our attention is focused on crack evolution in nacre under a quasi-static state. We use the notched three-point bending test of dehydrated nacre in situ in a scanning electron microscope(SEM) to monitor the evolution of damage mechanisms ahead of the crack tip. The observations show that the crack deflection actually occurs by constrained microcracking. On the basis of our findings, a crack propagation model is proposed, which will contribute to uncovering the underlying mechanisms of nacre’s fracture toughness and its damage evolution. These investigations would be of great value to the design and synthesis of novel biomimetic materials.
文摘High-performance concrete （HPC） is stronger and more durable than conventional concrete. However, shrinkage and shrinkage cracking are common phenomena in HPC, especially early-age cracking. This study assessed early-age cracking of HPC for two mixtures using restrained ring tests. The two mixtures were produced with water/binder mass ratio （mw/mB） of 0.22 and 0.40, respectively. The results show that, with greater steel thickness, the higher degree of restraint resulted in a higher interface pressure and earlier cracking. With steel thickness of 6 mm, 19 mm, and 30 mm, the age of cracking were, respectively, 12 days, 8 days, and 5.4 days with the mw/mB = 0.22 mixture; and 22.5 days, 12.6 days, and 7.1 days with the mw/mB= 0.40 mixture. Cases of the same steel thickness show that the ring specimens with a thicker concrete wall crack later. With the mw/mB = 0.22 mixture, concrete walls with thicknesses of 37.5 mm, 75 mm, and 112.5 mm cracked at 3.4 days, 8.0 days, and 9.8 days, respectively; with the mw/mB = 0.40 mixture, the ages of cracking were 7.1 days, 12.6 days, and 16.0 days, respectively.
文摘The effect of hydrogen on the fractttre behaviors of Incoloy alloy 825 was investigated by means of slow strain rate testing （SSRT） Hydrogen was introduced into the sample by electrochemical charging. The results show that surface microcracks form gradually during ag- ing at room temperature when desorption of hydrogen takes place after hydrogen charging at a current density of 5 mA/cm^2 for 24 h. SSRT shows that the increase of ductility loss is significantly obvious as the hydrogen charging current density increases. Scanning electron microscopy （SEM） images reveal ductile fracture in the pre-charged sample with low current densities, while the fracture includes small quasi-cleavage regions and tends to be brittle fracture as the hydrogen charging current density increases to 5 mA/cm^2.