Chitosan-montmorillonite(CS-MMT) hybrid was prepared and characterized by XRD,FTIR and TG.The results showed that chitosan was intercalated into the layer structure of Na+-montmorillonite.The ability of CS-MMT hybrid ...Chitosan-montmorillonite(CS-MMT) hybrid was prepared and characterized by XRD,FTIR and TG.The results showed that chitosan was intercalated into the layer structure of Na+-montmorillonite.The ability of CS-MMT hybrid as an adsorbent for the removal of reactive orange X-GN from aqueous solution has been studied.The effects of various parameters such as initial concentration and temperature were also studied.The Langmuir and Freundlich adsorption isotherms have been used to fit the experimental data,and the former giving the higher correlation.Thermodynamic parameters of the adsorption process,ΔG°,ΔH° and ΔS° were determined to be-24.90 kJ·mol-1(at 20℃),10.58 kJ·mol-1 and 121.0 J·mol-1·K-1,respectively.The results indicated that the adsorption of reactive orange X-GN on CS-MMT hybrid was spontaneous.展开更多
Poly(styrene-acrylonitrile) emulsion particles with positive charges on the surface were synthesized by emulsion polymerization using cationic surfactant octotyltrimethyl ammonium chloride (OTAC) as emulsifier.The sus...Poly(styrene-acrylonitrile) emulsion particles with positive charges on the surface were synthesized by emulsion polymerization using cationic surfactant octotyltrimethyl ammonium chloride (OTAC) as emulsifier.The suspension of montmorillonite was slowly dropped into the emulsion.Through the interaction between the negative charges on the montmorillonite layers and the cations on the surface of poly(styrene-acrylonitrile) particles, the montmorillonite layers and emulsion particles could assemble and absorb on each other by themselves.The change of δ voltage and particle size of the emulsion during the process of dropping was characterized, which demonstrated that the emulsion particles and montmorillonite layers absorbed on each other by the electrovalent bond and an intersectional structure was formed in the complex emulsion.Poly(styrene-acrylonitrile)/ montmorillonite nanocomposite was obtained after coagulation.The structure of nanocomposite was characterized with XRD and TEM.The results indicated that montmorillonite was exfoliated into layers with a thickness of several nanometers and uniformly dispersed in the polymer matrix.展开更多
文摘Chitosan-montmorillonite(CS-MMT) hybrid was prepared and characterized by XRD,FTIR and TG.The results showed that chitosan was intercalated into the layer structure of Na+-montmorillonite.The ability of CS-MMT hybrid as an adsorbent for the removal of reactive orange X-GN from aqueous solution has been studied.The effects of various parameters such as initial concentration and temperature were also studied.The Langmuir and Freundlich adsorption isotherms have been used to fit the experimental data,and the former giving the higher correlation.Thermodynamic parameters of the adsorption process,ΔG°,ΔH° and ΔS° were determined to be-24.90 kJ·mol-1(at 20℃),10.58 kJ·mol-1 and 121.0 J·mol-1·K-1,respectively.The results indicated that the adsorption of reactive orange X-GN on CS-MMT hybrid was spontaneous.
文摘Poly(styrene-acrylonitrile) emulsion particles with positive charges on the surface were synthesized by emulsion polymerization using cationic surfactant octotyltrimethyl ammonium chloride (OTAC) as emulsifier.The suspension of montmorillonite was slowly dropped into the emulsion.Through the interaction between the negative charges on the montmorillonite layers and the cations on the surface of poly(styrene-acrylonitrile) particles, the montmorillonite layers and emulsion particles could assemble and absorb on each other by themselves.The change of δ voltage and particle size of the emulsion during the process of dropping was characterized, which demonstrated that the emulsion particles and montmorillonite layers absorbed on each other by the electrovalent bond and an intersectional structure was formed in the complex emulsion.Poly(styrene-acrylonitrile)/ montmorillonite nanocomposite was obtained after coagulation.The structure of nanocomposite was characterized with XRD and TEM.The results indicated that montmorillonite was exfoliated into layers with a thickness of several nanometers and uniformly dispersed in the polymer matrix.