The objective of the present work was to determine the influence of the neutral salt spray corrosion on the wear resistance of HVOF sprayed NiCr-Cr3C2 coating with intermediate layer. Ni-Zn-Al2O3 coatings as interlaye...The objective of the present work was to determine the influence of the neutral salt spray corrosion on the wear resistance of HVOF sprayed NiCr-Cr3C2 coating with intermediate layer. Ni-Zn-Al2O3 coatings as interlayers were prepared by low pressure cold spray（LPCS） between NiCr-Cr3C2 cermet coatings to form a sandwich structure to enhance the corrosion resistance properties. The tribological properties were examined using the UMT-3 fricition and wear tester by line-contact reciprocating sliding under dry and salt spray one week corrosion. The morphology, element distribution, and phase compositions of the coating and worn sufaces were analyzed by using scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction respectively. The corrosion behavior of the coating was studied by the open-circuit potential, the electrochemical impedance spectroscopy, potentiodynamic polarization, and salt spray corrosion methods. It is found that the sandwich structured coating has better corrosion resistance than the single layer coating. The results show that under dry wear conditions, the wear mechanism is abrasive and adhesive wear, whereas under salt spray corrosion conditions it becomes corrosion wear. The friction coefficient of the sandwich structured coating after salt spray corrosion is slightly lower than the dry friction coefficient, but the weight of the wear loss is lower than that under dry condition.展开更多
Hollow Bi2WO6 microspheres are successfully synthesized by a facile ultrasonic spray pyrolysis（USP） method using NaCl as a salt template.The as-prepared hollow microspheres assembled as nanoplates with dimensions of...Hollow Bi2WO6 microspheres are successfully synthesized by a facile ultrasonic spray pyrolysis（USP） method using NaCl as a salt template.The as-prepared hollow microspheres assembled as nanoplates with dimensions of approximately 41-148 nm and are dispersed with non-uniform pores on the template surface.By swapping the salt template with KC1 or Na2SO4,different morphologies of Bi2WO6 are obtained.The experimental results demonstrate that NaCl plays a key role on the formation of Bi2WO6 with hollow structures.The specific growth mechanism of hollow microspheres was studied in detail.The Bi2WO6 hollow microspheres exhibit an excellent photocatalytic efficiency for NO removal under solar light irradiation,which is 1.73 times higher than for the Bi2WO6 obtained in the absence of any salt template.This enhancement can be ascribed to the simultaneous improvement on the surface area and visible light-harvesting ability from the hollow structures.Electron spin resonance（ESR） results suggest that both radicals of ·OH and ·O2^- are involved in the photocatalytic process over the BWO-NaCl sample.The production of ·O2^- radicals offers better durability for NO removal.展开更多
The double-layer NiCr-Cr_(3)C_(2)/Ni-Zn-Al_(2)O_(3) coatings with sufficient corrosion and wear resistance were prepared on low carbon steel substrates.The intermediate layers Ni-Zn-Al_(2)O_(3) were fabricated by usin...The double-layer NiCr-Cr_(3)C_(2)/Ni-Zn-Al_(2)O_(3) coatings with sufficient corrosion and wear resistance were prepared on low carbon steel substrates.The intermediate layers Ni-Zn-Al_(2)O_(3) were fabricated by using low-pressure cold spray (LPCS) method to improve the salt fog corrosion resistance properties of the supersonic plasma spray (SPS) NiCr-Cr_(3)C_(2) coatings.The friction and wear performance for the double-layer and single-layer NiCr-Cr_(3)C_(2) coatings were carried out by line-contact reciprocating sliding,respectively.Combined with the coating surface analysis techniques,the effect of the salt fog corrosion on the tribological properties of the double-layer coatings was studied.The results showed that the double-layer coatings exhibited better wear resistance than that of the single-layer coatings,due to the better corrosion resistance of the intermediate layer;the wear mass losses of the double-layer coatings was reduced by 70%than that of the single layer coatings and the wear mechanism of coatings after salt fog corrosion conditions is mainly corrosion wear.展开更多
The nano-concentrates and flame retardant nano-coating were prepared in thhis study. The effect of nano-SiO2 on the corrosion resistance and fire resistance of ammonium polyphosphate-pentaerythritol-melamine （APP- PE...The nano-concentrates and flame retardant nano-coating were prepared in thhis study. The effect of nano-SiO2 on the corrosion resistance and fire resistance of ammonium polyphosphate-pentaerythritol-melamine （APP- PER-MEL） coating was investigated by differential thermal analysis （DTA）, scanning electron microscopy （SEM）, effective thermal conductivity （λ/d）, X-ray photoelectron spectroscopy （XPS） and fire protection test. The chemical action and endothermic effect of ammonium polyphosphate, pentaerythritol and melamine in traditional flame retardant coating were damaged by salt spray condition, whereas the flame-retardant additives in the nano-coating demonstrated the good chemical interaction in salt spray condition. The uniformly dispersed nano-SiO2 particles could improve corrosion resistance of the coating, and hence nano-coating could remain the good fire-resistant properties even after 500 h salt spray test.展开更多
