The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with r...The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.展开更多
A type of red luminescent Sr3Al2O6：Eu2＋, Dy3＋ phosphor powder is synthesised by sol-gel-combustion processing, with metal nitrates used as the source of metal ions and citric acid as a chelating agent of metal ions...A type of red luminescent Sr3Al2O6：Eu2＋, Dy3＋ phosphor powder is synthesised by sol-gel-combustion processing, with metal nitrates used as the source of metal ions and citric acid as a chelating agent of metal ions. By tracing the formation process of the sol-gel, it is found that it is necessary to reduce the amount of NO3 by dropping ethanol into the solution for forming a stable and homogeneous sol-gel. Thermogravimetric and Differential Scanning Calorimeter Analysis, x-ray diffractionmeter, scanning electron microscopy and photoluminescence spectroscopy are used to investigate the luminescent properties of the as-synthesised Sr3A1206：Eu2＋, Dy3＋. The results reveal that the Sr3Al2O6 crystallises completely when the combustion ash is sintered at 1250℃. The excitation and the emission spectra indicate that the excitation broadband lies mainly in a visible range and the phosphors emit a strong light at 618 nm under the excitation of 472 nm. The afterglow of （Sr0.94Eu0.03Dy0.03）3Al2O6 phosphors sintered at 1250℃ lasts for over 1000 s when the excited source is cut off.展开更多
To discuss the function of Eu and Dy and their interaction in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ long afterglow material,the Eu and Dy single doped and their co-doped Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ were prepared.The samples wer...To discuss the function of Eu and Dy and their interaction in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ long afterglow material,the Eu and Dy single doped and their co-doped Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ were prepared.The samples were characterized by X-ray diffraction（XRD）,decay curves,photoluminescence（PL）,and thermoluminescence（TL）.The results indicate that Sr2 Mg Si2O7：Eu has afterglow properties,and the doping of Eu ion in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ can lower the depth of traps.Eu ion can not only serve as luminescence center,but also produce traps in the matrix,meanwhile,it also exerts certain influences on the traps produced by Dy in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋.The Dy ion can not act as luminescence center but relates to the change of the traps in the Sr2 Mg Si2O7 matrix.展开更多
基金the National Natural Science Foundation of China (No. 51602126)the National Key Research and Development Plan of China (No. 2016YFB0303505)+1 种基金China and University of Jinan Postdoctoral Science Foundation (No. 2017M622118 and XBH1716)the 111 Project of International Corporation on Advanced Cement-based Materials (D17001).
文摘The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.
基金Project supported by the Key Research Project of Science and Technology of Shanxi, Shanxi Province, China (Grant No 2007031141)the Natural Science Foundation of Shanxi Province, China (Grant No 2007011061)the Scientific Research Foundation of the Higher Education Institutions of Shanxi Province, China (Grant No 20080012)
文摘A type of red luminescent Sr3Al2O6：Eu2＋, Dy3＋ phosphor powder is synthesised by sol-gel-combustion processing, with metal nitrates used as the source of metal ions and citric acid as a chelating agent of metal ions. By tracing the formation process of the sol-gel, it is found that it is necessary to reduce the amount of NO3 by dropping ethanol into the solution for forming a stable and homogeneous sol-gel. Thermogravimetric and Differential Scanning Calorimeter Analysis, x-ray diffractionmeter, scanning electron microscopy and photoluminescence spectroscopy are used to investigate the luminescent properties of the as-synthesised Sr3A1206：Eu2＋, Dy3＋. The results reveal that the Sr3Al2O6 crystallises completely when the combustion ash is sintered at 1250℃. The excitation and the emission spectra indicate that the excitation broadband lies mainly in a visible range and the phosphors emit a strong light at 618 nm under the excitation of 472 nm. The afterglow of （Sr0.94Eu0.03Dy0.03）3Al2O6 phosphors sintered at 1250℃ lasts for over 1000 s when the excited source is cut off.
文摘To discuss the function of Eu and Dy and their interaction in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ long afterglow material,the Eu and Dy single doped and their co-doped Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ were prepared.The samples were characterized by X-ray diffraction（XRD）,decay curves,photoluminescence（PL）,and thermoluminescence（TL）.The results indicate that Sr2 Mg Si2O7：Eu has afterglow properties,and the doping of Eu ion in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ can lower the depth of traps.Eu ion can not only serve as luminescence center,but also produce traps in the matrix,meanwhile,it also exerts certain influences on the traps produced by Dy in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋.The Dy ion can not act as luminescence center but relates to the change of the traps in the Sr2 Mg Si2O7 matrix.