The evolution of the microstructure and tensile rupture mechanism of laser welds in UNS N10003 alloy exposed to 700℃are investigated.Fine M_(6)C carbides precipitate around the primary eutectic M_(6)C-γcarbides in t...The evolution of the microstructure and tensile rupture mechanism of laser welds in UNS N10003 alloy exposed to 700℃are investigated.Fine M_(6)C carbides precipitate around the primary eutectic M_(6)C-γcarbides in the fusion zone after 100 h of exposure.During long-term thermal exposure,the size of the fine M_(6)C carbides increased.The eutectic M_(6)C-γcarbides in the as-welded fusion zone transformed into spherical M_(6)C carbides as the exposure time extends to 10000 h.Additionally,the spherical M_(6)C particles exhibit size coarsening with increasing exposure time.The tensile properties of the welded joints are not adversely affected by the evolution of eutectic M_(6)C-γcarbides and the coarsening of M_(6)C carbides.展开更多
基金supported by the Technology Star of Shanghai Institute of Applied Physics,Chinese Academy of Sciences(No.E2551130)the Youth Innovation Promotion Association,Chinese Academy of Sciences(No.E2292202).
文摘The evolution of the microstructure and tensile rupture mechanism of laser welds in UNS N10003 alloy exposed to 700℃are investigated.Fine M_(6)C carbides precipitate around the primary eutectic M_(6)C-γcarbides in the fusion zone after 100 h of exposure.During long-term thermal exposure,the size of the fine M_(6)C carbides increased.The eutectic M_(6)C-γcarbides in the as-welded fusion zone transformed into spherical M_(6)C carbides as the exposure time extends to 10000 h.Additionally,the spherical M_(6)C particles exhibit size coarsening with increasing exposure time.The tensile properties of the welded joints are not adversely affected by the evolution of eutectic M_(6)C-γcarbides and the coarsening of M_(6)C carbides.