The core-shell structured TiO2/SiO2 @Fe3O4 photocatalysts were prepared using Fe3O4 as magnetic core,tetraethoxysilane（TEOS） as silica source and tetrabutyl titanate（TBOT） as titanium sources.The as-obtained struc...The core-shell structured TiO2/SiO2 @Fe3O4 photocatalysts were prepared using Fe3O4 as magnetic core,tetraethoxysilane（TEOS） as silica source and tetrabutyl titanate（TBOT） as titanium sources.The as-obtained structure was composed of a SiO2@Fe3O4 core and a porous TiO2 shell.The diameter of SiO2@Fe3O4 core was about 205 nm with thickness of porous TiO2 of about 5-6 nm.The 9%TiO2/6%SiO2@Fe3O4 microspheres possess the highest BET surface area and the BJH pore volume,which are 373.5 m2.g-1 and 0.28 cm3.g-1,respectively.The 9%TiO2/6%SiO2@Fe3O4 photocatalyst exhibited an excellent performance for the degradation of methyl orange and methylene blue dyes.Two different dyes were completely decolorized in 60 min under UV irradiation.The photocatalytic activity and the amount of catalyst were almost not decrease after recycling for 6 times by using external magnetic field.展开更多
A hollow glass microsphere(HGM)/TiO2 composite hollow sphere was successfully prepared via a simple precipitation method.The TiO2 coating layers grew on the surface of the HGMs that range from 20 to 50μm in diameter ...A hollow glass microsphere(HGM)/TiO2 composite hollow sphere was successfully prepared via a simple precipitation method.The TiO2 coating layers grew on the surface of the HGMs that range from 20 to 50μm in diameter as nanoparticles with the formation of the SiO Ti bonds.The growth mechanism accounting for the formation of the TiO2 nanolayers was proposed.The morphology,composition,thermal insulation properties,and visible-near infrared(VIS-NIR)refl ectance of the HGMs/TiO2 composite hollow spheres were characterized.The VIS-NIR reflectance of the HGMs/TiO2 composite hollow spheres increased by more than 30%compared to raw HGMs.The thermal conductivity of the particles is 0.058 W/(m K).The result indicates that the VIS-NIR reflectance of the composite hollow spheres is strongly influenced by the coating of TiO2.The composite hollow spheres were used as the main functional filler to prepare the organic-inorganic composite coatings.The glass substrates coated by the organic-inorganic coatings had lower thermal conductivity and higher near infrared reflectivity.Therefore,the HGMs/TiO2 composite hollow spheres can reflect most of the solar energy and effectively keep out the heat as a thermal insulation coating for energy-saving constructions.展开更多
TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to es...TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to estimate activity of catalysts and determine the kinetics. And the effects of parameters including the initial concentration of AY, light intensity and TiO2 content in catalysts were examined. The results indicate that TAs has a higher efficiency in decomposition of AY than P25, pure TiO2 particles as well as the mixture of TiO2 powder and active carbon. The photocatalytic degradation rate is found to follow the pseudo-first order kinetics with respect to the AY concentration. The new kinetic model fairly resembles the classic Langmuir-Hinshelwood equation, and the rate constant is proportional to the square root of the light intensity in a wide range. However, its absorption performance depends on the surface areas of catalysts. The model fits quite well with the experimental data and elucidates phenomena about the effects of the TiO2 content in TAs on the degradation rate.展开更多
TiO2-coated SnO2 （TCS） hollow spheres, which are new anode materials for lithium ion （Li-ion） batteries, were prepared and characterized with X-ray diffraction （XRD）, scanning electron microscopy （SEM）, transm...TiO2-coated SnO2 （TCS） hollow spheres, which are new anode materials for lithium ion （Li-ion） batteries, were prepared and characterized with X-ray diffraction （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, cyclic voltammetry （CV）, and galvanostatic charge/discharge tests. The results obtained from XRD, SEM, and TEM show that TiO2 can be uniforrrdy coated on the surface of SnO2 hollow spheres with the assistance of anionic surfactant. The cyclic voltammograms indicate that both TiO2 and SnO2 exhibit the activity for Li-ion storage. The charge/discharge tests show that the prepared TCS hollow spheres have a higher reversible coulomb efficiency and a better cycling stability than the uncoated SnO2 hollow spheres.展开更多
