In order to improve the cyclic stability of La-Mg-Ni system （Ce2Ni7-type） alloy electrode, small amount of Co was added in La0.75Mg0.25Ni3.5 alloy. The effect of Co on electrochemical performance and microstructure ...In order to improve the cyclic stability of La-Mg-Ni system （Ce2Ni7-type） alloy electrode, small amount of Co was added in La0.75Mg0.25Ni3.5 alloy. The effect of Co on electrochemical performance and microstructure of the alloys were investigated in detail. XRD results showed that the alloys had multiphase structure composed of （La, Mg）2Ni7, LaNi5 and small amount of LaNi2 phases. The discharge capacity of the alloys first increased and then decreased with increasing Co content. At a discharge current density of 900 mA/g, the HRD of the alloy electrodes increased from 81.3% （x=0） to 89.2 % （x=0.2）, and then reduced to 87.8 % （x=0.6）. After 60 charge/discharge cycles, the capacity retention rate of the alloys enhanced from 52.67% to 61.32%, and the capacity decay rate of the alloys decreased from 2.60 to 2.05 mAh/g per cycle with increasing Co content. The obtained results by XPS and XRD showed that the fundamental reasons for the capacity decay of the La-Mg-Ni system （Ce2Ni7-type） alloy electrodes were corrosion and oxidation as well as passivation of Mg and Lain alkaline solution.展开更多
Hydrogen storage alloys(LaGdMg)Ni3.35-xCoxAl0.15(x=0,0.1,0.3,0.5,1.0,1.5,2.0) were prepared by induction melting followed by annealing treatment in argon atmosphere.The effects of partly replacing Ni by Co element in(...Hydrogen storage alloys(LaGdMg)Ni3.35-xCoxAl0.15(x=0,0.1,0.3,0.5,1.0,1.5,2.0) were prepared by induction melting followed by annealing treatment in argon atmosphere.The effects of partly replacing Ni by Co element in(LaGdMg)Ni3.35Al0.15 on the phase structure and electrochemical properties of(LaGdMg)Ni3.35-xCoxAl0.15 alloys were investigated.Structure analysis showed that the alloys consisted of Ce2Ni7-type(Gd2Co7-type),CaCu5-type,Pr5Co19-type,PuNi3-type phase structure.The addition of Co element obviously reduced the contents of CaCu5-type phase and increased the contents of Ce2Ni7-type phase.However,Pr5Co19-type and CaCu5-type phase obviously increased with the high content of Co.Rietveld analysis showed that the c-axis lattice parameters and cell volumes of the component phases increased with increasing Co content.The electrochemical measurements showed that as the Co content increased,the maximum discharge capacity and the cyclic stability of the annealed alloys both first increased then decreased.The(LaGdMg)Ni3.05Co0.3Al0.15 alloy electrode exhibited the maximum discharge capacity(392.92 mAh/g),and the(LaGdMg)Ni1.85Co1.0Al0.15 alloy electrode showed the best cyclic stability(S100=96.1%).展开更多
基金the National Natural Science Foundation of China (50701011)Natural Science Foundation of Inner Mongolia, China (200711020703)Science and Technology Planned Project of Inner Mongolia, China (20050205)
文摘In order to improve the cyclic stability of La-Mg-Ni system （Ce2Ni7-type） alloy electrode, small amount of Co was added in La0.75Mg0.25Ni3.5 alloy. The effect of Co on electrochemical performance and microstructure of the alloys were investigated in detail. XRD results showed that the alloys had multiphase structure composed of （La, Mg）2Ni7, LaNi5 and small amount of LaNi2 phases. The discharge capacity of the alloys first increased and then decreased with increasing Co content. At a discharge current density of 900 mA/g, the HRD of the alloy electrodes increased from 81.3% （x=0） to 89.2 % （x=0.2）, and then reduced to 87.8 % （x=0.6）. After 60 charge/discharge cycles, the capacity retention rate of the alloys enhanced from 52.67% to 61.32%, and the capacity decay rate of the alloys decreased from 2.60 to 2.05 mAh/g per cycle with increasing Co content. The obtained results by XPS and XRD showed that the fundamental reasons for the capacity decay of the La-Mg-Ni system （Ce2Ni7-type） alloy electrodes were corrosion and oxidation as well as passivation of Mg and Lain alkaline solution.
基金Project supported by the National Natural Science Foundation of China (50941019)
文摘Hydrogen storage alloys(LaGdMg)Ni3.35-xCoxAl0.15(x=0,0.1,0.3,0.5,1.0,1.5,2.0) were prepared by induction melting followed by annealing treatment in argon atmosphere.The effects of partly replacing Ni by Co element in(LaGdMg)Ni3.35Al0.15 on the phase structure and electrochemical properties of(LaGdMg)Ni3.35-xCoxAl0.15 alloys were investigated.Structure analysis showed that the alloys consisted of Ce2Ni7-type(Gd2Co7-type),CaCu5-type,Pr5Co19-type,PuNi3-type phase structure.The addition of Co element obviously reduced the contents of CaCu5-type phase and increased the contents of Ce2Ni7-type phase.However,Pr5Co19-type and CaCu5-type phase obviously increased with the high content of Co.Rietveld analysis showed that the c-axis lattice parameters and cell volumes of the component phases increased with increasing Co content.The electrochemical measurements showed that as the Co content increased,the maximum discharge capacity and the cyclic stability of the annealed alloys both first increased then decreased.The(LaGdMg)Ni3.05Co0.3Al0.15 alloy electrode exhibited the maximum discharge capacity(392.92 mAh/g),and the(LaGdMg)Ni1.85Co1.0Al0.15 alloy electrode showed the best cyclic stability(S100=96.1%).