Cyanide-free silver electroplating was conducted in thiosulfate baths containing AgNO3 and AgBr major salts, respectively. The effects of major salt content and current density on surface quality, deposition rate and ...Cyanide-free silver electroplating was conducted in thiosulfate baths containing AgNO3 and AgBr major salts, respectively. The effects of major salt content and current density on surface quality, deposition rate and microhardness of Ag coatings were investigated. The optimized electroplating parameters were established. The adhesion strength of Ag coating on Cu substrate was evaluated and the grain size of Ag coating was measured under optimized electroplating parameters. The optimized AgNO3 content is 40 g/L with current density of 0.25 A/dm2. The deposited bright, smooth, and well adhered Ag coating had nanocrystalline grains with mean size of 35 nm. The optimized AgBr content was 30 g/L with current density of 0.20 A/dm2. The resultant Ag coating had nanocrystalline grains with mean size of 55 nm. Compared with the bath containing AgBr main salt, the bath containing AgNO3 main salt had a wider current density range, and corresponding Ag coating had a higher microhardness and a smaller grain size.展开更多
AZ61Mg alloy was multi directionally forged(MDFed) during decreasing temperature condition from 643 K to 483 K at a true strain rate of 3×10-3 s-1 up to cumulative strain of∑△ε=4.0 at maximum.A pass strain of...AZ61Mg alloy was multi directionally forged(MDFed) during decreasing temperature condition from 643 K to 483 K at a true strain rate of 3×10-3 s-1 up to cumulative strain of∑△ε=4.0 at maximum.A pass strain of△ε=0.8 was employed.While average grain size decreased gradually with increasing cumulative strain,the evolution of fine-grained structure strongly depended on the MDF temperature.Under the condition where the temperature was higher than the most adequate one,grain coarsening partially took place during MDF.In contrast,at lower temperature,inhomogeneous microstructure composed of the initial coarse and newly appeared fine grains was evolved.After straining over∑△ε=3.2(i.e.,over 4 passes of MDF) ,equiaxed ultrafine grains(UFGs) having average size of about and lower than 1μm were uniformly evolved.While the MDFed alloy to∑△ε=4.0 possessed relatively high hardness of HV 99,and it accepted further about 20%cold rolling almost without cracking.Because of the superior formability of the UFGed AZ61Mg alloy,the hardness was further easily raised to HV 120 by following cold rolling.展开更多
基金Project (50771042) supported by the National Natural Science Foundation of ChinaProjects (1041005100052009HASTIT023) supported by the Program for Science and Technology Innovation Talents of Henan Province,China
文摘Cyanide-free silver electroplating was conducted in thiosulfate baths containing AgNO3 and AgBr major salts, respectively. The effects of major salt content and current density on surface quality, deposition rate and microhardness of Ag coatings were investigated. The optimized electroplating parameters were established. The adhesion strength of Ag coating on Cu substrate was evaluated and the grain size of Ag coating was measured under optimized electroplating parameters. The optimized AgNO3 content is 40 g/L with current density of 0.25 A/dm2. The deposited bright, smooth, and well adhered Ag coating had nanocrystalline grains with mean size of 35 nm. The optimized AgBr content was 30 g/L with current density of 0.20 A/dm2. The resultant Ag coating had nanocrystalline grains with mean size of 55 nm. Compared with the bath containing AgBr main salt, the bath containing AgNO3 main salt had a wider current density range, and corresponding Ag coating had a higher microhardness and a smaller grain size.
基金support given by the Light Metals Educational Foundation,Japan,and Ministry of Education,Culture,Sports and Technology,Japan,with Grant No.20560647
文摘AZ61Mg alloy was multi directionally forged(MDFed) during decreasing temperature condition from 643 K to 483 K at a true strain rate of 3×10-3 s-1 up to cumulative strain of∑△ε=4.0 at maximum.A pass strain of△ε=0.8 was employed.While average grain size decreased gradually with increasing cumulative strain,the evolution of fine-grained structure strongly depended on the MDF temperature.Under the condition where the temperature was higher than the most adequate one,grain coarsening partially took place during MDF.In contrast,at lower temperature,inhomogeneous microstructure composed of the initial coarse and newly appeared fine grains was evolved.After straining over∑△ε=3.2(i.e.,over 4 passes of MDF) ,equiaxed ultrafine grains(UFGs) having average size of about and lower than 1μm were uniformly evolved.While the MDFed alloy to∑△ε=4.0 possessed relatively high hardness of HV 99,and it accepted further about 20%cold rolling almost without cracking.Because of the superior formability of the UFGed AZ61Mg alloy,the hardness was further easily raised to HV 120 by following cold rolling.