基金Funded by the High-Tech Research and Development Program of China(No.2012AA09A203)the Fundmental Research Funds for the Central Universities(No.15CX06061A)the Postgraduate Innovation Project of China University of Petroleum(East China)(No.YCXJ2016059)
文摘The objective of the present work was to determine the influence of the neutral salt spray corrosion on the wear resistance of HVOF sprayed NiCr-Cr3C2 coating with intermediate layer. Ni-Zn-Al2O3 coatings as interlayers were prepared by low pressure cold spray（LPCS） between NiCr-Cr3C2 cermet coatings to form a sandwich structure to enhance the corrosion resistance properties. The tribological properties were examined using the UMT-3 fricition and wear tester by line-contact reciprocating sliding under dry and salt spray one week corrosion. The morphology, element distribution, and phase compositions of the coating and worn sufaces were analyzed by using scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction respectively. The corrosion behavior of the coating was studied by the open-circuit potential, the electrochemical impedance spectroscopy, potentiodynamic polarization, and salt spray corrosion methods. It is found that the sandwich structured coating has better corrosion resistance than the single layer coating. The results show that under dry wear conditions, the wear mechanism is abrasive and adhesive wear, whereas under salt spray corrosion conditions it becomes corrosion wear. The friction coefficient of the sandwich structured coating after salt spray corrosion is slightly lower than the dry friction coefficient, but the weight of the wear loss is lower than that under dry condition.
基金supported by the National Natural Science Foundation of China (41503102, 41401567, 41573138)the China Postdoctoral Science Foundation (2015M572568)~~
文摘Hollow Bi2WO6 microspheres are successfully synthesized by a facile ultrasonic spray pyrolysis（USP） method using NaCl as a salt template.The as-prepared hollow microspheres assembled as nanoplates with dimensions of approximately 41-148 nm and are dispersed with non-uniform pores on the template surface.By swapping the salt template with KC1 or Na2SO4,different morphologies of Bi2WO6 are obtained.The experimental results demonstrate that NaCl plays a key role on the formation of Bi2WO6 with hollow structures.The specific growth mechanism of hollow microspheres was studied in detail.The Bi2WO6 hollow microspheres exhibit an excellent photocatalytic efficiency for NO removal under solar light irradiation,which is 1.73 times higher than for the Bi2WO6 obtained in the absence of any salt template.This enhancement can be ascribed to the simultaneous improvement on the surface area and visible light-harvesting ability from the hollow structures.Electron spin resonance（ESR） results suggest that both radicals of ·OH and ·O2^- are involved in the photocatalytic process over the BWO-NaCl sample.The production of ·O2^- radicals offers better durability for NO removal.
基金Fundamental Research Funds for Central Universities Project (No. 1CX05021A)Shandong Provincial Key R&D Plan Project (No. 2GHY15108)Shandong Postdoctoral Innovation Project and Qingdao Postdoctoral Applied Research Project。
文摘The double-layer NiCr-Cr_(3)C_(2)/Ni-Zn-Al_(2)O_(3) coatings with sufficient corrosion and wear resistance were prepared on low carbon steel substrates.The intermediate layers Ni-Zn-Al_(2)O_(3) were fabricated by using low-pressure cold spray (LPCS) method to improve the salt fog corrosion resistance properties of the supersonic plasma spray (SPS) NiCr-Cr_(3)C_(2) coatings.The friction and wear performance for the double-layer and single-layer NiCr-Cr_(3)C_(2) coatings were carried out by line-contact reciprocating sliding,respectively.Combined with the coating surface analysis techniques,the effect of the salt fog corrosion on the tribological properties of the double-layer coatings was studied.The results showed that the double-layer coatings exhibited better wear resistance than that of the single-layer coatings,due to the better corrosion resistance of the intermediate layer;the wear mass losses of the double-layer coatings was reduced by 70%than that of the single layer coatings and the wear mechanism of coatings after salt fog corrosion conditions is mainly corrosion wear.
文摘The nano-concentrates and flame retardant nano-coating were prepared in thhis study. The effect of nano-SiO2 on the corrosion resistance and fire resistance of ammonium polyphosphate-pentaerythritol-melamine （APP- PER-MEL） coating was investigated by differential thermal analysis （DTA）, scanning electron microscopy （SEM）, effective thermal conductivity （λ/d）, X-ray photoelectron spectroscopy （XPS） and fire protection test. The chemical action and endothermic effect of ammonium polyphosphate, pentaerythritol and melamine in traditional flame retardant coating were damaged by salt spray condition, whereas the flame-retardant additives in the nano-coating demonstrated the good chemical interaction in salt spray condition. The uniformly dispersed nano-SiO2 particles could improve corrosion resistance of the coating, and hence nano-coating could remain the good fire-resistant properties even after 500 h salt spray test.