The anti-bacterial adhesion properties of TiO2-coated polymethyl methacrylate （PMMA） surfaces are investigated systematically. In detail, the adhesion of S. aureus （gram positive） and E. coli （gram negative） to ...The anti-bacterial adhesion properties of TiO2-coated polymethyl methacrylate （PMMA） surfaces are investigated systematically. In detail, the adhesion of S. aureus （gram positive） and E. coli （gram negative） to TiO2-coated and uncoated PMMA surfaces are performed by the plate counting method. Afterwards, the adhesion free energy of bacteria on both supporting materials is quantified using the thermodynamic approach of Lifshitz van der Waals and acid/base interactions. The superior anti-adhesion capability of TiO2-coated PMMA is demonstrated when compared to native PMMA, both experimentally and theoretically.展开更多
The photocatalytic degradation of the synthetic textile dye Reactive Yellow 145 (RY 145) in aqueous solution, using TiO2 coated non-woven fibers as photocatalyst, under UV-lamp irradiation, was studied. The effects of...The photocatalytic degradation of the synthetic textile dye Reactive Yellow 145 (RY 145) in aqueous solution, using TiO2 coated non-woven fibers as photocatalyst, under UV-lamp irradiation, was studied. The effects of the operational parameters such as initial dye concentration, pH, addition of oxidant hydrogen peroxide and addition of ethanol on the reaction rate were investigated. The effect of some inorganic ions such as and , commonly present in real effluents, on the photodegradation of RY 145 was also examined. The experimental results showed that the photocatalytic degradation rate was favoured by a high concentration of solution in respect to Langmuir-Hinshelwood model. The maximum rate of complete decolorization of RY 145 was observed in the acidic medium at pH 3. The presence of and anions led to an increase of the effectiveness of the photocatalytic degradation. However, the presence of and anions decreased differently the photodegradation reaction rate. TiO2/UV process was proved to be capable of the complete degradation of the RY 145.展开更多
Several lithium-ion batteries of 18650-type were assembled with pristine or Al2O3-coated LiNi0.4Co0.2Mn0.4O2（NCM） as cathode material and mesocarbon microbeads（MCMB） as anode material.The cycling performance of th...Several lithium-ion batteries of 18650-type were assembled with pristine or Al2O3-coated LiNi0.4Co0.2Mn0.4O2（NCM） as cathode material and mesocarbon microbeads（MCMB） as anode material.The cycling performance of the batteries was examined under 25 °C at a 2C rate within a potential range of 2.75―4.20 V.The changes of the crystal structure,the lattice parameter,the mean crystallite size,and the mean micro-strain of pristine NCM and Al2O3-coated NCM during the charge-discharge cycling were determined by X-ray diffraction（XRD）.The results indicate that the bulk structure of Al2O3-coated NCM is more stable than that of pristine NCM,which leads to the better cycling performance of Al2O3-coated NCM compared to that of pristine NCM.展开更多
Growth of single-crystal Sn O_2 nanowires using a fluorine-doped Sn O_2(FTO) thin film as both the source and substrate is demonstrated for the first time at relatively low temperature(580 °C) which preserves the...Growth of single-crystal Sn O_2 nanowires using a fluorine-doped Sn O_2(FTO) thin film as both the source and substrate is demonstrated for the first time at relatively low temperature(580 °C) which preserves the integrity of the underlying glass support and improves scalability to devices. Furthermore, a microwave hydrothermal process is shown to grow Ti O_2 nanorods on these nanowires to create a hierarchical nanoheterostructure that will lead to efficient photogenerated charge carrier separation and rapid transport of electrons to the substrate. This process simplifies nanowire growth by using commercially available and widely used FTO substrates without the need for an additional upstream Sn source and can be used as a high surface area host structure to many other hierarchical structures.展开更多
The synthesis of gold nanoparticles caped with visible light-responsible TiO2 nanoparticles. was prepared by using electrochemical Oxidation-Reduction Cycles （ORC） in 0.1 M HCI aqueous solution containing 60 mM visi...The synthesis of gold nanoparticles caped with visible light-responsible TiO2 nanoparticles. was prepared by using electrochemical Oxidation-Reduction Cycles （ORC） in 0.1 M HCI aqueous solution containing 60 mM visible light-responsible TiO2 nanoparticles. Firstly, an Au substrate was cycled in a deoxygenated aqueous solution containing 0.1 M HCI and 60 mM anatase TiO2 nanoparticles from -0.28 to ＋1.22 V vs Ag/AgCI at 500 mV/s with 25 scans. The durations at the cathodic and anodic vertexes are 10 and 5 s, respectively. After this process, Au-and TiO2-containing complexes were left in the solution. Then a Pt electrode immediately replaced the Au working electrode, and a cathodic overpotential of 0.6 V from the Open Circuit Potential （OCP） was applied under sonification to synthesize Au nanoparticles. Encouragingly, the prepared Au nanoparticles caped with visible light-responsible TiO2 nanoparticles are more active for the decomposition of formaldehyde than pure visible light-responsible TiO2 nanoparticles are in the same condition. After 5 days testing, the formaldehyde was decomposed ca. 35% in containing Au nanoparticles caped with visible light-responsible TiO2 nanoparticles, but the formaldehyde was decomposed only ca. 25% in containing pure visible light-responsible TiO2 nanoparticles.展开更多
