The welding property of TiB2/ZL101 composite was investigated using electron beam（EB） welding experimental system with a function generator.The fine defect-free welding seam was obtained under proper processing para...The welding property of TiB2/ZL101 composite was investigated using electron beam（EB） welding experimental system with a function generator.The fine defect-free welding seam was obtained under proper processing parameters and scanning rate.The reinforcement particles TiB2 distributed homogeneously in welding seam without any segregation.The tensile results show that fracture occurs at the base metal and elastic modulus increases compared with base metal.Wear resistance of welding seam is improved greatly compared with base metal.The results show that the TiB2/ZL101 composite can be successfully welded by EB technology.展开更多
The effects of current pulsing on the microstructure, hardness and tensile properties at different temperatures of gas tungsten arc （GTA） weldments of titanium matrix composites were studied. Full-penetration butt j...The effects of current pulsing on the microstructure, hardness and tensile properties at different temperatures of gas tungsten arc （GTA） weldments of titanium matrix composites were studied. Full-penetration butt joints were made with or without current pulsing. Optical microscopy, hardness test and scanning electron microscopy were employed to evaluate the metallurgical characteristics of welded joints. Tensile properties of weldments at different temperatures were studied and correlated with the microstructure. The results exhibit that current pulsing leads to the refinement of the weld microstrucmre and TiB whisker and the redistribution of reinforcements resulting in higher hardness, tensile strength and ductility of weldments in the as-welded condition.展开更多
Calculations have been made for weld depths occurring for TIG welding activated by a flux over the surface of the weld pool. In this case, the flux introduces an electrically insulating layer over the outer regions of...Calculations have been made for weld depths occurring for TIG welding activated by a flux over the surface of the weld pool. In this case, the flux introduces an electrically insulating layer over the outer regions of the weld pool surface. There is then an increase in the current density at the surface of the centre of the weld pool with a consequent increase in the J×B forces, which drive a strong convective flow of the molten metal downwards, tending to make a deep weld. For a flux which produces an insulating layer for all but a central region of radius 2 mm, the calculated weld depth is 7 mm, and an arc spot is predicted at the centre of the weld pool surface. As yet we have not resolved the reason for significant differences that exist between our measurements of weld depth and the theoretical predictions.展开更多
A novel Sn-2.5Ag-2.0Ni alloy was used for soldering SiCp/Al composites substrate deposited with electroless Ni(5%P) (mass fraction)and Ni(10%P)(mass fraction)layers.It is observed that variation of P contents in the e...A novel Sn-2.5Ag-2.0Ni alloy was used for soldering SiCp/Al composites substrate deposited with electroless Ni(5%P) (mass fraction)and Ni(10%P)(mass fraction)layers.It is observed that variation of P contents in the electroless Ni(P)layer results in different types of microstructures of SnAgNi/Ni(P)solder joint.The morphology of Ni3Sn4 intermetallic compounds(IMCs)formed between the solder and Ni(10%P)layer is observed to be needle-like and this shape provides high speed diffusion channels for Ni to diffuse into solder that culminates in high growth rate of Ni3Sn4.The diffusion of Ni into solder furthermore results in the formation of Kirkendall voids at the interface of Ni(P)layer and SiCp/Al composites substrate.It is observed that solder reliability is degraded by the formation of Ni2SnP,P rich Ni layer and Kirkendall voids.The compact Ni3Sn4 IMC layer in Ni(5%P)solder joint prevents Ni element from diffusing into solder,resulting in a low growth rate of Ni3Sn4 layer.Meanwhile,the formation of Ni2SnP that significantly affects the reliability of solder joints is suppressed by the low P content Ni(5%P)layer.Thus,shear strength of Ni(5%P) solder joint is concluded to be higher than that of Ni(10%P)solder joint.Growth of Ni3Sn4 IMC layer and formation of crack are accounted to be the major sources of the failure of Ni(5%P)solder joint.展开更多
Currently the aluminum alloy resistance spot welding(AA-RSW) has been extensively used for light weight automotive body-in-white manufacturing.However the aluminum alloys such as AA5182 have inferior weldability for f...Currently the aluminum alloy resistance spot welding(AA-RSW) has been extensively used for light weight automotive body-in-white manufacturing.However the aluminum alloys such as AA5182 have inferior weldability for forming the joint due to their high reflectiveness to heat and light.Therefore it is necessary to further develop the high performance control strategy and the set-up of a new welding schedule.The welding process identification is the essential issue where the difficulty arises from the fact that the AA-RSW is a nonlinear time-varying uncertain process which couples the thermal,electrical,mechanical and metallurgical dynamics.To understand this complicated physical phenomenon a novel dual-phase M-series pseudo-random electrical pattern is adopted to excite the AA-RSW electrical-thermal process and the thermal response is recorded according to the welding power outputs.Based on the experimental information,the transfer function of an AA-RSW electrical- thermal mechanism is identified,and the optimum model order and parameters are determined.Subsequently a control-oriented DC AA-RSW model is established to explore the welding power control algorithm.The simulated results of the control model show agreement with the experimental data,which validates its feasibility for the corresponding welding control.展开更多
基金Project(11ZR1417500) supported by Natural Science Foundation of Shanghai,China
文摘The welding property of TiB2/ZL101 composite was investigated using electron beam（EB） welding experimental system with a function generator.The fine defect-free welding seam was obtained under proper processing parameters and scanning rate.The reinforcement particles TiB2 distributed homogeneously in welding seam without any segregation.The tensile results show that fracture occurs at the base metal and elastic modulus increases compared with base metal.Wear resistance of welding seam is improved greatly compared with base metal.The results show that the TiB2/ZL101 composite can be successfully welded by EB technology.
