The influence of solution treatment on the microstructure and properties of Mg2Si/AZ91D composites fabricated from Mg-SiO2 system via in-situ processing method was investigated.The results show that coarse Chinese scr...The influence of solution treatment on the microstructure and properties of Mg2Si/AZ91D composites fabricated from Mg-SiO2 system via in-situ processing method was investigated.The results show that coarse Chinese script shape Mg2Si phases can be formed by adding SiO2 into AZ91D magnesium alloy with Si content up to 1.5% of the alloy melt.During solution treatment,the morphology and distribution of the coarse Chinese script shape Mg2Si phases are modified.Meanwhile,the β-Mg17Al12 phase is dissolved into the magnesium matrix.With increasing holding time,the coarse Mg2Si phases tend to dissolve,break and spheroidize.After solution treatment at 420 ℃ for 16 h,Mg2Si phases become the finest and relatively well-distributed phase.The tensile strength and elongation are increased by 14.9% and 38.9%,respectively.It is believed that the Mg2Si phases continuously dissolve and break,and finally the spheroidized Mg2Si particles are obtained due to the interface tension of Mg2Si/Mg interface.展开更多
The effects of cooling rates corresponding to different diameters of the steel mould and laser surface melting(LSM)on the as-cast microstructures of Mg-9Al-xSi(x=1,3)(mass fraction,%)alloys were investigated by XRD an...The effects of cooling rates corresponding to different diameters of the steel mould and laser surface melting(LSM)on the as-cast microstructures of Mg-9Al-xSi(x=1,3)(mass fraction,%)alloys were investigated by XRD and OM.The results show that obvious refinement of the alloy microstructure is obtained with increasing cooling rate by conventional ingot metallurgy.However, no evident modified morphologies of both dendritic primary Mg2Si and Chinese script eutectic Mg2Si in the Mg-Al-Si alloy occurs. Surprisingly,the morphologies of Mg2Si phases within the laser-melted Mg-Al-Si alloy transform drastically from both coarse Chinese script shape for the eutectic Mg2Si and dendrite for the primary Mg2Si to fine spherical particles with an average size of about 3μm due to the rapid cooling of the melted layer,and the Mg2Si particulates distribute more uniformly in theα-Mg matrix.展开更多
基金Project (BG2007030) supported by High-tech Research Program of Jiangsu Province, ChinaProject (07KJA43008) supported by the Natural Science Foundation of Jiangsu Province, ChinaProject (20070299004) supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China
文摘The influence of solution treatment on the microstructure and properties of Mg2Si/AZ91D composites fabricated from Mg-SiO2 system via in-situ processing method was investigated.The results show that coarse Chinese script shape Mg2Si phases can be formed by adding SiO2 into AZ91D magnesium alloy with Si content up to 1.5% of the alloy melt.During solution treatment,the morphology and distribution of the coarse Chinese script shape Mg2Si phases are modified.Meanwhile,the β-Mg17Al12 phase is dissolved into the magnesium matrix.With increasing holding time,the coarse Mg2Si phases tend to dissolve,break and spheroidize.After solution treatment at 420 ℃ for 16 h,Mg2Si phases become the finest and relatively well-distributed phase.The tensile strength and elongation are increased by 14.9% and 38.9%,respectively.It is believed that the Mg2Si phases continuously dissolve and break,and finally the spheroidized Mg2Si particles are obtained due to the interface tension of Mg2Si/Mg interface.
基金Project(LRB05-311)supported by the Postdoctoral Foundation of Heilongjiang Province,ChinaProject(HEUFT05038)supported by the Basic Research Foundation of Harbin Engineering University,ChinaProject(2009AA03Z423)supported by the National High-TechResearch and Development Program of China
文摘The effects of cooling rates corresponding to different diameters of the steel mould and laser surface melting(LSM)on the as-cast microstructures of Mg-9Al-xSi(x=1,3)(mass fraction,%)alloys were investigated by XRD and OM.The results show that obvious refinement of the alloy microstructure is obtained with increasing cooling rate by conventional ingot metallurgy.However, no evident modified morphologies of both dendritic primary Mg2Si and Chinese script eutectic Mg2Si in the Mg-Al-Si alloy occurs. Surprisingly,the morphologies of Mg2Si phases within the laser-melted Mg-Al-Si alloy transform drastically from both coarse Chinese script shape for the eutectic Mg2Si and dendrite for the primary Mg2Si to fine spherical particles with an average size of about 3μm due to the rapid cooling of the melted layer,and the Mg2Si particulates distribute more uniformly in theα-Mg matrix.