Commercial cathode material （LiCoO2） was modified by coating with a thin layer of SrO/Li2O/La2O3/Ta2O5/TiO2 for improving its performance in lithium ion battery. The morphology and structure of the modified cathode ...Commercial cathode material （LiCoO2） was modified by coating with a thin layer of SrO/Li2O/La2O3/Ta2O5/TiO2 for improving its performance in lithium ion battery. The morphology and structure of the modified cathode material were characterized by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The performance including cycling stability, diffusion coefficient under different voltage, C-rate discharge of the batteries with this modified cathode material was examined. The results showed that the battery with the coated cathode material could discharge at a large current density, and it possessed a stable cycle performance in the range from 3.0 V to 4.2 V. It was explained that the rate of Li ion diffusion increased in the batteries using SrO/Li2O/La2O3/Ta2O5/TiO2-coated LiCoO2 as the cathode and the coated layer could act as a fast ion conductor （SrO/Li2O/La2O3/Ta2O5/TiO2） and as a protecting shell to prevent LiCoO2particles from being attacked by the acidic electrolyte.展开更多
Conventional cathode material （LiCoO2） was modified by coating with a thin layer of La2O3/Li2O/TiO2 for improving its performance for lithium ion battery. The morphology and structure of the modified cathode materia...Conventional cathode material （LiCoO2） was modified by coating with a thin layer of La2O3/Li2O/TiO2 for improving its performance for lithium ion battery. The morphology and structure of the modified cathode material was characterized by SEM, XRD, and Auger electron spectroscopy. The performance of the cells with the modified cathode material was examined, including the cycling stability, the diffusion coefficient under different voltages, and the C-rate discharge. The results showed that the cell composed of the coated cathode material discharged at a large current density, and possesses a stable cycle performance in the range from 3.0 to 4.4 V. It was explained that the rate of Li ion diffusion increased in the cell while using La2O3/Li2O/TiO2-coated LiCoO2 as the cathode and the coating layer may act as a faster ion conductor （La2O3/Li2O/TiO2）.展开更多
基金Supported by the National Natural Science Foundation of China（21173018,20473009）
文摘The core-shell structured TiO2/SiO2 @Fe3O4 photocatalysts were prepared using Fe3O4 as magnetic core,tetraethoxysilane（TEOS） as silica source and tetrabutyl titanate（TBOT） as titanium sources.The as-obtained structure was composed of a SiO2@Fe3O4 core and a porous TiO2 shell.The diameter of SiO2@Fe3O4 core was about 205 nm with thickness of porous TiO2 of about 5-6 nm.The 9%TiO2/6%SiO2@Fe3O4 microspheres possess the highest BET surface area and the BJH pore volume,which are 373.5 m2.g-1 and 0.28 cm3.g-1,respectively.The 9%TiO2/6%SiO2@Fe3O4 photocatalyst exhibited an excellent performance for the degradation of methyl orange and methylene blue dyes.Two different dyes were completely decolorized in 60 min under UV irradiation.The photocatalytic activity and the amount of catalyst were almost not decrease after recycling for 6 times by using external magnetic field.
文摘A hollow glass microsphere(HGM)/TiO2 composite hollow sphere was successfully prepared via a simple precipitation method.The TiO2 coating layers grew on the surface of the HGMs that range from 20 to 50μm in diameter as nanoparticles with the formation of the SiO Ti bonds.The growth mechanism accounting for the formation of the TiO2 nanolayers was proposed.The morphology,composition,thermal insulation properties,and visible-near infrared(VIS-NIR)refl ectance of the HGMs/TiO2 composite hollow spheres were characterized.The VIS-NIR reflectance of the HGMs/TiO2 composite hollow spheres increased by more than 30%compared to raw HGMs.The thermal conductivity of the particles is 0.058 W/(m K).The result indicates that the VIS-NIR reflectance of the composite hollow spheres is strongly influenced by the coating of TiO2.The composite hollow spheres were used as the main functional filler to prepare the organic-inorganic composite coatings.The glass substrates coated by the organic-inorganic coatings had lower thermal conductivity and higher near infrared reflectivity.Therefore,the HGMs/TiO2 composite hollow spheres can reflect most of the solar energy and effectively keep out the heat as a thermal insulation coating for energy-saving constructions.
