Producing methanol from coke oven gas(COG) is one of the important applications of COG. Removal of sulfur from COG is a key step of this process. Conversion and reaction kinetics over a commercial Fe-Mo/Al2O3 catalyst...Producing methanol from coke oven gas(COG) is one of the important applications of COG. Removal of sulfur from COG is a key step of this process. Conversion and reaction kinetics over a commercial Fe-Mo/Al2O3 catalyst(T-202) were studied in a continuous flow fixed bed reactor under pressures of 1.6-2.8 MPa, space time of 1.32-3.55 s and temperatures of 240-360 °C. Though the COG contains about 0.6 mol/mol H2, hydrogenation of CO and CO2 is not significant on this catalyst. The conversions of unsaturated hydrocarbons depend on their molecular structures. Diolefins and alkynes can be completely hydrogenated even at relatively low temperature and pressure. Olefins, in contrast, can only be progressively hydrogenated with increasing temperature and pressure. The hydrodesulfurization(HDS) of CS2 on this catalyst is easy. Complete conversion of CS2 was observed in the whole range of the conditions used in this work. The original COS in the COG can also be easily converted to a low level. However, its complete HDS is difficult due to the relatively high concentration of CO in the COG and due to the limitation of thermodynamics. H2 S can react with unsaturated hydrocarbons to form ethyl mercaptan and thiophene, which are then progressively hydrodesulfurized with increasing temperature and pressure. Based on the experimental observations, reaction kinetic models for the conversion of ethylene and sulfur-containing compounds were proposed; the values of the parameters in the models were obtained by regression of the experimental data.展开更多
Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO ...以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。展开更多
文摘Producing methanol from coke oven gas(COG) is one of the important applications of COG. Removal of sulfur from COG is a key step of this process. Conversion and reaction kinetics over a commercial Fe-Mo/Al2O3 catalyst(T-202) were studied in a continuous flow fixed bed reactor under pressures of 1.6-2.8 MPa, space time of 1.32-3.55 s and temperatures of 240-360 °C. Though the COG contains about 0.6 mol/mol H2, hydrogenation of CO and CO2 is not significant on this catalyst. The conversions of unsaturated hydrocarbons depend on their molecular structures. Diolefins and alkynes can be completely hydrogenated even at relatively low temperature and pressure. Olefins, in contrast, can only be progressively hydrogenated with increasing temperature and pressure. The hydrodesulfurization(HDS) of CS2 on this catalyst is easy. Complete conversion of CS2 was observed in the whole range of the conditions used in this work. The original COS in the COG can also be easily converted to a low level. However, its complete HDS is difficult due to the relatively high concentration of CO in the COG and due to the limitation of thermodynamics. H2 S can react with unsaturated hydrocarbons to form ethyl mercaptan and thiophene, which are then progressively hydrodesulfurized with increasing temperature and pressure. Based on the experimental observations, reaction kinetic models for the conversion of ethylene and sulfur-containing compounds were proposed; the values of the parameters in the models were obtained by regression of the experimental data.
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
文摘以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。