Three different stress states of the combination of tensile（t） stress and compressive（c） stress,t t,t c and t c c,exist in the deformed commercially pure titanium（CP-Ti） sheet during cold drawing-bulging.The tex...Three different stress states of the combination of tensile（t） stress and compressive（c） stress,t t,t c and t c c,exist in the deformed commercially pure titanium（CP-Ti） sheet during cold drawing-bulging.The textures and microstructures in the different stress state regions were investigated by means of XRD and TEM analysis.Similar development of texture and microstructure is achieved with less thickness strain under multiaxial stresses in drawing-bulging than in cold rolling.The results show that texture and microstructure are much sensitive to multiaxial stresses.Twinning is more easily activated under compressive stress than tensile stress.Prism a slip is heavily affected by tensile stress,resulting in a remarkable change of the intensity of（0°,35°,0°） texture,while pyramidal c＋a slip,forming（20°,35°,30°） texture,weakens with the increase of thickness strain in spite of stress state.展开更多
基金Project(2010CB731701) supported by the National Basic Research Program of ChinaProjects(50805121,51175428) supported by the National Natural Science Foundation of China+3 种基金Project(50935007) supported by the National Natural Science Foundation of China for Key ProgramProject(NPU-FFR-JC20100229) supported by the Foundation for Fundamental Research of Northwestern Polytechnical University in ChinaProject(2011-P06) supported by the Foundation of the State Key Laboratory of Materials Processing and Die & Mould Technology,Huazhong University of Science and TechnologyProject(B08040) supported by Program of Introducing Talents of Discipline to Universities("111"),China
文摘Three different stress states of the combination of tensile（t） stress and compressive（c） stress,t t,t c and t c c,exist in the deformed commercially pure titanium（CP-Ti） sheet during cold drawing-bulging.The textures and microstructures in the different stress state regions were investigated by means of XRD and TEM analysis.Similar development of texture and microstructure is achieved with less thickness strain under multiaxial stresses in drawing-bulging than in cold rolling.The results show that texture and microstructure are much sensitive to multiaxial stresses.Twinning is more easily activated under compressive stress than tensile stress.Prism a slip is heavily affected by tensile stress,resulting in a remarkable change of the intensity of（0°,35°,0°） texture,while pyramidal c＋a slip,forming（20°,35°,30°） texture,weakens with the increase of thickness strain in spite of stress state.