Two kinds of unidirectional PAN M40 carbon fiber （55%, volume fraction） reinforced 6061Al and 5A06Al composites were fabricated by the squeeze-casting technology and their interface structure and thermal expansion p...Two kinds of unidirectional PAN M40 carbon fiber （55%, volume fraction） reinforced 6061Al and 5A06Al composites were fabricated by the squeeze-casting technology and their interface structure and thermal expansion properties were investigated. Results showed that the combination between aluminum alloy and fibers was well in two composites and interface reaction in M40/5A06Al composite was weaker than that in M40/6061Al composite. Coefficients of thermal expansion （CTE） of M40/Al composites varied approximately from （1.45-2.68）×10^-6 K^-1 to （0.35-1.44）×10^-6 K^-1 between 20℃ and 450℃, and decreased slowly with the increase of temperature. In addition, the CTE of M40/6061Al composite was lower than that of M40/SA06Al composite. It was observed that fibers were protruded significantly from the matrix after thermal expansion, which demonstrated the existence of interface sliding between fiber and matrix during the thermal expansion. It was believed that weak interracial reaction resulted in a higher CTE. It was found that the experimental CTEs were closer to the predicted values by Schapery model.展开更多
Two micron SiC particles with angular and spherical shape and the sub-micron Al2O3 particles with spherical shape were introduced to reinforce 6061 aluminium by squeeze casting technology. Microstructures and effect o...Two micron SiC particles with angular and spherical shape and the sub-micron Al2O3 particles with spherical shape were introduced to reinforce 6061 aluminium by squeeze casting technology. Microstructures and effect of thermal-cooling cycle treatment （TCCT） on the thermal expansion behaviors of three composites were investigated. The results show that the composites are free of porosity and SiC/Al2O3 particles are distributed uniformly. Inflections at about 300℃ are observed in coefficient of thermal expansion （CTE） versus temperature curves of two SiCp/Al composites, and this characteristic is not affected by TCCT. The TCCT has significant effect on thermal expansion behavior of SiCp/Al composites and CTE of them after 3 cycles is lower than that of 1 or 5 cycles. However, no inflection is observed in Al2O3p/Al composite, while TCCT has effect on CTE of Al2O3p/Al composite. These results should be due to different relaxation behavior of internal stress in three composites.展开更多
基金the foundation from the National Key Research and Development Program of China (No. 2020YFB1505901)the support by Xiao-qin ZENG Expert Workstation in Yunnan Province, China (No. 202005AF150059)。
基金Project(DL09BB23) supported by the Fundamental Research Funds for the Central Universities in China
文摘Two kinds of unidirectional PAN M40 carbon fiber （55%, volume fraction） reinforced 6061Al and 5A06Al composites were fabricated by the squeeze-casting technology and their interface structure and thermal expansion properties were investigated. Results showed that the combination between aluminum alloy and fibers was well in two composites and interface reaction in M40/5A06Al composite was weaker than that in M40/6061Al composite. Coefficients of thermal expansion （CTE） of M40/Al composites varied approximately from （1.45-2.68）×10^-6 K^-1 to （0.35-1.44）×10^-6 K^-1 between 20℃ and 450℃, and decreased slowly with the increase of temperature. In addition, the CTE of M40/6061Al composite was lower than that of M40/SA06Al composite. It was observed that fibers were protruded significantly from the matrix after thermal expansion, which demonstrated the existence of interface sliding between fiber and matrix during the thermal expansion. It was believed that weak interracial reaction resulted in a higher CTE. It was found that the experimental CTEs were closer to the predicted values by Schapery model.
基金Project(20080430895) supported by China Postdoctoral Science FoundationProject(2008RFQXG045) supported by Special Fund of Technological Innovation of HarbinProject(HITQNJS.2009.021) supported by Development Program for Outstanding Young Teachers in Harbin Institute of Technology
文摘Two micron SiC particles with angular and spherical shape and the sub-micron Al2O3 particles with spherical shape were introduced to reinforce 6061 aluminium by squeeze casting technology. Microstructures and effect of thermal-cooling cycle treatment （TCCT） on the thermal expansion behaviors of three composites were investigated. The results show that the composites are free of porosity and SiC/Al2O3 particles are distributed uniformly. Inflections at about 300℃ are observed in coefficient of thermal expansion （CTE） versus temperature curves of two SiCp/Al composites, and this characteristic is not affected by TCCT. The TCCT has significant effect on thermal expansion behavior of SiCp/Al composites and CTE of them after 3 cycles is lower than that of 1 or 5 cycles. However, no inflection is observed in Al2O3p/Al composite, while TCCT has effect on CTE of Al2O3p/Al composite. These results should be due to different relaxation behavior of internal stress in three composites.