基金Project(50802034) supported by the National Natural Science Foundation of ChinaProject(11A093) supported by the Key Project Foundation by the Education Department of Hunan Province,China
文摘TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to estimate activity of catalysts and determine the kinetics. And the effects of parameters including the initial concentration of AY, light intensity and TiO2 content in catalysts were examined. The results indicate that TAs has a higher efficiency in decomposition of AY than P25, pure TiO2 particles as well as the mixture of TiO2 powder and active carbon. The photocatalytic degradation rate is found to follow the pseudo-first order kinetics with respect to the AY concentration. The new kinetic model fairly resembles the classic Langmuir-Hinshelwood equation, and the rate constant is proportional to the square root of the light intensity in a wide range. However, its absorption performance depends on the surface areas of catalysts. The model fits quite well with the experimental data and elucidates phenomena about the effects of the TiO2 content in TAs on the degradation rate.
基金financially supported by the National Natural Science Foundation of China (No.20873046)the Specialized Research Fund for the Doctoral Program of HigherEducation (No.200805740004)Natural Science Foundation of Guangdong Province (No.10351063101000001)
文摘TiO2-coated SnO2 （TCS） hollow spheres, which are new anode materials for lithium ion （Li-ion） batteries, were prepared and characterized with X-ray diffraction （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, cyclic voltammetry （CV）, and galvanostatic charge/discharge tests. The results obtained from XRD, SEM, and TEM show that TiO2 can be uniforrrdy coated on the surface of SnO2 hollow spheres with the assistance of anionic surfactant. The cyclic voltammograms indicate that both TiO2 and SnO2 exhibit the activity for Li-ion storage. The charge/discharge tests show that the prepared TCS hollow spheres have a higher reversible coulomb efficiency and a better cycling stability than the uncoated SnO2 hollow spheres.
基金Supported by the Program for Changjiang Scholars and Innovative Research Team in University (PCSIR0818)Health Ministry Foundation of China (WKJ2005-2-003)Natural Science Foundation of Fujian Province (2008H0089 and 2009J01025)
文摘The anti-bacterial adhesion properties of TiO2-coated polymethyl methacrylate （PMMA） surfaces are investigated systematically. In detail, the adhesion of S. aureus （gram positive） and E. coli （gram negative） to TiO2-coated and uncoated PMMA surfaces are performed by the plate counting method. Afterwards, the adhesion free energy of bacteria on both supporting materials is quantified using the thermodynamic approach of Lifshitz van der Waals and acid/base interactions. The superior anti-adhesion capability of TiO2-coated PMMA is demonstrated when compared to native PMMA, both experimentally and theoretically.
文摘The photocatalytic degradation of the synthetic textile dye Reactive Yellow 145 (RY 145) in aqueous solution, using TiO2 coated non-woven fibers as photocatalyst, under UV-lamp irradiation, was studied. The effects of the operational parameters such as initial dye concentration, pH, addition of oxidant hydrogen peroxide and addition of ethanol on the reaction rate were investigated. The effect of some inorganic ions such as and , commonly present in real effluents, on the photodegradation of RY 145 was also examined. The experimental results showed that the photocatalytic degradation rate was favoured by a high concentration of solution in respect to Langmuir-Hinshelwood model. The maximum rate of complete decolorization of RY 145 was observed in the acidic medium at pH 3. The presence of and anions led to an increase of the effectiveness of the photocatalytic degradation. However, the presence of and anions decreased differently the photodegradation reaction rate. TiO2/UV process was proved to be capable of the complete degradation of the RY 145.
