Monodisperse core/shell latex particles composed of a polystyrene(PS) core and a thin conductive polypyrrole (PPy) shell were synthesized by means of two-stage emulsion polymerization. Proofs for the success of core/s...Monodisperse core/shell latex particles composed of a polystyrene(PS) core and a thin conductive polypyrrole (PPy) shell were synthesized by means of two-stage emulsion polymerization. Proofs for the success of core/shell synthesis were obtained by using transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy(XPS). Pressed pellet conductivity measurements on the dried composites indicated a low percolation threshold of 13.8%. The conductivity for the composites was higher than that of a heterogeneous admixture of dried PS latex and PPy bulk powder. The highest conductivity of the core/shell composite was 0.14 S/cm.展开更多
文摘Monodisperse core/shell latex particles composed of a polystyrene(PS) core and a thin conductive polypyrrole (PPy) shell were synthesized by means of two-stage emulsion polymerization. Proofs for the success of core/shell synthesis were obtained by using transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy(XPS). Pressed pellet conductivity measurements on the dried composites indicated a low percolation threshold of 13.8%. The conductivity for the composites was higher than that of a heterogeneous admixture of dried PS latex and PPy bulk powder. The highest conductivity of the core/shell composite was 0.14 S/cm.