基金Project(51371114)supported by the National Natural Science Foundation of ChinaProject(2012CB619600)supported by the National Basic Research Program of China+1 种基金Project(10SG15)supported by the Dawn Program of Shanghai Education Commission,ChinaProject(12XD1402800)supported by Shanghai Science and Technology Committee,China
文摘The effects of current pulsing on the microstructure, hardness and tensile properties at different temperatures of gas tungsten arc （GTA） weldments of titanium matrix composites were studied. Full-penetration butt joints were made with or without current pulsing. Optical microscopy, hardness test and scanning electron microscopy were employed to evaluate the metallurgical characteristics of welded joints. Tensile properties of weldments at different temperatures were studied and correlated with the microstructure. The results exhibit that current pulsing leads to the refinement of the weld microstrucmre and TiB whisker and the redistribution of reinforcements resulting in higher hardness, tensile strength and ductility of weldments in the as-welded condition.
文摘Calculations have been made for weld depths occurring for TIG welding activated by a flux over the surface of the weld pool. In this case, the flux introduces an electrically insulating layer over the outer regions of the weld pool surface. There is then an increase in the current density at the surface of the centre of the weld pool with a consequent increase in the J×B forces, which drive a strong convective flow of the molten metal downwards, tending to make a deep weld. For a flux which produces an insulating layer for all but a central region of radius 2 mm, the calculated weld depth is 7 mm, and an arc spot is predicted at the centre of the weld pool surface. As yet we have not resolved the reason for significant differences that exist between our measurements of weld depth and the theoretical predictions.
基金Projects(50274014, 50774005) supported by the National Natural Science Foundation of ChinaProject(2006CB605207) supported by the National Basic Research Program of China+1 种基金Project(2006AA03Z557) supported by the National High-tech Research and Development of ChinaProject(I2P407) supported by MOE Program for Changjiang Scholars
文摘A novel Sn-2.5Ag-2.0Ni alloy was used for soldering SiCp/Al composites substrate deposited with electroless Ni(5%P) (mass fraction)and Ni(10%P)(mass fraction)layers.It is observed that variation of P contents in the electroless Ni(P)layer results in different types of microstructures of SnAgNi/Ni(P)solder joint.The morphology of Ni3Sn4 intermetallic compounds(IMCs)formed between the solder and Ni(10%P)layer is observed to be needle-like and this shape provides high speed diffusion channels for Ni to diffuse into solder that culminates in high growth rate of Ni3Sn4.The diffusion of Ni into solder furthermore results in the formation of Kirkendall voids at the interface of Ni(P)layer and SiCp/Al composites substrate.It is observed that solder reliability is degraded by the formation of Ni2SnP,P rich Ni layer and Kirkendall voids.The compact Ni3Sn4 IMC layer in Ni(5%P)solder joint prevents Ni element from diffusing into solder,resulting in a low growth rate of Ni3Sn4 layer.Meanwhile,the formation of Ni2SnP that significantly affects the reliability of solder joints is suppressed by the low P content Ni(5%P)layer.Thus,shear strength of Ni(5%P) solder joint is concluded to be higher than that of Ni(10%P)solder joint.Growth of Ni3Sn4 IMC layer and formation of crack are accounted to be the major sources of the failure of Ni(5%P)solder joint.
基金the National High Technology Research and Development Program (863) of China (No.2012AA041802)the Agricultural Science and Technology Achievement Transformation Funds from China Ministry of Science and Technology (No.2011GB23800022)
文摘Currently the aluminum alloy resistance spot welding(AA-RSW) has been extensively used for light weight automotive body-in-white manufacturing.However the aluminum alloys such as AA5182 have inferior weldability for forming the joint due to their high reflectiveness to heat and light.Therefore it is necessary to further develop the high performance control strategy and the set-up of a new welding schedule.The welding process identification is the essential issue where the difficulty arises from the fact that the AA-RSW is a nonlinear time-varying uncertain process which couples the thermal,electrical,mechanical and metallurgical dynamics.To understand this complicated physical phenomenon a novel dual-phase M-series pseudo-random electrical pattern is adopted to excite the AA-RSW electrical-thermal process and the thermal response is recorded according to the welding power outputs.Based on the experimental information,the transfer function of an AA-RSW electrical- thermal mechanism is identified,and the optimum model order and parameters are determined.Subsequently a control-oriented DC AA-RSW model is established to explore the welding power control algorithm.The simulated results of the control model show agreement with the experimental data,which validates its feasibility for the corresponding welding control.