基金Supported by the Project of Shanghai Committee of Science and Technology,China(Nos.1052nm00100,09ZR1437600)
文摘Several lithium-ion batteries of 18650-type were assembled with pristine or Al2O3-coated LiNi0.4Co0.2Mn0.4O2（NCM） as cathode material and mesocarbon microbeads（MCMB） as anode material.The cycling performance of the batteries was examined under 25 °C at a 2C rate within a potential range of 2.75―4.20 V.The changes of the crystal structure,the lattice parameter,the mean crystallite size,and the mean micro-strain of pristine NCM and Al2O3-coated NCM during the charge-discharge cycling were determined by X-ray diffraction（XRD）.The results indicate that the bulk structure of Al2O3-coated NCM is more stable than that of pristine NCM,which leads to the better cycling performance of Al2O3-coated NCM compared to that of pristine NCM.
基金funded by a NASA Space Technology Research Fellowshipa Facilities Grant from the Institute for Materials Research(IMR)at The Ohio State University
文摘Growth of single-crystal Sn O_2 nanowires using a fluorine-doped Sn O_2(FTO) thin film as both the source and substrate is demonstrated for the first time at relatively low temperature(580 °C) which preserves the integrity of the underlying glass support and improves scalability to devices. Furthermore, a microwave hydrothermal process is shown to grow Ti O_2 nanorods on these nanowires to create a hierarchical nanoheterostructure that will lead to efficient photogenerated charge carrier separation and rapid transport of electrons to the substrate. This process simplifies nanowire growth by using commercially available and widely used FTO substrates without the need for an additional upstream Sn source and can be used as a high surface area host structure to many other hierarchical structures.
文摘The synthesis of gold nanoparticles caped with visible light-responsible TiO2 nanoparticles. was prepared by using electrochemical Oxidation-Reduction Cycles （ORC） in 0.1 M HCI aqueous solution containing 60 mM visible light-responsible TiO2 nanoparticles. Firstly, an Au substrate was cycled in a deoxygenated aqueous solution containing 0.1 M HCI and 60 mM anatase TiO2 nanoparticles from -0.28 to ＋1.22 V vs Ag/AgCI at 500 mV/s with 25 scans. The durations at the cathodic and anodic vertexes are 10 and 5 s, respectively. After this process, Au-and TiO2-containing complexes were left in the solution. Then a Pt electrode immediately replaced the Au working electrode, and a cathodic overpotential of 0.6 V from the Open Circuit Potential （OCP） was applied under sonification to synthesize Au nanoparticles. Encouragingly, the prepared Au nanoparticles caped with visible light-responsible TiO2 nanoparticles are more active for the decomposition of formaldehyde than pure visible light-responsible TiO2 nanoparticles are in the same condition. After 5 days testing, the formaldehyde was decomposed ca. 35% in containing Au nanoparticles caped with visible light-responsible TiO2 nanoparticles, but the formaldehyde was decomposed only ca. 25% in containing pure visible light-responsible TiO2 nanoparticles.
基金supported by the Natural Science Foundation of Guangdong Province,China (06105562)the Foundation of Manyang Bureau of Sci-ence and Technology,China (07Y003-1)
文摘Commercial cathode material （LiCoO2） was modified by coating with a thin layer of SrO/Li2O/La2O3/Ta2O5/TiO2 for improving its performance in lithium ion battery. The morphology and structure of the modified cathode material were characterized by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The performance including cycling stability, diffusion coefficient under different voltage, C-rate discharge of the batteries with this modified cathode material was examined. The results showed that the battery with the coated cathode material could discharge at a large current density, and it possessed a stable cycle performance in the range from 3.0 V to 4.2 V. It was explained that the rate of Li ion diffusion increased in the batteries using SrO/Li2O/La2O3/Ta2O5/TiO2-coated LiCoO2 as the cathode and the coated layer could act as a fast ion conductor （SrO/Li2O/La2O3/Ta2O5/TiO2） and as a protecting shell to prevent LiCoO2particles from being attacked by the acidic electrolyte.
基金Key Program Project of Natural Science Foundation of Guangdong Province (06105562)
文摘Conventional cathode material （LiCoO2） was modified by coating with a thin layer of La2O3/Li2O/TiO2 for improving its performance for lithium ion battery. The morphology and structure of the modified cathode material was characterized by SEM, XRD, and Auger electron spectroscopy. The performance of the cells with the modified cathode material was examined, including the cycling stability, the diffusion coefficient under different voltages, and the C-rate discharge. The results showed that the cell composed of the coated cathode material discharged at a large current density, and possesses a stable cycle performance in the range from 3.0 to 4.4 V. It was explained that the rate of Li ion diffusion increased in the cell while using La2O3/Li2O/TiO2-coated LiCoO2 as the cathode and the coating layer may act as a faster ion conductor （La2O3/Li2O/TiO2）.